JP7064130B2 - Olefin-based thermoplastic elastomer with excellent transparency - Google Patents

Olefin-based thermoplastic elastomer with excellent transparency Download PDF

Info

Publication number
JP7064130B2
JP7064130B2 JP2018030469A JP2018030469A JP7064130B2 JP 7064130 B2 JP7064130 B2 JP 7064130B2 JP 2018030469 A JP2018030469 A JP 2018030469A JP 2018030469 A JP2018030469 A JP 2018030469A JP 7064130 B2 JP7064130 B2 JP 7064130B2
Authority
JP
Japan
Prior art keywords
thermoplastic elastomer
bis
olefin
sorbitol
mass
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2018030469A
Other languages
Japanese (ja)
Other versions
JP2019143088A (en
Inventor
篠田佑里恵
岩崎祥平
内山陽平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
New Japan Chemical Co Ltd
Original Assignee
New Japan Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by New Japan Chemical Co Ltd filed Critical New Japan Chemical Co Ltd
Priority to JP2018030469A priority Critical patent/JP7064130B2/en
Publication of JP2019143088A publication Critical patent/JP2019143088A/en
Application granted granted Critical
Publication of JP7064130B2 publication Critical patent/JP7064130B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Description

本発明は、透明性に優れる熱可塑性エラストマーに関し、詳しくは特定のオレフィン系の熱可塑性エラストマーに特定の構造のジアセタール化合物を配合することにより、柔軟性や強度等の機械的特性を損なうことなく、透明性が著しく改善された熱可塑性エラストマーに関する。 The present invention relates to a thermoplastic elastomer having excellent transparency. Specifically, by blending a diacetal compound having a specific structure with a specific olefin-based thermoplastic elastomer, the mechanical properties such as flexibility and strength are not impaired. With respect to thermoplastic elastomers with significantly improved transparency.

熱可塑性エラストマーは、常温で加硫ゴムと同じ様なゴム弾性を有し、かつ加硫ゴムの様な加硫工程を必要とせず、熱可塑性樹脂と同様に加熱により可塑化・溶融できるので、成形加工が容易であり、しかもリサイクル使用が可能であることから、近年、自動車部品、家電部品、医療用部品、建材、玩具、スポーツ用品、日用品などの幅広い分野で使用されている。この様な熱可塑性エラストマーとしては、オレフィン系、スチレン系、ウレタン系、エステル系、アミド系、塩化ビニル系などがあるが、なかでもオレフィン系の熱可塑性エラストマーは軽量であり、更に成形加工性にも優れるなどの様々な特徴を有しており、上記分野で広く用いられている(非特許文献1、2)。 Thermoplastic elastomer has rubber elasticity similar to that of vulcanized rubber at room temperature, does not require a vulcanization step like vulcanized rubber, and can be plasticized and melted by heating like thermoplastic resin. Since it is easy to mold and can be recycled, it has been used in a wide range of fields such as automobile parts, home appliance parts, medical parts, building materials, toys, sporting goods, and daily necessities in recent years. Examples of such thermoplastic elastomers include olefin-based, styrene-based, urethane-based, ester-based, amide-based, vinyl chloride-based, etc. Among them, olefin-based thermoplastic elastomers are lightweight and have more moldability. It also has various features such as excellentness, and is widely used in the above fields (Non-Patent Documents 1 and 2).

また、最近は、視認性の必要性や意匠性の観点より透明性の必要とされる医療材料、被覆材、包装材、玩具などの用途で熱可塑性エラストマーを用いられることも多く、柔軟性や強度等の機械的特性に優れることは当然ながら、更に透明性に優れた熱可塑性エラストマーが求められている。従来、その様な透明性を必要とする用途では、例えば、特定のエステル系やアクリレート系などのエラストマーが一部用途で実用化されている(特許文献1~3)。しかし、上記の様なエラストマーは汎用的ではなく、汎用性の高いオレフィン系等の熱可塑性エラストマーでの透明性の改善も試みられている(特許文献4)が、これまで満足する様な透明性を得ることが難しいのが現状であった。従って、オレフィン系などの汎用的な可塑性エラストマーの透明性の改善が望まれている。 Recently, thermoplastic elastomers are often used in applications such as medical materials, covering materials, packaging materials, and toys that require transparency from the viewpoint of visibility and design, and are flexible. As a matter of course, there is a demand for a thermoplastic elastomer having excellent mechanical properties such as strength and further excellent transparency. Conventionally, in applications requiring such transparency, for example, specific ester-based and acrylate-based elastomers have been put into practical use in some applications (Patent Documents 1 to 3). However, the above-mentioned elastomers are not versatile, and attempts have been made to improve the transparency of thermoplastic elastomers such as olefins with high versatility (Patent Document 4), but the transparency is satisfactory so far. The current situation is that it is difficult to obtain. Therefore, it is desired to improve the transparency of general-purpose plastic elastomers such as olefins.

特開2000-63644号公報Japanese Unexamined Patent Publication No. 2000-6364 特開2007-126527号公報Japanese Unexamined Patent Publication No. 2007-126527 特開2016-79226号公報Japanese Unexamined Patent Publication No. 2016-79226 特表2007-511643号公報Japanese Patent Publication No. 2007-511643

日本ゴム協会紙、51巻10号、779-796(1978)Japan Rubber Association Paper, Vol. 51, No. 10, 779-796 (1978) 日本ゴム協会紙、83巻9号、269-276(2010)Japan Rubber Association Paper, Vol. 83, No. 9, 269-276 (2010)

本発明は、汎用の熱可塑性エラストマーであるオレフィン系の熱可塑性エラストマーの透明性を改善し、透明性に優れたオレフィン系の熱可塑性エラストマーを提供することを目的とし、その為に特定のオレフィン系の熱可塑性エラストマーと特定の構造のジアセタール化合物を含んでなるオレフィン系の熱可塑性エラストマー組成物を提供することを目的とする。 An object of the present invention is to improve the transparency of an olefin-based thermoplastic elastomer which is a general-purpose thermoplastic elastomer, and to provide an olefin-based thermoplastic elastomer having excellent transparency, and for that purpose, a specific olefin-based It is an object of the present invention to provide an olefin-based thermoplastic elastomer composition comprising the thermoplastic elastomer of the above and a diacetal compound having a specific structure.

本発明者らは、上記課題を解決すべく、鋭意検討した結果、特定の構造のオレフィン系の熱可塑性エラストマーに特定の構造のジアセタール化合物を配合することにより、柔軟性や強度等の機械的特性を損なうことなく、透明性を大きく改善できることを確認し、その結果、透明性に非常に優れた熱可塑性エラストマーが得られることを見出し、それに基づき本発明を完成するに至った。 As a result of diligent studies to solve the above problems, the present inventors have obtained mechanical properties such as flexibility and strength by blending a diacetal compound having a specific structure with an olefin-based thermoplastic elastomer having a specific structure. It was confirmed that the transparency could be greatly improved without impairing the transparency, and as a result, it was found that a thermoplastic elastomer having very excellent transparency could be obtained, and the present invention was completed based on this.

即ち、本発明は下記に示す熱可塑性エラストマーの透明性の改善方法及びオレフィン系の熱可塑性エラストマー組成物、更にその組成物を原料とし、その方法により透明性の改善されたオレフィン系の熱可塑性エラストマー成形体に関する。 That is, the present invention is a method for improving the transparency of a thermoplastic elastomer shown below, an olefin-based thermoplastic elastomer composition, and an olefin-based thermoplastic elastomer whose transparency is improved by the method using the composition as a raw material. Regarding molded products.

[項1] 透明性に優れたオレフィン系の熱可塑性エラストマー組成物であって、オレフィン系の熱可塑性エラストマー100質量部に対して、下記一般式(1)で示されるジアセタール化合物を0.05~5.0質量部を含有することを特徴とするオレフィン系の熱可塑性エラストマー組成物。

Figure 0007064130000001
[式(1)中、R及びRは、同一又は異なって、それぞれ、水素原子、直鎖状若しくは分岐鎖状の炭素数1~4のアルキル基、直鎖状若しくは分岐鎖状の炭素数1~4のアルコキシ基、直鎖状若しくは分岐鎖状の炭素数1~4のアルコキシカルボニル基又はハロゲン原子を示す。Rは、水素原子、直鎖状若しくは分岐鎖状の炭素数1~4のアルキル基、直鎖状若しくは分岐鎖状の炭素数2~4のアルケニル基又は直鎖状若しくは分岐鎖状の炭素数1~4のヒドロキシアルキル基を示す。m及びnは、それぞれ1~5の整数を示す。pは0又は1を示す。2つのRは互いに結合してそれらが結合するベンゼン環と共にテトラリン環を形成していてもよい。2つのR基は互いに結合してそれらが結合するベンゼン環と共にテトラリン環を形成していてもよい。] [Item 1] An olefin-based thermoplastic elastomer composition having excellent transparency, in which a diacetal compound represented by the following general formula (1) is added from 0.05 to 100 parts by mass of the olefin-based thermoplastic elastomer. An olefin-based thermoplastic elastomer composition containing 5.0 parts by mass.
Figure 0007064130000001
[In the formula (1), R 1 and R 2 are the same or different, respectively, a hydrogen atom, a linear or branched alkyl group having 1 to 4 carbon atoms, and a linear or branched carbon. It indicates an alkoxy group having the number of 1 to 4, a linear or branched alkoxycarbonyl group having 1 to 4 carbon atoms, or a halogen atom. R3 is a hydrogen atom , a linear or branched-chain alkyl group having 1 to 4 carbon atoms, a linear or branched-chain alkenyl group having 2 to 4 carbon atoms, or a linear or branched-chain carbon. The number 1 to 4 hydroxyalkyl groups are shown. m and n represent integers of 1 to 5, respectively. p indicates 0 or 1. The two R1s may be bonded to each other to form a tetralin ring with the benzene ring to which they are bonded. The two R2 groups may be bonded to each other to form a tetralin ring with the benzene ring to which they are bonded. ]

[項2] オレフィン系の熱可塑性エラストマーが、該熱可塑性エラストマーの全質量に対して60~99質量%のプロピレン誘導単位と、該熱可塑性エラストマーの全質量に対して1~40質量%のエチレン誘導単位及び/又は炭素数4~10のα-オレフィン誘導単位からなる共重合体であり、かつ、示差走査熱量分析で測定した融解熱量が50J/g以下である、[項1]に記載のオレフィン系の熱可塑性エラストマー組成物。 [Item 2] The olefin-based thermoplastic elastomer contains 60 to 99% by mass of propylene-inducing units with respect to the total mass of the thermoplastic elastomer and 1 to 40% by mass of ethylene with respect to the total mass of the thermoplastic elastomer. Item 6. The item 1], wherein the copolymer is composed of an induction unit and / or an α-olefin induction unit having 4 to 10 carbon atoms, and the heat of fusion measured by the differential scanning calorific value analysis is 50 J / g or less. An olefin-based thermoplastic elastomer composition.

[項3] オレフィン系の熱可塑性エラストマーが、該熱可塑性エラストマーの全質量に対して70~97質量%のプロピレン誘導単位と、該熱可塑性エラストマーの全質量に対して3~30質量%のエチレン誘導単位及び/又は炭素数4~10のα-オレフィン誘導単位からなる共重合体であり、かつ、示差走査熱量分析で測定した融解熱量が30J/g以下である、[項2]に記載のオレフィン系の熱可塑性エラストマー組成物。 [Item 3] The olefin-based thermoplastic elastomer contains 70 to 97% by mass of propylene-inducing units with respect to the total mass of the thermoplastic elastomer and 3 to 30% by mass of ethylene with respect to the total mass of the thermoplastic elastomer. Item 2. The item 2], wherein the copolymer is composed of an induction unit and / or an α-olefin induction unit having 4 to 10 carbon atoms, and the heat of fusion measured by the differential scanning calorific value analysis is 30 J / g or less. An olefin-based thermoplastic elastomer composition.

[項4] 示差走査熱量分析で測定した最大の融解ピーク温度が115℃以下である、又は示差走査熱量分析の測定では融解ピーク温度が観察されない、[項1]~[項3]の何れかに記載のオレフィン系の熱可塑性エラストマー組成物。 [Item 4] Any of [Item 1] to [Item 3], in which the maximum melting peak temperature measured by the differential scanning calorimetry is 115 ° C. or less, or the melting peak temperature is not observed by the measurement of the differential scanning calorimetry. The olefin-based thermoplastic elastomer composition according to.

[項5] ジアセタール化合物が、前記一般式(1)において、R及びRが、同一又は異なって、メチル基又はエチル基であり、かつ、Rが水素原子であり、m及びnが1又は2の整数であり、pが1である、[項1]~[項4]の何れかに記載のオレフィン系の熱可塑性エラストマー組成物。 [Item 5] In the general formula (1), R 1 and R 2 are the same or different, and the diacetal compound is a methyl group or an ethyl group, and R 3 is a hydrogen atom, and m and n are. The olefin-based thermoplastic elastomer composition according to any one of [Item 1] to [Item 4], which is an integer of 1 or 2 and p is 1.

[項6] ジアセタール化合物が、前記一般式(1)において、R及びRが、同一又は異なって、プロピル基又はプロポキシ基であり、かつ、Rがプロピル基又はプロペニル基であり、m及びnが1であり、pが1である、[項1]~[項4]の何れかに記載のオレフィン系の熱可塑性エラストマー組成物。 [Item 6] In the general formula (1), R 1 and R 2 are the same or different, and the diacetal compound is a propyl group or a propoxy group, and R 3 is a propyl group or a propenyl group. The olefin-based thermoplastic elastomer composition according to any one of [Item 1] to [Item 4], wherein n is 1 and p is 1.

[項7] ジアセタール化合物の含有量が、熱可塑性エラストマー100質量部に対して0.05~1.0質量部である、[項1]~[項6]の何れかに記載のオレフィン系の熱可塑性エラストマー組成物。 [Item 7] The olefin-based compound according to any one of [Item 1] to [Item 6], wherein the content of the diacetal compound is 0.05 to 1.0 part by mass with respect to 100 parts by mass of the thermoplastic elastomer. Thermoplastic elastomer composition.

[項8] [項1]~[項7]の何れかに記載のオレフィン系の熱可塑性エラストマー組成物を原料とする、透明性に優れた熱可塑性エラストマー成形体。 [Item 8] A thermoplastic elastomer molded product having excellent transparency, using the olefin-based thermoplastic elastomer composition according to any one of [Item 1] to [Item 7] as a raw material.

[項9] 熱可塑性エラストマーの透明性の改善方法であって、オレフィン系の熱可塑性エラストマー100質量部に対してジアセタール化合物を0.05~5.0質量部含有させること、更に、前記オレフィン系の熱可塑性エラストマーが、該熱可塑性エラストマーの全質量に対して60~99質量%のプロピレン誘導単位と、該熱可塑性エラストマーの全質量に対して1~40質量%のエチレン誘導単位及び/又は炭素数4~10のα-オレフィン誘導単位からなる共重合体であり、更に、示差走査熱量分析で測定した融解熱量が50J/g以下であり、且つ、ジアセタール化合物が、下記一般式(1)で示される化合物であることを特徴とする改善方法。

Figure 0007064130000002
[式(1)中、R及びRは、同一又は異なって、それぞれ、水素原子、直鎖状若しくは分岐鎖状の炭素数1~4のアルキル基、直鎖状若しくは分岐鎖状の炭素数1~4のアルコキシ基、直鎖状若しくは分岐鎖状の炭素数1~4のアルコキシカルボニル基又はハロゲン原子を示す。Rは、水素原子、直鎖状若しくは分岐鎖状の炭素数1~4のアルキル基、直鎖状若しくは分岐鎖状の炭素数2~4のアルケニル基又は直鎖状若しくは分岐鎖状の炭素数1~4のヒドロキシアルキル基を示す。m及びnは、それぞれ1~5の整数を示す。pは0又は1を示す。2つのRは互いに結合してそれらが結合するベンゼン環と共にテトラリン環を形成していてもよい。2つのR基は互いに結合してそれらが結合するベンゼン環と共にテトラリン環を形成していてもよい。] [Item 9] A method for improving the transparency of a thermoplastic elastomer, wherein the diacetal compound is contained in an amount of 0.05 to 5.0 parts by mass with respect to 100 parts by mass of the olefin-based thermoplastic elastomer, and further, the olefin-based thermoplastic elastomer is contained. The thermoplastic elastomer of the above is 60 to 99% by mass of propylene inductive units based on the total mass of the thermoplastic elastomer, and 1 to 40% by mass of ethylene inductive units and / or carbon based on the total mass of the thermoplastic elastomer. It is a copolymer composed of α-olefin induction units of several 4 to 10, further, the heat of fusion measured by differential scanning calorific value analysis is 50 J / g or less, and the diacetal compound is represented by the following general formula (1). An improvement method characterized by being the indicated compound.
Figure 0007064130000002
[In the formula (1), R 1 and R 2 are the same or different, respectively, a hydrogen atom, a linear or branched alkyl group having 1 to 4 carbon atoms, and a linear or branched carbon. It indicates an alkoxy group having the number of 1 to 4, a linear or branched alkoxycarbonyl group having 1 to 4 carbon atoms, or a halogen atom. R3 is a hydrogen atom , a linear or branched-chain alkyl group having 1 to 4 carbon atoms, a linear or branched-chain alkenyl group having 2 to 4 carbon atoms, or a linear or branched-chain carbon. The number 1 to 4 hydroxyalkyl groups are shown. m and n represent integers of 1 to 5, respectively. p indicates 0 or 1. The two R1s may be bonded to each other to form a tetralin ring with the benzene ring to which they are bonded. The two R2 groups may be bonded to each other to form a tetralin ring with the benzene ring to which they are bonded. ]

本発明の方法及びオレフィン系の熱可塑性エラストマー組成物を用いることにより、これまで課題であったオレフィン系の熱可塑性エラストマーに優れた透明性を付与することが可能となり、これまでオレフィン系のエラストマーの使用が難しかった透明性を必要とする用途でも、軽量でリサイクル性等に優れたオレフィン系のエラストマーを使用することが可能となる。 By using the method of the present invention and the olefin-based thermoplastic elastomer composition, it is possible to impart excellent transparency to the olefin-based thermoplastic elastomer, which has been a problem so far, and it has become possible to impart excellent transparency to the olefin-based elastomer. It is possible to use an olefin-based elastomer that is lightweight and has excellent recyclability even in applications that require transparency, which was difficult to use.

<オレフィン系の熱可塑性エラストマー組成物>
本発明のオレフィン系の熱可塑性エラストマーは、特定の構造のオレフィン系の熱可塑性エラストマーと特定の構造のジアセタール化合物を含有することを特徴とする。
<Olefin-based thermoplastic elastomer composition>
The olefin-based thermoplastic elastomer of the present invention is characterized by containing an olefin-based thermoplastic elastomer having a specific structure and a diacetal compound having a specific structure.

オレフィン系の熱可塑性エラストマー
本発明の熱可塑性エラストマーは、オレフィン系の熱可塑性エラストマーであり、好ましくは、熱可塑性エラストマーの全質量に対して60~99質量%、より好ましくは70~97質量%のプロピレン誘導単位と、1~40質量%、より好ましくは3~30質量%のエチレン誘導単位及び/又は炭素数4~10のα-オレフィン誘導単位からなる共重合体である。
Olefin-based thermoplastic elastomer The thermoplastic elastomer of the present invention is an olefin-based thermoplastic elastomer, preferably 60 to 99% by mass, more preferably 70 to 97% by mass, based on the total mass of the thermoplastic elastomer. It is a copolymer composed of a propylene-inducing unit, an ethylene-inducing unit of 1 to 40% by mass, more preferably 3 to 30% by mass, and / or an α-olefin inducing unit having 4 to 10 carbon atoms.

上記α-オレフィン誘導単位の基となるα-オレフィンとしては、具体的には、1-ブテン、イソブテン、1-ペンテン、1-ヘキセン、3-メチル-1-ペンテン、4-メチル-1-ペンテン、1-ヘプテン、1-オクテン、1-ノネン、1-デセンなどが挙げられ、なかでも好ましいα-オレフィンとしては、1-ブテン、4-メチル-1-ペンテンなどが挙げられる。これらのα-オレフィンは、単独で、又は2種以上を組み合わせて用いても良い。 Specific examples of the α-olefin that forms the basis of the α-olefin inducing unit include 1-butene, isobutene, 1-pentene, 1-hexene, 3-methyl-1-pentene, and 4-methyl-1-pentene. , 1-heptene, 1-octene, 1-nonen, 1-decene and the like, and among them, preferable α-olefins include 1-butene and 4-methyl-1-pentene. These α-olefins may be used alone or in combination of two or more.

また、本発明の熱可塑性エラストマーは、好ましくは示差走査熱量分析で測定した融解熱量が50J/g以下、より好ましくは30J/g以下であることが推奨される。融解熱量は結晶性の目安となる数値であり、上記範囲であれば、エラストマーとしての本来の特徴である柔軟性を付与できる程度に低い結晶性を有していることを示している。 Further, it is recommended that the thermoplastic elastomer of the present invention preferably has a heat of fusion measured by differential scanning calorimetry of 50 J / g or less, more preferably 30 J / g or less. The amount of heat of fusion is a numerical value that serves as a guideline for crystallinity, and within the above range, it indicates that the elastomer has low crystallinity to the extent that it can impart flexibility, which is the original characteristic of the elastomer.

上記示差走査熱量分析での測定は、汎用の分析装置を用いて、一般的な条件で測定することが可能である。具体的には、例えば、パーキンエルマー社製の示差走査熱量測定装置(商品名「DSC8500」)を用いて、測定サンプル(サンプル重量=5mgから10mg程度)を精秤し、10℃から10℃/minの昇温速度で220℃まで昇温し、サンプルが融解したときの融解ピークおよびその熱量を測定することができる。 The measurement in the differential scanning calorimetry can be performed under general conditions using a general-purpose analyzer. Specifically, for example, a measurement sample (sample weight = about 5 mg to 10 mg) is precisely weighed using a differential scanning calorimetry device (trade name “DSC8500”) manufactured by PerkinElmer, and the temperature is 10 ° C to 10 ° C /. The temperature is raised to 220 ° C. at a heating rate of min, and the melting peak and the amount of heat thereof when the sample is melted can be measured.

また、本発明の熱可塑性エラストマーは、示差走査熱量分析で測定した最大の融解ピーク温度が、好ましくは115℃以下であるか、又は示差走査熱量分析の測定では融解ピーク温度が観察されないことが推奨される。上記融解ピーク温度が上記範囲内であるとき、熱可塑性エラストマーとしての特徴を最大限に発揮することができる。 Further, it is recommended that the maximum melting peak temperature of the thermoplastic elastomer of the present invention measured by differential scanning calorimetry is preferably 115 ° C. or lower, or that the melting peak temperature is not observed by the measurement of differential scanning calorimetry. Will be done. When the melting peak temperature is within the above range, the characteristics of the thermoplastic elastomer can be maximized.

上記示差走査熱量分析での測定は、融解熱量と同様に汎用の分析装置を用いて、一般的な条件で測定することが可能である。 The measurement in the differential scanning calorimetry can be performed under general conditions using a general-purpose analyzer as in the case of the heat of fusion.

本発明のオレフィン系の熱可塑性エラストマーは、公知の製造方法、例えば、メタロセン触媒の存在下、プロピレンとエチレン及び/又は炭素数4~10のα-オレフィンを通常の条件で共重合することにより得られる。具体的には、特開2007-2266号公報に記載の製造方法などを用いて製造することができる。 The olefin-based thermoplastic elastomer of the present invention can be obtained by copolymerizing propylene with ethylene and / or an α-olefin having 4 to 10 carbon atoms under normal conditions in the presence of a known production method, for example, a metallocene catalyst. Be done. Specifically, it can be produced by using the production method described in JP-A-2007-2266.

また、本発明のオレフィン系の熱可塑性エラストマーとして、本発明の効果を奏する、即ち本発明の範囲に合致する市販のオレフィン系の熱可塑性エラストマーをそのまま用いることもできる。その様な市販のオレフィン系の熱可塑性エラストマーとしては、例えば、エクソン・モービル社のVistamaxxシリーズ、ダウケミカル社のVersifyシリーズ、三井化学(株)のTafmerシリーズやNotioシリーズ、住友化学(株)のTafthrenシリーズなどの製品が挙げられる。 Further, as the olefin-based thermoplastic elastomer of the present invention, a commercially available olefin-based thermoplastic elastomer that exhibits the effect of the present invention, that is, that meets the scope of the present invention can be used as it is. Examples of such commercially available olefin-based thermoplastic elastomers include ExxonMobil's Vistamaxx series, Dow Chemical's Versify series, Mitsui Chemicals'Tafmer series and Notio series, and Sumitomo Chemical's Tafthren. Products such as series can be mentioned.

ジアセタール化合物
本発明のジアセタール化合物は、下記一般式(1)で示されるジアセタール化合物である。

Figure 0007064130000003
[式(1)中、R及びRは、同一又は異なって、それぞれ、水素原子、直鎖状若しくは分岐鎖状の炭素数1~4のアルキル基、直鎖状若しくは分岐鎖状の炭素数1~4のアルコキシ基、直鎖状若しくは分岐鎖状の炭素数1~4のアルコキシカルボニル基又はハロゲン原子を示す。Rは、水素原子、直鎖状若しくは分岐鎖状の炭素数1~4のアルキル基、直鎖状若しくは分岐鎖状の炭素数2~4のアルケニル基又は直鎖状若しくは分岐鎖状の炭素数1~4のヒドロキシアルキル基を示す。m及びnは、それぞれ1~5の整数を示す。pは0又は1を示す。2つのRは互いに結合してそれらが結合するベンゼン環と共にテトラリン環を形成していてもよい。2つのR基は互いに結合してそれらが結合するベンゼン環と共にテトラリン環を形成していてもよい。] Diasetal compound The diacetal compound of the present invention is a diacetal compound represented by the following general formula (1).
Figure 0007064130000003
[In the formula (1), R 1 and R 2 are the same or different, respectively, a hydrogen atom, a linear or branched alkyl group having 1 to 4 carbon atoms, and a linear or branched carbon. It indicates an alkoxy group having the number of 1 to 4, a linear or branched alkoxycarbonyl group having 1 to 4 carbon atoms, or a halogen atom. R3 is a hydrogen atom , a linear or branched-chain alkyl group having 1 to 4 carbon atoms, a linear or branched-chain alkenyl group having 2 to 4 carbon atoms, or a linear or branched-chain carbon. The number 1 to 4 hydroxyalkyl groups are shown. m and n represent integers of 1 to 5, respectively. p indicates 0 or 1. The two R1s may be bonded to each other to form a tetralin ring with the benzene ring to which they are bonded. The two R2 groups may be bonded to each other to form a tetralin ring with the benzene ring to which they are bonded. ]

上記ジアセタール化合物の中でも、更に好ましい化合物としては、例えば、上記一般式(1)中のR及びRが、同一又は異なって、メチル基又はエチル基であり、かつ、Rが水素原子であり、m及びnが1又は2の整数であり、pが1である化合物や、上記一般式(1)中のR及びRがプロピル基又はプロピルオキシ基であり、かつ、Rがプロピル基又はプロペニル基であり、m及びnが1であり、pが1である化合物などが挙げられる。 Among the diacetal compounds, as more preferable compounds, for example, R 1 and R 2 in the above general formula (1) are the same or different, and are a methyl group or an ethyl group, and R 3 is a hydrogen atom. Yes, m and n are integers of 1 or 2, p is 1, and R 1 and R 2 in the above general formula (1) are propyl groups or propyloxy groups, and R 3 is. Examples thereof include compounds which are propyl groups or propenyl groups, in which m and n are 1, and p is 1.

また、次の様な化合物も更に好ましい化合物として例示することができる;上記一般式(1)において、R及びRがプロピル基又はプロピルオキシ基であり、かつ、Rがプロピル基又はプロペニル基であり、m及びnが1であり、pが1である化合物。 Further, the following compounds can also be exemplified as further preferable compounds; in the above general formula (1), R 1 and R 2 are propyl groups or propyloxy groups, and R 3 is a propyl group or propenyl. A compound that is a group, m and n are 1, and p is 1.

上記ジアセタール化合物の具体的な態様としては、次の様な化合物が例示される。1,3:2,4-ジ-O-ベンジリデン-D-ソルビトール、1,3:2,4-ビス-O-(メチルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(o-メチルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(m-メチルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(p-メチルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(エチルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(o-エチルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(m-エチルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(p-エチルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(o-イソプロピルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(m-イソプロピルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(p-イソプロピルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(o-n-プロピルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(m-n-プロピルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(p-n-プロピルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(o-n-ブチルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(m-n-ブチルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(p-n-ブチルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(o-t-ブチルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(m-t-ブチルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(p-t-ブチルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(ジメチルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(2’,3’-ジメチルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(2’,4’-ジメチルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(2’,5’-ジメチルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(2’,6’-ジメチルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(3’,4’-ジメチルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(3’,5’-ジメチルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(2’,3’-ジエチルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(2’,4’-ジエチルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(2’,5’-ジエチルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(2’,6’-ジエチルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(3’,4’-ジエチルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(3’,5’-ジエチルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(2’,4’,5’-トリメチルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(3’,4’,5’-トリメチルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(2’,4’,5’-トリエチルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(3’,4’,5’-トリエチルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(o-メトキシベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(m-メトキシベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(p-メトキシベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(o-エトキシベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(m-エトキシベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(p-エトキシベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(o-イソプロポキシベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(m-イソプロポキシベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(p-イソプロポキシベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(o-n-プロポキシベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(m-n-プロポキシベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(p-n-プロポキシベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(o-メトキシカルボニルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(m-メトキシカルボニルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(p-メトキシカルボニルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(o-エトキシカルボニルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(m-エトキシカルボニルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(p-エトキシカルボニルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(o-イソプロポキシカルボニルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(m-イソプロポキシカルボニルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(p-イソプロポキシカルボニルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(o-n-プロポキシカルボニルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(m-n-プロポキシカルボニルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(p-n-プロポキシカルボニルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(o-フルオロベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(m-フルオロベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(p-フルオロベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(o-クロロベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(m-クロロベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(p-クロロベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(o-ブロモベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(m-ブロモベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(p-ブロモベンジリデン)-D-ソルビトール、1,3-O-ベンジリデン-2,4-O-(p-メチルベンジリデン)-D-ソルビトール、1,3-O-(p-メチルベンジリデン)-2,4-O-ベンジリデン-D-ソルビトール、1,3-O-ベンジリデン-2,4-O-(p-エチルベンジリデン)-D-ソルビトール、1,3-O-(p-エチルベンジリデン)-2,4-O-ベンジリデン-D-ソルビトール、1,3-O-ベンジリデン-2,4-O-(p-クロロベンジリデン)-D-ソルビトール、1,3-O-(p-クロロベンジリデン)-2,4-O-ベンジリデン-D-ソルビトール、1,3-O-ベンジリデン-2,4-O-(2’,4’-ジメチルベンジリデン)-D-ソルビトール、1,3-O-(2’,4’-ジメチルベンジリデン)-2,4-O-ベンジリデン-D-ソルビトール、1,3-O-ベンジリデン-2,4-O-(3’,4’-ジメチルベンジリデン)-D-ソルビトール、1,3-O-(3’,4’-ジメチルベンジリデン)-2,4-O-ベンジリデン-D-ソルビトール、1,3-O-(p-メチルベンジリデン)-2,4-O-(p-エチルベンジリデン)-D-ソルビトール、1,3-O-(p-エチルベンジリデン)-2,4-O-(p-メチルベンジリデン)-D-ソルビトール、1,3-O-(p-メチルベンジリデン)-2,4-O-(3’,4’-ジメチルベンジリデン)-D-ソルビトール、1,3-O-(3’,4’-ジメチルベンジリデン)-2,4-O-p-メチルベンジリデン-D-ソルビトール、1,3-O-(p-エチルベンジリデン)-2,4-O-(3’,4’-ジメチルベンジリデン)-D-ソルビトール、1,3-O-(3’,4’-ジメチルベンジリデン)-2,4-O-p-エチルベンジリデン-D-ソルビトール、1,3-O-(p-メチルベンジリデン)-2,4-O-(p-クロロベンジリデン)-D-ソルビトール、1,3-O-(p-クロロベンジリデン)-2,4-O-(p-メチルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(3’,4’-ジクロロベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-ベンジリデン-1-メチルソルビトール、1,3:2,4-ビス-O-(p-メチルベンジリデン)-1-メチルソルビトール、1,3:2,4-ビス-O-(p-エチルベンジリデン)-1-メチルソルビトール、1,3:2,4-ビス-O-(p-n-プロピルベンジリデン)-1-メチルソルビトール、1,3:2,4-ビス-O-(2’,3’-ジメチルベンジリデン)-1-メチルソルビトール、1,3:2,4-ビス-O-(2’,4’-ジメチルベンジリデン)-1-メチルソルビトール、1,3:2,4-ビス-O-(2’,5’-ジメチルベンジリデン)-1-メチルソルビトール、1,3:2,4-ビス-O-(2’,6’-ジメチルベンジリデン)-1-メチルソルビトール、1,3:2,4-ビス-O-(3’,4’-ジメチルベンジリデン)-1-メチルソルビトール、1,3:2,4-ビス-O-(3’,5’-ジメチルベンジリデン)-1-メチルソルビトール、1,3:2,4-ビス-O-(2’,3’-ジエチルベンジリデン)-1-メチルソルビトール、1,3:2,4-ビス-O-(2’,4’-ジエチルベンジリデン)-1-メチルソルビトール、1,3:2,4-ビス-O-(2’,5’-ジエチルベンジリデン)-1-メチルソルビトール、1,3:2,4-ビス-O-(2’,6’-ジエチルベンジリデン)-1-メチルソルビトール、1,3:2,4-ビス-O-(3’,4’-ジエチルベンジリデン)-1-メチルソルビトール、1,3:2,4-ビス-O-(3’,5’-ジエチルベンジリデン)-1-メチルソルビトール、1,3:2,4-ビス-O-(3’-メチル-4’-メトキシベンジリデン)-1-メチルソルビトール、1,3:2,4-ビス-O-(3’,4’-ジクロロベンジリデン)-1-メチルソルビトール、1,3:2,4-ビス-O-(p-メトキシカルボニルベンジリデン)-1-メチルソルビトール、1,3:2,4-ビス-O-(3’-メチル-4’-フルオロベンジリデン)-1-メチルソルビトール、1,3:2,4-ビス-O-(3’-ブロモ-4’-エチルベンジリデン)-1-メチルソルビトール、1,3:2,4-ビス-O-ベンジリデン-1-エチルソルビトール、1,3:2,4-ビス-O-(p-メチルベンジリデン)-1-エチルソルビトール、1,3:2,4-ビス-O-(p-エチルベンジリデン)-1-エチルソルビトール、1,3:2,4-ビス-O-(p-n-プロピルベンジリデン)-1-エチルソルビトール、1,3:2,4-ビス-O-(2’,3’-ジメチルベンジリデン)-1-エチルソルビトール、1,3:2,4-ビス-O-(2’,4’-ジメチルベンジリデン)-1-エチルソルビトール、1,3:2,4-ビス-O-(2’,5’-ジメチルベンジリデン)-1-エチルソルビトール、1,3:2,4-ビス-O-(2’,6’-ジメチルベンジリデン)-1-エチルソルビトール、1,3:2,4-ビス-O-(3’,4’-ジメチルベンジリデン)-1-エチルソルビトール、1,3:2,4-ビス-O-(3’,5’-ジメチルベンジリデン)-1-エチルソルビトール、1,3:2,4-ビス-O-(2’,3’-ジエチルベンジリデン)-1-エチルソルビトール、1,3:2,4-ビス-O-(2’,4’-ジエチルベンジリデン
)-1-エチルソルビトール、1,3:2,4-ビス-O-(2’,5’-ジエチルベンジリデン)-1-エチルソルビトール、1,3:2,4-ビス-O-(2’,6’-ジエチルベンジリデン)-1-エチルソルビトール、1,3:2,4-ビス-O-(3’,4’-ジエチルベンジリデン)-1-エチルソルビトール、1,3:2,4-ビス-O-(3’,5’-ジエチルベンジリデン)-1-エチルソルビトール、1,3:2,4-ビス-O-(3’-メチル-4’-メトキシベンジリデン)-1-エチルソルビトール、1,3:2,4-ビス-O-(3’,4’-ジクロロベンジリデン)-1-エチルソルビトール、1,3:2,4-ビス-O-(p-メトキシカルボニルベンジリデン)-1-エチルソルビトール、1,3:2,4-ビス-O-(3’-メチル-4’-フルオロベンジリデン)-1-エチルソルビトール、1,3:2,4-ビス-O-(3’-ブロモ-4’-エチルベンジリデン)-1-エチルソルビトール、1,3:2,4-ビス-O-ベンジリデン-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(p-メチルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(p-エチルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(p-n-プロピルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(2’,3’-ジメチルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(2’,4’-ジメチルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(2’,5’-ジメチルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(2’,6’-ジメチルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(3’,4’-ジメチルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(3’,5’-ジメチルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(2’,3’-ジエチルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(2’,4’-ジエチルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(2’,5’-ジエチルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(2’,6’-ジエチルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(3’,4’-ジエチルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(3’,5’-ジエチルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(3’-メチル-4’-メトキシベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(3’,4’-ジクロロベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(p-メトキシカルボニルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(p-エトキシカルボニルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(p-プロポキシカルボニルベンジリデン)-1-n-プロピルソルビトール、1,3-O-(p-n-プロピルベンジリデン)-2,4-O-(p-プロポキシベンジリデン)-1-n-プロピルソルビトール、1,3-O-(p-プロポキシベンジリデン)-2,4-O-(p-n-プロピルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(3’-メチル-4’-フルオロベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(3’-ブロモ-4’-エチルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(p-n-プロピルベンジリデン)-1-プロペニルソルビトール、1,3:2,4-ビス-O-(p-エトキシカルボニルベンジリデン)-1-プロペニルソルビトール、1,3:2,4-ビス-O-(p-プロポキシカルボニルベンジリデン)-1-プロペニルソルビトール、1,3-O-(p-n-プロピルベンジリデン)-2,4-O-(p-プロポキシベンジリデン)-1-プロペニルソルビトール、1,3-O-(p-プロポキシベンジリデン)-2,4-O-(p-n-プロピルベンジリデン)-1-プロペニルソルビトール、1,3:2,4-ビス-O-ベンジリデン-1-アリルソルビトール、1,3:2,4-ビス-O-(p-メチルベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(p-エチルベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(p-n-プロピルベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(2’,3’-ジメチルベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(2’,4’-ジメチルベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(2’,5’-ジメチルベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(2’,6’-ジメチルベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(3’,4’-ジメチルベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(3’,5’-ジメチルベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(2’,3’-ジエチルベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(2’,4’-ジエチルベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(2’,5’-ジエチルベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(2’,6’-ジエチルベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(3’,4’-ジエチルベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(p-エトキシカルボニルベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(p-プロポキシカルボニルベンジリデン)-1-アリルソルビトール、1,3-O-(p-n-プロピルベンジリデン)-2,4-O-(p-プロポキシベンジリデン)-1-アリルソルビトール、1,3-O-(p-プロポキシベンジリデン)-2,4-O-(p-n-プロピルベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(3’,5’-ジエチルベンジリデン)-1-n-プロピルソルビトール、1,3:2,4-ビス-O-(3’-メチル-4’-メトキシベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(3’,4’-ジクロロベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(p-メトキシカルボニルベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(3’-メチル-4’-フルオロベンジリデン)-1-アリルソルビトール、1,3:2,4-ビス-O-(3’-ブロモ-4’-エチルベンジリデン)-1-アリルソルビトール等が例示される。
Specific embodiments of the diacetal compound include the following compounds. 1,3: 2,4-di-O-benzylidene-D-sorbitol, 1,3: 2,4-bis-O- (methylbenzylidene) -D-sorbitol, 1,3: 2,4-bis-O -(O-Methylbenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (m-methylbenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (p-) Methylbenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (ethylbenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (o-ethylbenzylidene) -D- Sorbitol, 1,3: 2,4-bis-O- (m-ethylbenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (p-ethylbenzylidene) -D-sorbitol, 1, 3: 2,4-bis-O- (o-isopropylbenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (m-isopropylbenzylidene) -D-sorbitol, 1,3: 2, 4-bis-O- (p-isopropylbenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (one-propylbenzylidene) -D-sorbitol, 1,3: 2,4- Bis-O- (mn-propylbenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (pn-propylbenzylidene) -D-sorbitol, 1,3: 2,4- Bis-O- (one-butylbenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (mn-butylbenzylidene) -D-sorbitol, 1,3: 2,4- Bis-O- (pn-butylbenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (ot-butylbenzylidene) -D-sorbitol, 1,3: 2,4- Bis-O- (mt-butylbenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (pt-butylbenzylidene) -D-sorbitol, 1,3: 2,4- Bis-O- (dimethylbenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (2', 3'-dimethylbenzylidene) -D-sorbitol, 1,3: 2,4-bis- O- (2', 4'-dimethylbenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (2', 5'-dimethylbenzylidene) -D-sorbitol, 1,3: 2, 4-bis-O- (2', 6'-dimethylbenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (3', 4'-dimethylbenzyl) Liden) -D-sorbitol, 1,3: 2,4-bis-O- (3', 5'-dimethylbenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (2', 3'-diethylbenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (2', 4'-diethylbenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (2', 5'-diethylbenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (2', 6'-diethylbenzylidene) -D-sorbitol, 1,3: 2,4- Bis-O- (3', 4'-diethylbenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (3', 5'-diethylbenzylidene) -D-sorbitol, 1,3: 2,4-Bis-O- (2', 4', 5'-trimethylbenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (3', 4', 5'-trimethylbendylidene) ) -D-sorbitol, 1,3: 2,4-bis-O- (2', 4', 5'-triethylbenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (3) ', 4', 5'-triethylbenzitol) -D-sorbitol, 1,3: 2,4-bis-O- (o-methoxybenzylidene) -D-sorbitol, 1,3: 2,4-bis-O -(M-Meth benzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (p-methoxybenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (o-) Ethoxybenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (m-ethoxybenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (p-ethoxybenzylidene)- D-sorbitol, 1,3: 2,4-bis-O- (o-isopropoxybenziliden) -D-sorbitol, 1,3: 2,4-bis-O- (m-isopropoxybenziliden) -D- Sorbitol, 1,3: 2,4-bis-O- (p-isopropoxybenziliden) -D-sorbitol, 1,3: 2,4-bis-O- (one-propoxybenziliden) -D-sorbitol , 1,3: 2,4-bis-O- (mn-propoxybenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (pn-propoxybenzylidene) -D-sorbitol , 1,3: 2,4-bis-O- (o-methoxycarbonylbenzylene) -D-sorbitol, 1,3: 2,4-bis-O- (m) -Methoxycarbonylbenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (p-methoxycarbonylbenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (o-ethoxy) CarbonylBenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (m-ethoxycarbonylbenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (p-ethoxycarbonylbenzylidene) ) -D-Sorbitol, 1,3: 2,4-bis-O- (o-isopropoxycarbonylbenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (m-isopropoxycarbonylbenzylidene) ) -D-Sorbitol, 1,3: 2,4-bis-O- (p-isopropoxycarbonylbenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (one-propoxycarbonyl) Benzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (mn-propoxycarbonylbenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (pn-) Propoxycarbonylbenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (o-fluorobenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (m-fluorobenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (p-fluorobenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (o-chlorobenzylidene) -D-sorbitol , 1,3: 2,4-bis-O- (m-chlorobenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (p-chlorobenzylidene) -D-sorbitol, 1,3 : 2,4-bis-O- (o-bromobenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (m-bromobenzylidene) -D-sorbitol, 1,3: 2,4 -Bis-O- (p-bromobenzylidene) -D-sorbitol, 1,3-O-benzylidene-2,4-O- (p-methylbenzylidene) -D-sorbitol, 1,3-O- (p-) Methylbenzylidene) -2,4-O-benzylidene-D-sorbitol, 1,3-O-benzylidene-2,4-O- (p-ethylbenzylidene) -D-sorbitol, 1,3-O- (p-) Ethylbenzylidene) -2,4-O-benzylidene-D-sorbitol, 1,3-O-benzylidene-2,4-O- (p-chlorobenzylidene) -D-sorbito Le, 1,3-O- (p-chlorobenziliden) -2,4-O-benziliden-D-sorbitol, 1,3-O-benziliden-2,4-O- (2', 4'-dimethylbenziliden) ) -D-Sorbitol, 1,3-O- (2', 4'-Dimethylbenziliden) -2,4-O-Benzilidene-D-Sorbitol, 1,3-O-Benzilidene-2,4-O- ( 3', 4'-dimethylbenzylidene) -D-sorbitol, 1,3-O- (3', 4'-dimethylbenziliden) -2,4-O-benziliden-D-sorbitol, 1,3-O- ( p-Methylbenzylidene) -2,4-O- (p-ethylbendylidene) -D-sorbitol, 1,3-O- (p-ethylbendylidene) -2,4-O- (p-methylbenziliden) -D -Sorbitol, 1,3-O- (p-methylbenziliden) -2,4-O- (3', 4'-dimethylbenziliden) -D-Sorbitol, 1,3-O- (3', 4'- Dimethylbenziliden) -2,4-O-p-methylbenziliden-D-sorbitol, 1,3-O- (p-ethylbendiliden) -2,4-O- (3', 4'-dimethylbenziliden) -D -Sorbitol, 1,3-O- (3', 4'-dimethylbenziliden) -2,4-O-p-ethylbendylidene-D-sorbitol, 1,3-O- (p-methylbenziliden) -2, 4-O- (p-chlorobenziliden) -D-sorbitol, 1,3-O- (p-chlorobenziliden) -2,4-O- (p-methylbenziliden) -D-sorbitol, 1,3: 2 , 4-bis-O- (3', 4'-dichlorobenzylidene) -D-sorbitol, 1,3: 2,4-bis-O-benziliden-1-methylsorbitol, 1,3: 2,4-bis -O- (p-Methylbenziliden) -1-methylsorbitol, 1,3: 2,4-bis-O- (p-ethylbenzylidene) -1-methylsorbitol, 1,3: 2,4-bis-O -(Pn-propylbenzylene) -1-methylsorbitol, 1,3: 2,4-bis-O- (2', 3'-dimethylbenzylidene) -1-methylsorbitol, 1,3: 2,4 -Bis-O- (2', 4'-dimethylbenziliden) -1-methylsorbitol, 1,3: 2,4-bis-O- (2', 5'-dimethylbenziliden) -1-methylsorbitol, 1 , 3: 2,4-Bis-O- (2', 6'-dimethylbenzylidene) -1-me Tyrsorbitol, 1,3: 2,4-bis-O- (3', 4'-dimethylbenzylidene) -1-methylsorbitol, 1,3: 2,4-bis-O- (3', 5'- Dimethylbenzylidene) -1-methylsorbitol, 1,3: 2,4-bis-O- (2', 3'-diethylbenzylidene) -1-methylsorbitol, 1,3: 2,4-bis-O-( 2', 4'-diethylbenzylidene) -1-methylsorbitol, 1,3: 2,4-bis-O- (2', 5'-diethylbenziliden) -1-methylsorbitol, 1,3: 2,4 -Bis-O- (2', 6'-diethylbenzylidene) -1-methylsorbitol, 1,3: 2,4-bis-O- (3', 4'-diethylbenzylidene) -1-methylsorbitol, 1 , 3: 2,4-bis-O- (3', 5'-diethylbenzylidene) -1-methylsorbitol, 1,3: 2,4-bis-O- (3'-methyl-4'-methoxybenziliden) ) -1-Methylsorbitol, 1,3: 2,4-bis-O- (3', 4'-dichlorobenzylidene) -1-methylsorbitol, 1,3: 2,4-bis-O- (p-) Methylcarbonylbenzylidene) -1-methylsorbitol, 1,3: 2,4-bis-O- (3'-methyl-4'-fluorobenzylidene) -1-methylsorbitol, 1,3: 2,4-bis- O- (3'-bromo-4'-ethylbenzylidene) -1-methylsorbitol, 1,3: 2,4-bis-O-benziliden-1-ethylsorbitol, 1,3: 2,4-bis-O -(P-Methylbenziliden) -1-ethylsorbitol, 1,3: 2,4-bis-O- (p-ethylbenziliden) -1-ethylsorbitol, 1,3: 2,4-bis-O- ( pn-propylbenziliden) -1-ethylsorbitol, 1,3: 2,4-bis-O- (2', 3'-dimethylbenziliden) -1-ethylsorbitol, 1,3: 2,4-bis -O- (2', 4'-dimethylbenzylidene) -1-ethylsorbitol, 1,3: 2,4-bis-O- (2', 5'-dimethylbenziliden) -1-ethylsorbitol, 1,3 : 2,4-bis-O- (2', 6'-dimethylbenzylidene) -1-ethylsorbitol, 1,3: 2,4-bis-O- (3', 4'-dimethylbenziliden) -1- Ethylsorbitol, 1,3: 2,4-bis-O- (3', 5'-dimethylbenziliden) -1-d Tyrsorbitol, 1,3: 2,4-bis-O- (2', 3'-diethylbenzylidene) -1-ethylsorbitol, 1,3: 2,4-bis-O- (2', 4'- Diethylbenzylidene) -1-ethylsorbitol, 1,3: 2,4-bis-O- (2', 5'-diethylbenzylidene) -1-ethylsorbitol, 1,3: 2,4-bis-O- (2', 5'-diethylbenzylidene) -1-ethylsorbitol, 1,3: 2,4-bis-O- 2', 6'-diethylbenzylidene) -1-ethylsorbitol, 1,3: 2,4-bis-O- (3', 4'-diethylbenzylidene) -1-ethylsorbitol, 1,3: 2,4 -Bis-O- (3', 5'-diethylbenzylidene) -1-ethylsorbitol, 1,3: 2,4-bis-O- (3'-methyl-4'-methoxybenzylidene) -1-ethylsorbitol , 1,3: 2,4-bis-O- (3', 4'-dichlorobenzylidene) -1-ethylsorbitol, 1,3: 2,4-bis-O- (p-methoxycarbonylbenzidene) -1 -Ethylsorbitol, 1,3: 2,4-bis-O- (3'-methyl-4'-fluorobenzylidene) -1-ethylsorbitol, 1,3: 2,4-bis-O- (3'- Bromo-4'-ethylbenzylene) -1-ethylsorbitol, 1,3: 2,4-bis-O-benzylidene-1-n-propylsorbitol, 1,3: 2,4-bis-O- (p-) Methylbenzylidene) -1-n-propylsorbitol, 1,3: 2,4-bis-O- (p-ethylbenzylidene) -1-n-propylsorbitol, 1,3: 2,4-bis-O- ( pn-propylbenziliden) -1-n-propylsorbitol, 1,3: 2,4-bis-O- (2', 3'-dimethylbenzylidene) -1-n-propylsorbitol, 1,3: 2 , 4-Bis-O- (2', 4'-Dimethylbenziliden) -1-n-propylsorbitol, 1,3: 2,4-Bis-O- (2', 5'-Dimethylbenziliden) -1- n-propylsorbitol, 1,3: 2,4-bis-O- (2', 6'-dimethylbenzylidene) -1-n-propylsorbitol, 1,3: 2,4-bis-O- (3') , 4'-Dimethylbenziliden) -1-n-propylsorbitol, 1,3: 2,4-bis-O- (3', 5'-dimethylbenzylidene) -1-n-propylsorbitol, 1,3: 2 , 4-Bis-O- (2', 3'-diethylbenzylidene) -1-n-propylsorbitol, 1, 3: 2,4-bis-O- (2', 4'-diethylbenzylidene) -1-n-propylsorbitol, 1,3: 2,4-bis-O- (2', 5'-diethylbenzylidene) -1-n-propylsorbitol, 1,3: 2,4-bis-O- (2', 6'-diethylbenzylidene) -1-n-propylsorbitol, 1,3: 2,4-bis-O- (3', 4'-diethylbenzylidene) -1-n-propylsorbitol, 1,3: 2,4-bis-O- (3', 5'-diethylbenzylidene) -1-n-propylsorbitol, 1, 3: 2,4-bis-O- (3'-methyl-4'-methoxybenzylidene) -1-n-propylsorbitol, 1,3: 2,4-bis-O- (3', 4'-dichloro Benzilidene) -1-n-propylsorbitol, 1,3: 2,4-bis-O- (p-methoxycarbonylbenziliden) -1-n-propylsorbitol, 1,3: 2,4-bis-O- ( p-ethoxycarbonylbenzylene) -1-n-propylsorbitol, 1,3: 2,4-bis-O- (p-propoxycarbonylbenzylene) -1-n-propylsorbitol, 1,3-O- (p-) n-propylbenziliden) -2,4-O- (p-propoxybenziliden) -1-n-propylsorbitol, 1,3-O- (p-propoxybenziliden) -2,4-O- (pn-) Propylbenzylidene) -1-n-propylsorbitol, 1,3: 2,4-bis-O- (3'-methyl-4'-fluorobenziliden) -1-n-propylsorbitol, 1,3: 2,4 -Bis-O- (3'-bromo-4'-ethylbenzylidene) -1-n-propylsorbitol, 1,3: 2,4-bis-O- (pn-propylbenziliden) -1-propenylsorbitol , 1,3: 2,4-bis-O- (p-ethoxycarbonylbenzylidene) -1-propenylsorbitol, 1,3: 2,4-bis-O- (p-propoxycarbonylbenziliden) -1-propenylsorbitol , 1,3-O- (pn-propylbenziliden) -2,4-O- (p-propoxybenzylidene) -1-propenyl sorbitol, 1,3-O- (p-propoxybenzylidene) -2,4 -O- (pn-Propylbenzylidene) -1-propenylsorbitol, 1,3: 2,4-bis-O-benzylidene-1-allylsorbitol, 1,3: 2,4-bis-O- ( p-Methylbenzylidene) -1-allyl sorbitol, 1,3: 2,4-bis-O- (p-ethylbenzylidene) -1-allyl sorbitol, 1,3: 2,4-bis-O- (p-) n-propylbenzylidene) -1-allyl sorbitol, 1,3: 2,4-bis-O- (2', 3'-dimethylbenzylidene) -1-allyl sorbitol, 1,3: 2,4-bis-O -(2', 4'-dimethylbenzylidene) -1-allyl sorbitol, 1,3: 2,4-bis-O- (2', 5'-dimethylbenzylidene) -1-allyl sorbitol, 1,3: 2 , 4-Bis-O- (2', 6'-dimethylbenzylidene) -1-allyl sorbitol, 1,3: 2,4-bis-O- (3', 4'-dimethylbenzylidene) -1-allyl sorbitol , 1,3: 2,4-bis-O- (3', 5'-dimethylbenzylidene) -1-allylsorbitol, 1,3: 2,4-bis-O- (2', 3'-diethylbenzylidene) ) -1-Allylsorbitol, 1,3: 2,4-bis-O- (2', 4'-diethylbenzylidene) -1-allylsorbitol, 1,3: 2,4-bis-O- (2') , 5'-diethylbenzylidene) -1-allyl sorbitol, 1,3: 2,4-bis-O- (2', 6'-diethylbenzylidene) -1-allyl sorbitol, 1,3: 2,4-bis -O- (3', 4'-diethylbenzylidene) -1-allyl sorbitol, 1,3: 2,4-bis-O- (p-ethoxycarbonylbenzylidene) -1-allyl sorbitol, 1,3: 2, 4-Bis-O- (p-propoxycarbonylbenzylidene) -1-allyl sorbitol, 1,3-O- (pn-propylbenzylidene) -2,4-O- (p-propoxybenzylidene) -1-allyl Sorbitol, 1,3-O- (p-propoxybenzylidene) -2,4-O- (pn-propylbenzylidene) -1-allyl sorbitol, 1,3: 2,4-bis-O- (3' , 5'-diethylbenzylidene) -1-n-propylsorbitol, 1,3: 2,4-bis-O- (3'-methyl-4'-methoxybenzylidene) -1-allylsorbitol, 1,3: 2 , 4-bis-O- (3', 4'-dichlorobenzylidene) -1-allyl sorbitol, 1,3: 2,4-bis-O- (p-methoxycarbonylbenzylidene) -1-allyl sorbitol, 1, 3: 2,4-bis-O- (3'-methyl-) Examples thereof include 4'-fluorobenzylidene) -1-allyl sorbitol, 1,3: 2,4-bis-O- (3'-bromo-4'-ethylbenzylidene) -1-allyl sorbitol and the like.

特に、好ましい態様としては、1,3:2,4-ビス-O-(p-メチルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(p-エチルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(3’,4’-ジメチルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(p-クロロベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(p-n-プロピルベンジリデン)-1-プロピルソルビトールが挙げられる。 Particularly preferred embodiments are 1,3: 2,4-bis-O- (p-methylbenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (p-ethylbenzylidene) -D. -Sorbitol, 1,3: 2,4-bis-O- (3', 4'-dimethylbenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (p-chlorobenzylidene) -D -Sorbitol, 1,3: 2,4-bis-O- (pn-propylbenzylidene) -1-propylsorbitol can be mentioned.

また、上記具体的な態様のジアセタール化合物は、単独で用いてもよいが、他の性能、例えば低温加工性等の観点から、2種以上のジアセタール化合物を併用、または予め混合した態様で用いてもよい。 Further, the diacetal compound of the above specific embodiment may be used alone, but from the viewpoint of other performance, for example, low temperature processability, two or more kinds of diacetal compounds may be used in combination or in a premixed manner. May be good.

上記併用または混合系で用いる場合、例えば、1,3:2,4-ジ-O-ベンジリデン-D-ソルビトールと1,3:2,4-ビス-O-(p-メチルベンジリデン)-D-ソルビトールの組合せや1,3:2,4-ビス-O-(p-エチルベンジリデン)-D-ソルビトールと1,3:2,4-ビス-O-(3’,4’-ジメチルベンジリデン)-D-ソルビトールの組合せ、1,3:2,4-ジベンジリデン-D-ソルビトールと1,3:2,4-ビス-O-(3’,4’-ジメチルベンジリデン)-D-ソルビトールの組合せ、1,3:2,4-ビス-O-(p-メチルベンジリデン)-D-ソルビトールと1,3:2,4-ビス-O-(3’,4’-ジメチルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(p-クロロベンジリデン)-D-ソルビトールと1,3:2,4-ビス-O-(3’,4’-ジメチルベンジリデン)-D-ソルビトール、1,3:2,4-ビス-O-(3’,4’-ジクロロベンジリデン)-D-ソルビトールと1,3:2,4-ビス-O-(3’,4’-ジメチルベンジリデン)-D-ソルビトール、の組合せなどが例示される。 When used in combination or in a mixed system, for example, 1,3: 2,4-di-O-benzylidene-D-sorbitol and 1,3: 2,4-bis-O- (p-methylbenziliden) -D- Combination of sorbitol and 1,3: 2,4-bis-O- (p-ethylbenzylidene) -D-sorbitol and 1,3: 2,4-bis-O- (3', 4'-dimethylbenzidene)- Combination of D-sorbitol, combination of 1,3: 2,4-dibenzylidene-D-sorbitol and 1,3: 2,4-bis-O- (3', 4'-dimethylbenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (p-methylbenzylidene) -D-sorbitol and 1,3: 2,4-bis-O- (3', 4'-dimethylbenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (p-chlorobenzylidene) -D-sorbitol and 1,3: 2,4-bis-O- (3', 4'-dimethylbenzylidene) -D-sorbitol, 1,3: 2,4-bis-O- (3', 4'-dichlorobenzylidene) -D-sorbitol and 1,3: 2,4-bis-O- (3', 4'-dimethylbenzidene)- An example is a combination of D-sorbitol.

上記ジアセタール化合物は、例えば、日本国特公昭48-43748号公報、特開昭53-5165号公報、特開昭57-185287号公報、特開平2-231488号公報等に記載されている製造方法などを用いて容易に製造することができる。また、現在ポリオレフィン用結晶核剤として市販されているもの、例えば、新日本理化(株)のゲルオールD、ゲルオールMD、ゲルオールDXR、ミリケン社(米国)のミラッド3988、ミラッドNX8000、GCH TECHNOLORY社(中国)のSIPAX NA-2などをそのまま使用してもよい。 The production method described for the diacetal compound is described in, for example, Japanese Patent Application Laid-Open No. 48-43748, JP-A-53-5165, JP-A-57-185287, JP-A-2-231488, and the like. It can be easily manufactured by using or the like. Also, those currently on the market as crystal nucleating agents for polyolefins, such as Gelol D, Gelol MD, Gelol DXR of Shin Nihon Rika Co., Ltd., Mirad 3988, Mirad NX8000, GCH TECHNOLORY of Milliken (USA) (China). ) SIPAX NA-2 or the like may be used as it is.

本発明のオレフィン系の熱可塑性エラストマー組成物中の上記ジアセタール化合物の含有量は、熱可塑性エラストマー100質量部に対して0.05~5.0質量部であり、好ましくは0.05~1.0質量部であることが推奨される。ジアセタール化合物の含有量が上記範囲にある場合、本発明の特徴である透明性の改善効果を最大限に発揮させることができる。 The content of the diacetal compound in the olefin-based thermoplastic elastomer composition of the present invention is 0.05 to 5.0 parts by mass with respect to 100 parts by mass of the thermoplastic elastomer, preferably 0.05 to 1. It is recommended to have 0 parts by mass. When the content of the diacetal compound is within the above range, the effect of improving transparency, which is a feature of the present invention, can be maximized.

その他の添加剤
本発明のオレフィン系の熱可塑性エラストマー組成物には、その使用目的やその用途に応じて、本発明の効果を損なわない範囲で本発明のジアセタール化合物以外の一般的に熱可塑性エラストマーに使われているその他の添加剤、例えば、通常のゴムに使用されている軟化剤や一般的にポリオレフィン系樹脂に使用されているポリオレフィン系樹脂用添加剤などが含まれていても良い。
Other Additives The olefin-based thermoplastic elastomer composition of the present invention is generally a thermoplastic elastomer other than the diacetal compound of the present invention, depending on the purpose of use and its use, as long as the effects of the present invention are not impaired. Other additives used in the above, for example, softeners used in ordinary rubbers and additives for polyolefin resins generally used in polyolefin resins may be contained.

上記ゴム用の軟化剤としては、具体的には、プロセスオイル、潤滑油、パラフィン、流動パラフィン、ポリエチレンワックス、ポリプロピレンワックス、石油アスファルト、ワセリン等の石油系軟化剤; コールタール、コールタールピッチ等のコールタール系軟化剤;ヒマシ油、アマニ油、ナタネ油、大豆油、椰子油等の脂肪油系軟化剤; トール油; サブ、( ファクチス) ; 蜜ロウ、カルナウバロウ、ラノリン等のロウ類; リシノール酸、パルミチン酸、ステアリン酸、ステアリン酸バリウム、ステアリン酸カルシウム、ラウリン酸亜鉛等の脂肪酸および脂肪酸塩; ナフテン酸; パイン油、ロジンまたはその誘導体; テルペン樹脂、石油樹脂、クマロンインデン樹脂、アタクチックポリプロピレン等の合成高分子物質; ジオクチルフタレート、ジオクチルアジペート、ジオクチルセバケート等のエステル系軟化剤; マイクロクリスタリンワックス、液状ポリブタジエン、変性液状ポリブタジエン、液状ポリイソプレン、末端変性ポリイソプレン、水添末端変性ポリイソプレン、液状チオコール、炭化水素系合成潤滑油などが挙げられる。軟化剤を配合する場合、その配合量は、例えば、熱可塑性エラストマー100質量部に対して20~100質量部程度であることが一般的である。 Specific examples of the softener for rubber include petroleum-based softeners such as process oil, lubricating oil, paraffin, liquid paraffin, polyethylene wax, polypropylene wax, petroleum asphalt, and vaseline; Coultal softeners; Fatty oil softeners such as castor oil, flaxseed oil, rapeseed oil, soybean oil, palm oil; tall oil; sub, (factis); waxes such as beeswax, carnauba wax, lanolin; , Palmitic acid, stearic acid, barium stearate, calcium stearate, zinc laurate and other fatty acids and fatty acid salts; naphthenic acid; pine oil, rosin or derivatives thereof; terpene resin, petroleum resin, kumaron inden resin, atactic polypropylene, etc. Synthetic polymer substances; ester-based softeners such as dioctylphthalate, dioctyl adipate, dioctyl sebacate; microcrystallin wax, liquid polybutadiene, modified liquid polybutadiene, liquid polyisoprene, terminal-modified polyisoprene, hydrogenated terminal-modified polyisoprene, liquid Examples thereof include thiocol and hydrocarbon-based synthetic lubricating oils. When the softening agent is blended, the blending amount is generally, for example, about 20 to 100 parts by mass with respect to 100 parts by mass of the thermoplastic elastomer.

上記ポリオレフィン系樹脂用添加剤としては、例えば、ポリオレフィン等衛生協議会編「ポジティブリストの添加剤要覧」(2004年9月)に記載されている各種添加剤が挙げられる。具体的には、ジアセタール化合物以外の造核剤(リン酸エステル金属塩、カルボン酸金属塩等)、蛍光増白剤(2,5-チオフェンジイル(5-t-ブチル-1,3-ベンゾキサゾール)、4,4’-ビス(ベンゾオキサゾール-2-イル)スチルベン等)、酸化防止剤、安定剤(金属化合物、エポキシ化合物、窒素化合物、燐化合物、硫黄化合物等)、紫外線吸収剤(ベンゾフェノン系化合物、ベンゾトリアゾール系化合物等)、界面活性剤、滑剤(パラフィン、ワックス等の脂肪族炭化水素、炭素数8~22の高級脂肪酸、炭素数8~22の高級脂肪酸金属(Al、Ca)塩、炭素数8~22の高級脂肪族アルコール、ポリグリコール、炭素数4~22の高級脂肪酸と炭素数4~18の脂肪族1価アルコールとのエステル、炭素数8~22の高級脂肪酸アマイド、シリコーン油、ロジン誘導体等)、充填剤(タルク、ハイドロタルサイト、マイカ、ゼオライト、パーライト、珪藻土、炭酸カルシウム、ガラス繊維等)、発泡剤、発泡助剤、ポリマー添加剤、可塑剤(ジアルキルフタレート、ジアルキルヘキサヒドロフタレート等)、架橋剤、架橋促進剤、帯電防止剤、難燃剤、分散剤、有機無機の顔料(インディゴ化合物、フタロシアニン系化合物、アントラキノン系化合物、ウルトラマリン化合物、アルミン酸コバルト化合物等)、加工助剤、他の核剤等の各種添加剤が例示される。 Examples of the additives for polyolefin resins include various additives described in "Handbook of Additives on the Positive List" (September 2004) edited by the Polyolefin Hygiene Council. Specifically, nucleating agents (phosphate ester metal salts, carboxylic acid metal salts, etc.) other than diacetal compounds, fluorescent whitening agents (2,5-thiophendiyl (5-t-butyl-1,3-benzoxa)). Zol), 4,4'-bis (benzoxazole-2-yl) stylben, etc.), antioxidants, stabilizers (metal compounds, epoxy compounds, nitrogen compounds, phosphorus compounds, sulfur compounds, etc.), ultraviolet absorbers (benzophenone) Systems compounds, benzotriazole compounds, etc.), surfactants, lubricants (aliphatic hydrocarbons such as paraffin and wax, higher fatty acids with 8 to 22 carbon atoms, higher fatty acid metal (Al, Ca) salts with 8 to 22 carbon atoms). , Higher aliphatic alcohol having 8 to 22 carbon atoms, polyglycol, ester of higher fatty acid having 4 to 22 carbon atoms and aliphatic monovalent alcohol having 4 to 18 carbon atoms, higher fatty acid amide having 8 to 22 carbon atoms, silicone. Oils, rosin derivatives, etc.), fillers (talc, hydrotalcite, mica, zeolite, pearlite, diatomaceous earth, calcium carbonate, glass fiber, etc.), foaming agents, foaming aids, polymer additives, plasticizers (dialkylphthalate, dialkyl) Hexahydrophthalate, etc.), cross-linking agent, cross-linking accelerator, antistatic agent, flame retardant, dispersant, organic-inorganic pigment (indigo compound, phthalocyanine-based compound, anthraquinone-based compound, ultramarine compound, cobalt aluminate compound, etc.), Various additives such as processing aids and other nucleating agents are exemplified.

これらのポリオレフィン系樹脂用添加剤を使用する場合、その使用量は、本発明の効果を阻害しない限り、通常使用されている範囲で使用すればよいが、例えば、ポリオレフィン系樹脂100質量部に対して、好ましくは0.0001~100質量部程度、より好ましくは0.001~50質量部程度で使用されるのが一般的である。 When these additives for polyolefin resins are used, the amount thereof may be used within the range normally used as long as the effects of the present invention are not impaired. For example, with respect to 100 parts by mass of the polyolefin resin. It is generally used in an amount of about 0.0001 to 100 parts by mass, more preferably about 0.001 to 50 parts by mass.

上記酸化防止剤としては、フェノール系酸化防止剤、亜リン酸エステル系酸化防止剤、イオウ系酸化防止剤等が例示され、具体的な酸化防止剤としては、2,6-ジ-tert-ブチルフェノール、テトラキス[メチレン-3-(3,5-tert-ブチル-4-ヒドロキシフェノール)プロピオネート]メタン、2-ヒドロキシ-4-メトキシベンゾフェノンなどのフェノール系酸化防止剤、アルキルジスルフィド、チオジプロピオン酸エステル、ベンゾチアゾールなどの硫黄系酸化防止剤、トリスノニルフェニルホスファイト、ジフェニルイソデシルホスファイト、トリフェニルホスファイト、トリス(2,4-ジ-tert-ブチルフェニル)ホスファイト、3,9-ビス(2,6-tert-ブチル-4-メチルフェノキシ)-2,4,8,10-テトラオキサ-3,9-ジホスファスピロ[5,5]ウンデカンなどの亜リン酸エステル系酸化防止剤等が例示される。中でも、フェノール系酸化防止剤であるテトラキス[メチレン-3-(3,5-ジ-t-ブチル-4-ヒドロキシフェニル)プロピオネート]メタン、亜リン酸エステル系の酸化防止剤であるトリス(2,4-ジ-tert-ブチルフェニル)ホスファイト、3,9-ビス(2,6-tert-ブチル-4-メチルフェノキシ)-2,4,8,10-テトラオキサ-3,9-ジホスファスピロ[5,5]ウンデカンなどが特に推奨される。 Examples of the antioxidant include phenol-based antioxidants, phosphite-based antioxidants, sulfur-based antioxidants, and the like, and specific antioxidants include 2,6-di-tert-butylphenol. , Tetrax [Methylene-3- (3,5-tert-butyl-4-hydroxyphenol) propionate] Phenolic antioxidants such as methane and 2-hydroxy-4-methoxybenzophenone, alkyl disulfides, thiodipropionic acid esters, Sulfur-based antioxidants such as benzothiazole, trisnonylphenylphosphite, diphenylisodecylphosphite, triphenylphosphite, tris (2,4-di-tert-butylphenyl) phosphite, 3,9-bis (2) , 6-tert-butyl-4-methylphenoxy) -2,4,8,10-tetraoxa-3,9-diphosphaspiro [5,5] Subphosphate ester-based antioxidants such as undecane are exemplified. Among them, tetrakis [methylene-3- (3,5-di-t-butyl-4-hydroxyphenyl) propionate] methane, which is a phenolic antioxidant, and tris (2,) which is a phosphite ester-based antioxidant. 4-Di-tert-butylphenyl) phosphite, 3,9-bis (2,6-tert-butyl-4-methylphenoxy) -2,4,8,10-tetraoxa-3,9-diphosphaspiro [5, 5] Undecan is especially recommended.

本発明のオレフィン系の熱可塑性エラストマー組成物の製造方法は、本発明の効果を奏する限り、特に限定されず、例えば、本発明のオレフィン系の熱可塑性エラストマー、ジアセタール化合物、及び必要に応じて他の添加剤を、汎用の溶融混合装置、一軸押出機、二軸押出機などを用いて溶融混合後、冷却固化し、ペレット状等の形状にカッティングする方法などが例示される。また、溶融混合前に予め前記各成分を均一にドライブレンドする方法なども有効な方法として挙げられる。更に、前記溶融混合時の温度が、配合されたジアセタール化合物の全量がオレフィン系の熱可塑性エラストマーに溶解する温度以上である場合、本発明の効果をより一層発揮することができる。 The method for producing the olefin-based thermoplastic elastomer composition of the present invention is not particularly limited as long as the effect of the present invention is exhibited, and for example, the olefin-based thermoplastic elastomer of the present invention, the diacetal compound, and if necessary, others. Examples thereof include a method in which the additive of the above is melt-mixed using a general-purpose melt-mixer, a single-screw extruder, a twin-screw extruder, etc., then cooled and solidified, and cut into a pellet-like shape. Further, a method of uniformly dry-blending each component in advance before melting and mixing is also mentioned as an effective method. Further, when the temperature at the time of melting and mixing is equal to or higher than the temperature at which the total amount of the compounded diacetal compound is dissolved in the olefin-based thermoplastic elastomer, the effect of the present invention can be further exhibited.

<透明性の改善方法>
本発明の透明性の改善方法は、オレフィン系の熱可塑性エラストマー100質量部に対してジアセタール化合物0.05~5.0質量部を含有させることを特徴とし、更に、前記オレフィン系の熱可塑性エラストマーが、該熱可塑性エラストマーの全質量に対して60~99質量%のプロピレン誘導単位と、該熱可塑性エラストマーの全質量に対して1~40質量%のエチレン誘導単位及び/又は炭素数4~10のα-オレフィン誘導単位からなる共重合体であり、更に、示差走査熱量分析で測定した融解熱量が50J/g以下であり、且つ、ジアセタール化合物が、下記一般式(1)で示される化合物であることを特徴とする。

Figure 0007064130000004
[式(1)中、R及びRは、同一又は異なって、それぞれ、水素原子、直鎖状若しくは分岐鎖状の炭素数1~4のアルキル基、直鎖状若しくは分岐鎖状の炭素数1~4のアルコキシ基、直鎖状若しくは分岐鎖状の炭素数1~4のアルコキシカルボニル基又はハロゲン原子を示す。Rは、水素原子、直鎖状若しくは分岐鎖状の炭素数1~4のアルキル基、直鎖状若しくは分岐鎖状の炭素数2~4のアルケニル基又は直鎖状若しくは分岐鎖状の炭素数1~4のヒドロキシアルキル基を示す。m及びnは、それぞれ1~5の整数を示す。pは0又は1を示す。2つのRは互いに結合してそれらが結合するベンゼン環と共にテトラリン環を形成していてもよい。2つのR基は互いに結合してそれらが結合するベンゼン環と共にテトラリン環を形成していてもよい。]
なお、本発明の透明性の改善方法に係る各構成の説明は、上記<オレフィン系の熱可塑性エラストマー組成物>に記載した構成の説明と同義である。 <How to improve transparency>
The method for improving transparency of the present invention is characterized by containing 0.05 to 5.0 parts by mass of a diacetal compound with respect to 100 parts by mass of an olefin-based thermoplastic elastomer, and further, the olefin-based thermoplastic elastomer is contained. However, 60 to 99% by mass of the propylene inductive unit with respect to the total mass of the thermoplastic elastomer, 1 to 40% by mass of the ethylene inductive unit with respect to the total mass of the thermoplastic elastomer, and / or 4 to 10 carbon atoms. It is a copolymer composed of the α-olefin inducing unit of the above, and further, the heat of fusion measured by the differential scanning calorific value analysis is 50 J / g or less, and the diacetal compound is a compound represented by the following general formula (1). It is characterized by being.
Figure 0007064130000004
[In the formula (1), R 1 and R 2 are the same or different, respectively, a hydrogen atom, a linear or branched alkyl group having 1 to 4 carbon atoms, and a linear or branched carbon. It indicates an alkoxy group having the number of 1 to 4, a linear or branched alkoxycarbonyl group having 1 to 4 carbon atoms, or a halogen atom. R3 is a hydrogen atom , a linear or branched-chain alkyl group having 1 to 4 carbon atoms, a linear or branched-chain alkenyl group having 2 to 4 carbon atoms, or a linear or branched-chain carbon. The number 1 to 4 hydroxyalkyl groups are shown. m and n represent integers of 1 to 5, respectively. p indicates 0 or 1. The two R1s may be bonded to each other to form a tetralin ring with the benzene ring to which they are bonded. The two R2 groups may be bonded to each other to form a tetralin ring with the benzene ring to which they are bonded. ]
The description of each configuration according to the method for improving transparency of the present invention is synonymous with the description of the configuration described in the above <olefin-based thermoplastic elastomer composition>.

<オレフィン系の熱可塑性エラストマー成形体>
本発明のオレフィン系の熱可塑性エラストマー成形体は、上記本発明のオレフィン系の熱可塑性エラストマー組成物を用いて、慣用されている成形方法に従って成形することにより得られる。前記成形方法としては、本発明の効果を奏する限り、特に制約はなく、射出成形、押出成形、ブロー成形、圧空成形、回転成形、フィルム成形等の従来公知の成形方法のいずれも採用できる。
<Olefin-based thermoplastic elastomer molded product>
The olefin-based thermoplastic elastomer molded product of the present invention can be obtained by molding using the above-mentioned olefin-based thermoplastic elastomer composition of the present invention according to a conventional molding method. The molding method is not particularly limited as long as the effect of the present invention is exhibited, and any conventionally known molding method such as injection molding, extrusion molding, blow molding, pneumatic molding, rotary molding, and film molding can be adopted.

かくして得られたオレフィン系の熱可塑性エラストマー成形体は、透明性等の光学的特性や柔軟性、強度等の機械的特性に非常に優れており、成形品やシート、フィルムとして、自動車部材、電気部材、機械部品、日常雑貨など様々な用途で、非常に有用である。特に、一般的な熱可塑性エラストマーでは得られなかった透明性を有しており、視認性の必要性や意匠性の観点より透明性の必要とされる医療材料、被覆材、包装材、玩具などの用途で、非常に有用である。 The olefin-based thermoplastic elastomer molded product thus obtained is extremely excellent in optical properties such as transparency and mechanical properties such as flexibility and strength. It is very useful in various applications such as parts, machine parts, and daily miscellaneous goods. In particular, it has transparency that cannot be obtained with general thermoplastic elastomers, and medical materials, coating materials, packaging materials, toys, etc. that require transparency from the viewpoint of visibility and design. It is very useful in the applications of.

以下に実施例を示し、本発明を更に詳しく説明するが、本発明はこれらの実施例によって制限されるものではない。尚、実施例中に記載した各特性の測定方法及び実施例で用いた熱可塑性エラストマーやジアセタール化合物は以下の通りである。 Examples are shown below and the present invention will be described in more detail, but the present invention is not limited to these examples. The methods for measuring each characteristic described in the examples and the thermoplastic elastomers and diacetal compounds used in the examples are as follows.

[熱可塑性エラストマーの性状]
(1)融解熱量及び最大の融解ピーク温度
パーキンエルマー社製の示差走査熱量測定装置(商品名「DSC8500」)を用いて、サンプル重量5mgから10mgの間の重量の測定サンプルを精秤し、10℃から10℃/minの昇温速度で220℃まで昇温し、サンプルが融解したときの融解ピークおよびその熱量を測定した。
[Characteristics of thermoplastic elastomer]
(1) Heat quantity of melting and maximum melting peak temperature Using a differential scanning calorimetry device (trade name "DSC8500") manufactured by PerkinElmer, a measurement sample having a weight between 5 mg and 10 mg is precisely weighed and 10 The temperature was raised from ° C. to 220 ° C. at a heating rate of 10 ° C./min, and the melting peak and the amount of heat thereof when the sample melted were measured.

[熱可塑性エラストマー成形体の光学的特性]
(2)透明性評価:ヘイズ値の測定
東洋精機製作所製のヘイズメータを用いて、JIS K7136(2000)に準じた方法でヘイズ値を測定した。評価試料には、1mm厚み射出成形品の熱可塑性エラストマー成形体を使用した。得られたヘイズ値の数値が小さい程、透明性に優れていることを示す。ヘイズ値の値が20%以下、好ましくは10%以下である場合、実用上十分な視認性が得られる程度に透明性に優れると言える。
[Optical properties of thermoplastic elastomer molded product]
(2) Transparency evaluation: Measurement of haze value The haze value was measured by a method according to JIS K7136 (2000) using a haze meter manufactured by Toyo Seiki Seisakusho. As the evaluation sample, a thermoplastic elastomer molded product having a thickness of 1 mm was used. The smaller the obtained haze value, the better the transparency. When the haze value is 20% or less, preferably 10% or less, it can be said that the transparency is excellent enough to obtain practically sufficient visibility.

[熱可塑性エラストマー成形体の機械的特性]
(3)引張試験:引張弾性率、引張降伏応力、引張破壊ひずみの測定
インストロン社製の万能材料試験器(機種名「インストロン5565」)を用いて、JIS K7161-1(2014)に準じた方法で引張試験を行い、引張弾性率、引張降伏応力、引張破壊ひずみの測定を行った。なお、試験環境、試験片形状、試験条件は、以下の通りである。
測定温度:23℃、試料長(チャック間距離):10mm、試験速度:50mm/min。
引張試験片:厚さ0.5mmの射出成形品を樹脂の流れ方向(MD方向)および垂直方向(TD方向)に幅7mm、長さ10mmの短冊状に切断したものを用いた。
[Mechanical properties of thermoplastic elastomer molded product]
(3) Tensile test: Measurement of tensile elastic modulus, tensile yield stress, and tensile fracture strain According to JIS K7161-1 (2014) using a universal material tester manufactured by Instron (model name "Instron 5565"). The tensile test was carried out by the above method, and the tensile elastic modulus, tensile yield stress, and tensile fracture strain were measured. The test environment, test piece shape, and test conditions are as follows.
Measurement temperature: 23 ° C., sample length (distance between chucks): 10 mm, test speed: 50 mm / min.
Tensile test piece: An injection-molded product having a thickness of 0.5 mm was cut into strips having a width of 7 mm and a length of 10 mm in the resin flow direction (MD direction) and vertical direction (TD direction).

オレフィン系の熱可塑性エラストマー
・エラストマーA:プロピレン・エチレン共重合体、商品名 Vistamaxx3588FL、エクソン・モービル社製、エチレン誘導単位の含有量:4質量%、MFR(230℃、荷重21.18N):8g/10分、融解熱量:29.3J/g、最大の融解ピーク温度:106.8℃。
・エラストマーB:プロピレン・エチレン共重合体、商品名 Vistamaxx6102、エクソン・モービル社製、エチレン誘導単位の含有量:16質量%、MFR(230℃、荷重21.18N):3g/10分、融解熱量:15J/g以下、最大の融解ピーク温度:観察されず。
Olefin-based thermoplastic elastomer elastomer A: propylene / ethylene copolymer, trade name Vistamaxx3588FL, manufactured by Exxon Mobile, content of ethylene induction unit: 4% by mass, MFR (230 ° C, load 21.18N): 8g / 10 minutes, heat of fusion: 29.3 J / g, maximum melting peak temperature: 106.8 ° C.
Elastomer B: propylene / ethylene copolymer, trade name Vistamaxx6102, manufactured by Exxon Mobile, content of ethylene induction unit: 16% by mass, MFR (230 ° C, load 21.18N): 3g / 10 minutes, heat of melting : 15 J / g or less, maximum melting peak temperature: not observed.

ジアセタール化合物
・化合物a:1,3:2,4-ビス-O-(p-メチルベンジリデン)-D-ソルビトール
・化合物b:1,3:2,4-ビス-O-(3’,4’-ジメチルベンジリデン)-D-ソルビトール
・化合物c:1,3:2,4-ビス-O-(p-n-プロピルベンジリデン)-1-n-プロピルソルビトール
・化合物d:1,3:2,4-ビス-O-(p-エチルベンジリデン)-D-ソルビトールと1,3:2,4-ビス-O-(3’,4’-ジメチルベンジリデン)-D-ソルビトールの7対3(質量比)の混合物
Diacetal compound / compound a: 1,3: 2,4-bis-O- (p-methylbenzylidene) -D-sorbitol compound b: 1,3: 2,4-bis-O- (3', 4') -Dimethylbenzylidene) -D-sorbitol compound c: 1,3: 2,4-bis-O- (pn-propylbenziliden) -1-n-propylsorbitol compound d: 1,3: 2,4 7: 3 (mass ratio) of -bis-O- (p-ethylbenzylidene) -D-sorbitol and 1,3: 2,4-bis-O- (3', 4'-dimethylbenzylidene) -D-sorbitol Mixture of

[実施例1]
オレフィン系の熱可塑性エラストマーとしてエクソン・モービル社製のVistamaxx3588FL(エラストマーA)100質量部とジアセタール化合物として1,3:2,4-ビス-O-(p-メチルベンジリデン)-D-ソルビトール(化合物a)0.05質量部を混合後、二軸押出機(株式会社テクノベル製KZW15TW-45MG-NH)を用いてバレル温度220℃で溶融混合した。押し出されたストランドを冷却し、ペレタイザーで切断することでペレット状の本発明のオレフィン系の熱可塑性エラストマー組成物を得た。
[Example 1]
ExxonMobil's Vistamaxx3588FL (elastomer A) 100 parts by mass as an olefin-based thermoplastic elastomer and 1,3: 2,4-bis-O- (p-methylbenzylidene) -D-sorbitol (compound a) as a diacetal compound. ) 0.05 parts by mass were mixed and then melt-mixed at a barrel temperature of 220 ° C. using a twin-screw extruder (KZW15TW-45MG-NH manufactured by Technobel Co., Ltd.). The extruded strands were cooled and cut with a pelletizer to obtain pelletized olefin-based thermoplastic elastomer composition of the present invention.

続いて、上記で得られたオレフィン系の熱可塑性エラストマー組成物を用いて、射出成形機(日精樹脂工業株式会社製NS40-5A)にて射出成形温度(加熱温度)220℃、金型温度(冷却温度)40℃の条件下で成形して、厚みが0.5mm、1.0mmの熱可塑性エラストマー成形体を得た。 Subsequently, using the olefin-based thermoplastic elastomer composition obtained above, an injection molding machine (NS40-5A manufactured by Nissei Plastic Industry Co., Ltd.) was used to inject molding temperature (heating temperature) 220 ° C. and mold temperature (mold temperature (NS40-5A)). Molding was performed under the condition of cooling temperature) 40 ° C. to obtain a thermoplastic elastomer molded product having a thickness of 0.5 mm and 1.0 mm.

上記で得られた成形体を評価試料として用いて、上記(2)に記載の方法によりヘイズ値を測定し、得られた結果を表1に示した。また、上記(3)に記載の方法に従って、成形体より短冊状の試験片を切り出し、引張試験を行い、その試験結果より引張弾性率、引張降伏応力及び引張破壊ひずみを求めて、表1に示した。 Using the molded product obtained above as an evaluation sample, the haze value was measured by the method described in (2) above, and the obtained results are shown in Table 1. Further, according to the method described in (3) above, a strip-shaped test piece is cut out from the molded body, a tensile test is performed, and the tensile elastic modulus, the tensile yield stress, and the tensile fracture strain are obtained from the test results, and Table 1 shows. Indicated.

[実施例2]
ジアセタール化合物の配合量を、0.1質量部に変えた以外は実施例1と同様に実施して、組成物及び成形体を調製し、得られた成形体を用いて実施例1と同様に試験を行い、得られたヘイズ値、引張弾性率、引張降伏応力及び引張破壊ひずみの結果を表1に示した。
[Example 2]
The same procedure as in Example 1 was carried out except that the blending amount of the diacetal compound was changed to 0.1 part by mass to prepare a composition and a molded product, and the obtained molded product was used in the same manner as in Example 1. The tests were performed and the results of the obtained haze value, tensile modulus, tensile yield stress and tensile fracture strain are shown in Table 1.

[実施例3]
ジアセタール化合物の配合量を、0.2質量部に変えた以外は実施例1と同様に実施して、組成物及び成形体を調製し、得られた成形体を用いて実施例1と同様に試験を行い、得られたヘイズ値、引張弾性率、引張降伏応力及び引張破壊ひずみの結果を表1に示した。
[Example 3]
The same procedure as in Example 1 was carried out except that the blending amount of the diacetal compound was changed to 0.2 parts by mass to prepare a composition and a molded product, and the obtained molded product was used in the same manner as in Example 1. The tests were performed and the results of the obtained haze value, tensile modulus, tensile yield stress and tensile fracture strain are shown in Table 1.

[実施例4]
ジアセタール化合物として、1,3:2,4-ビス-O-(p-メチルベンジリデン)-D-ソルビトール(化合物a)の代わりに1,3:2,4-ビス-O-(3’,4’-ジメチルベンジリデン)-D-ソルビトール(化合物b)を用いた以外は実施例2と同様に実施して、組成物及び成形体を調製し、得られた成形体を用いて実施例2と同様に試験を行い、得られたヘイズ値、引張弾性率、引張降伏応力及び引張破壊ひずみの結果を表1に示した。
[Example 4]
As a diacetal compound, 1,3: 2,4-bis-O- (3', 4) instead of 1,3: 2,4-bis-O- (p-methylbenzylidene) -D-sorbitol (compound a) The same procedure as in Example 2 was carried out except that'-dimethylbenzylidene) -D-sorbitol (compound b) was used to prepare a composition and a molded product, and the obtained molded product was used in the same manner as in Example 2. The results of the obtained haze value, tensile elastic modulus, tensile yield stress and tensile fracture strain are shown in Table 1.

[実施例5]
ジアセタール化合物として、1,3:2,4-ビス-O-(p-メチルベンジリデン)-D-ソルビトール(化合物a)の代わりに1,3:2,4-ビス-O-(p-n-プロピルベンジリデン)-1-n-プロピルソルビトール(化合物c)を用いた以外は実施例2と同様に実施して、組成物及び成形体を調製し、得られた成形体を用いて実施例2と同様に試験を行い、得られたヘイズ値、引張弾性率、引張降伏応力及び引張破壊ひずみの結果を表1に示した。
[Example 5]
As a diacetal compound, 1,3: 2,4-bis-O- (pn-) instead of 1,3: 2,4-bis-O- (p-methylbenzylidene) -D-sorbitol (compound a) The same procedure as in Example 2 was carried out except that propylbenzylidene) -1-n-propylsorbitol (compound c) was used to prepare a composition and a molded product, and the obtained molded product was used as the second embodiment. The same test was performed, and the results of the obtained haze value, tensile modulus, tensile yield stress and tensile fracture strain are shown in Table 1.

[実施例6]
ジアセタール化合物の配合量を、0.2質量部に変えた以外は実施例5と同様に実施して、組成物及び成形体を調製し、得られた成形体を用いて実施例5と同様に試験を行い、得られたヘイズ値、引張弾性率、引張降伏応力及び引張破壊ひずみの結果を表1に示した。
[Example 6]
The same procedure as in Example 5 was carried out except that the blending amount of the diacetal compound was changed to 0.2 parts by mass to prepare a composition and a molded product, and the obtained molded product was used in the same manner as in Example 5. The tests were performed and the results of the obtained haze value, tensile modulus, tensile yield stress and tensile fracture strain are shown in Table 1.

[実施例7]
ジアセタール化合物として、1,3:2,4-ビス-O-(p-メチルベンジリデン)-D-ソルビトール(化合物a)の代わりに1,3:2,4-ビス-O-(p-エチルベンジリデン)-D-ソルビトールと1,3:2,4-ビス-O-(3’,4’-ジメチルベンジリデン)-D-ソルビトールの7対3(質量比)の混合物(化合物d)を用いた以外は実施例2と同様に実施して、組成物及び成形体を調製し、得られた成形体を用いて実施例2と同様に試験を行い、得られたヘイズ値、引張弾性率、引張降伏応力及び引張破壊ひずみの結果を表1に示した。
[Example 7]
As a diacetal compound, 1,3: 2,4-bis-O- (p-ethylbenzylidene) instead of 1,3: 2,4-bis-O- (p-methylbenzylidene) -D-sorbitol (compound a) )-D-sorbitol and 1,3: 2,4-bis-O- (3', 4'-dimethylbenzylidene) -D-sorbitol 7: 3 (mass ratio) mixture (compound d) was used. Is carried out in the same manner as in Example 2, the composition and the molded product are prepared, and the obtained molded product is used in the same test as in Example 2, and the obtained haze value, tensile elastic modulus and tensile yield are obtained. The results of stress and tensile fracture strain are shown in Table 1.

[実施例8]
オレフィン系の熱可塑性エラストマーとして、Vistamaxx3588FL(エラストマーA)の代わりにエクソン・モービル社製のVistamaxx6102(エラストマーB)を用いた以外は実施例2と同様に実施して、組成物及び成形体を調製し、得られた成形体を用いて実施例2と同様に試験を行い、得られたヘイズ値、引張弾性率、引張降伏応力及び引張破壊ひずみの結果を表1に示した。
[Example 8]
The composition and the molded product were prepared in the same manner as in Example 2 except that Vistamaxx6102 (elastomer B) manufactured by Exxon Mobile Co., Ltd. was used instead of Vistamaxx3588FL (elastomer A) as the olefin-based thermoplastic elastomer. The same test as in Example 2 was carried out using the obtained molded product, and the results of the obtained haze value, tensile elastic modulus, tensile yield stress and tensile fracture strain are shown in Table 1.

[比較例1]
ジアセタール化合物を配合しないで実施例1と同様に実施して、組成物及び成形体を調製し、得られた成形体を用いて実施例1と同様に試験を行い、得られたヘイズ値、引張弾性率、引張降伏応力及び引張破壊ひずみの結果を表1に示した。
[Comparative Example 1]
The same procedure as in Example 1 was carried out without blending the diacetal compound to prepare a composition and a molded product, and the obtained molded product was used in the same test as in Example 1 to obtain a haze value and tension. The results of elastic modulus, tensile yield stress and tensile fracture strain are shown in Table 1.

[比較例2]
ジアセタール化合物を配合しないで実施例8と同様に実施して、組成物及び成形体を調製し、得られた成形体を用いて実施例8と同様に試験を行い、得られたヘイズ値、引張弾性率、引張降伏応力及び引張破壊ひずみの結果を表1に示した。
[Comparative Example 2]
The same procedure as in Example 8 was carried out without blending the diacetal compound to prepare a composition and a molded product, and the obtained molded product was used in the same test as in Example 8 to obtain the haze value and tensile strength. The results of elastic modulus, tensile yield stress and tensile fracture strain are shown in Table 1.

Figure 0007064130000005
Figure 0007064130000005

表1の結果より、本発明の熱可塑性エラストマー組成物を用いることによりヘイズ値が大きく低下し、透明性が向上していることがわかる。また、機械的特性に関しては、本発明の組成物を用いることによる低下は全く認められていない。即ち、本発明の熱可塑性エラストマー組成物が、本来の熱可塑性エラストマーとしての機械的特性を保持しつつ、透明性を大幅に改善できていることがわかる。 From the results in Table 1, it can be seen that the haze value is greatly reduced and the transparency is improved by using the thermoplastic elastomer composition of the present invention. Further, regarding the mechanical properties, no deterioration due to the use of the composition of the present invention was observed. That is, it can be seen that the thermoplastic elastomer composition of the present invention can significantly improve the transparency while maintaining the mechanical properties of the original thermoplastic elastomer.

本発明の熱可塑性エラストマーの透明性改善方法及びオレフィン系の熱可塑性エラストマー組成物は、熱可塑性エラストマーの透明性改善に大きな効果を発揮し、その方法や組成物を用いることにより従来使用することが難しかった視認性の必要性や意匠性の観点より透明性の必要とされる医療用途、被覆材、包装材、玩具などの用途でもオレフィン系の熱可塑性エラストマーを使用することが可能となる。また、オレフィン系のエラストマーの特徴である軽量性、リサイクル性等の利点を活かして、成形品やシート、フィルムとして、自動車部材、電気部材、機械部品、日常雑貨など様々な用途で利用することができる。 The method for improving the transparency of a thermoplastic elastomer and the olefin-based thermoplastic elastomer composition of the present invention exert a great effect on improving the transparency of a thermoplastic elastomer, and can be conventionally used by using the method or composition. Olefin-based thermoplastic elastomers can also be used in medical applications, covering materials, packaging materials, toys, etc., where transparency is required from the viewpoint of visibility and design, which were difficult. In addition, by taking advantage of the features of olefin-based elastomers such as light weight and recyclability, it can be used as molded products, sheets, and films for various purposes such as automobile parts, electrical parts, machine parts, and daily miscellaneous goods. can.

Claims (7)

透明性に優れたオレフィン系の熱可塑性エラストマー組成物であって、
オレフィン系の熱可塑性エラストマーが、該熱可塑性エラストマーの全質量に対して60~99質量%のプロピレン誘導単位と、該熱可塑性エラストマーの全質量に対して1~40質量%のエチレン誘導単位及び/又は炭素数4~10のα-オレフィン誘導単位からなる共重合体であり、且つ、
示差走査熱量分析で測定した融解熱量が15J/g以上、50J/g以下の結晶性を有する
オレフィン系の熱可塑性エラストマー100質量部に対して、下記一般式(1)で示されるジアセタール化合物を0.05~5.0質量部を含有することを特徴とするオレフィン系の熱可塑性エラストマー組成物。
Figure 0007064130000006
[式(1)中、R及びRは、同一又は異なって、それぞれ、水素原子、直鎖状若しくは分岐鎖状の炭素数1~4のアルキル基、直鎖状若しくは分岐鎖状の炭素数1~4のアルコキシ基、直鎖状若しくは分岐鎖状の炭素数1~4のアルコキシカルボニル基又はハロゲン原子を示す。Rは、水素原子、直鎖状若しくは分岐鎖状の炭素数1~4のアルキル基、直鎖状若しくは分岐鎖状の炭素数2~4のアルケニル基又は直鎖状若しくは分岐鎖状の炭素数1~4のヒドロキシアルキル基を示す。m及びnは、それぞれ1~5の整数を示す。pは0又は1を示す。
An olefin-based thermoplastic elastomer composition having excellent transparency.
The olefin-based thermoplastic elastomer contains 60 to 99% by mass of propylene-inducing units with respect to the total mass of the thermoplastic elastomer, and 1 to 40% by mass of ethylene-inducing units with respect to the total mass of the thermoplastic elastomer. Alternatively, it is a copolymer composed of an α-olefin inducing unit having 4 to 10 carbon atoms, and
The heat of fusion measured by differential scanning calorimetry has crystallinity of 15 J / g or more and 50 J / g or less.
An olefin-based thermoplastic elastomer composition containing 0.05 to 5.0 parts by mass of a diacetal compound represented by the following general formula (1) with respect to 100 parts by mass of the olefin-based thermoplastic elastomer. ..
Figure 0007064130000006
[In the formula (1), R 1 and R 2 are the same or different, respectively, a hydrogen atom, a linear or branched alkyl group having 1 to 4 carbon atoms, and a linear or branched carbon. It indicates an alkoxy group having the number of 1 to 4, a linear or branched alkoxycarbonyl group having 1 to 4 carbon atoms, or a halogen atom. R3 is a hydrogen atom , a linear or branched-chain alkyl group having 1 to 4 carbon atoms, a linear or branched-chain alkenyl group having 2 to 4 carbon atoms, or a linear or branched-chain carbon. The number 1 to 4 hydroxyalkyl groups are shown. m and n represent integers of 1 to 5, respectively. p indicates 0 or 1.
示差走査熱量分析で測定した最大の融解ピーク温度が115℃以下である、又は示差走査熱量分析の測定では融解ピーク温度が観察されない、請求項1に記載のオレフィン系の熱可塑性エラストマー組成物。 The olefin-based thermoplastic elastomer composition according to claim 1, wherein the maximum melting peak temperature measured by differential scanning calorimetry is 115 ° C. or lower, or no melting peak temperature is observed by differential scanning calorimetry. ジアセタール化合物が、前記一般式(1)において、R及びRが、同一又は異なって、メチル基又はエチル基であり、かつ、Rが水素原子であり、m及びnが1又は2の整数であり、pが1である、請求項1又は2に記載のオレフィン系の熱可塑性エラストマー組成物。 In the general formula (1), the diacetal compound has R 1 and R 2 which are the same or different, a methyl group or an ethyl group, R 3 is a hydrogen atom, and m and n are 1 or 2. The olefin-based thermoplastic elastomer composition according to claim 1 or 2 , which is an integer and p is 1. ジアセタール化合物が、前記一般式(1)において、R及びRが、同一又は異なって、プロピル基又はプロポキシ基であり、かつ、Rがプロピル基又はプロペニル基であり、m及びnが1であり、pが1である、請求項1又は2に記載のオレフィン系の熱可塑性エラストマー組成物。 In the diacetal compound, in the above general formula (1), R 1 and R 2 are the same or different, a propyl group or a propoxy group, R 3 is a propyl group or a propenyl group, and m and n are 1. The olefin-based thermoplastic elastomer composition according to claim 1 or 2 , wherein p is 1. ジアセタール化合物の含有量が、熱可塑性エラストマー100質量部に対して0.05~1.0質量部である、請求項1~の何れかに記載のオレフィン系の熱可塑性エラストマー組成物。 The olefin-based thermoplastic elastomer composition according to any one of claims 1 to 4 , wherein the content of the diacetal compound is 0.05 to 1.0 part by mass with respect to 100 parts by mass of the thermoplastic elastomer. 請求項1~の何れかに記載のオレフィン系の熱可塑性エラストマー組成物を原料とする、透明性に優れた熱可塑性エラストマー成形体。 A thermoplastic elastomer molded product having excellent transparency, using the olefin-based thermoplastic elastomer composition according to any one of claims 1 to 5 as a raw material. 熱可塑性エラストマーの透明性の改善方法であって、
オレフィン系の熱可塑性エラストマー100質量部に対してジアセタール化合物を0.05~5.0質量部含有させること、更に、
前記オレフィン系の熱可塑性エラストマーが、該熱可塑性エラストマーの全質量に対して60~99質量%のプロピレン誘導単位と、該熱可塑性エラストマーの全質量に対して1~40質量%のエチレン誘導単位及び/又は炭素数4~10のα-オレフィン誘導単位からなる共重合体であり、更に、示差走査熱量分析で測定した融解熱量が15J/g以上、50J/g以下の結晶性を有し、且つ、
ジアセタール化合物が、下記一般式(1)で示される化合物であることを特徴とする改善方法。
Figure 0007064130000007
[式(1)中、R及びRは、同一又は異なって、それぞれ、水素原子、直鎖状若しくは分岐鎖状の炭素数1~4のアルキル基、直鎖状若しくは分岐鎖状の炭素数1~4のアルコキシ基、直鎖状若しくは分岐鎖状の炭素数1~4のアルコキシカルボニル基又はハロゲン原子を示す。Rは、水素原子、直鎖状若しくは分岐鎖状の炭素数1~4のアルキル基、直鎖状若しくは分岐鎖状の炭素数2~4のアルケニル基又は直鎖状若しくは分岐鎖状の炭素数1~4のヒドロキシアルキル基を示す。m及びnは、それぞれ1~5の整数を示す。pは0又は1を示す。]
A method for improving the transparency of thermoplastic elastomers.
To contain 0.05 to 5.0 parts by mass of the diacetal compound with respect to 100 parts by mass of the olefin-based thermoplastic elastomer, further,
The olefin-based thermoplastic elastomer contains 60 to 99% by mass of propylene-inducing units with respect to the total mass of the thermoplastic elastomer, and 1 to 40% by mass of ethylene-inducing units with respect to the total mass of the thermoplastic elastomer. / Or a copolymer composed of α-olefin-inducing units having 4 to 10 carbon atoms, further having a crystallinity of 15 J / g or more and 50 J / g or less in melting heat measured by differential scanning calorific value analysis, and ,
An improvement method, wherein the diacetal compound is a compound represented by the following general formula (1).
Figure 0007064130000007
[In the formula (1), R 1 and R 2 are the same or different, respectively, a hydrogen atom, a linear or branched alkyl group having 1 to 4 carbon atoms, and a linear or branched carbon. It indicates an alkoxy group having the number of 1 to 4, a linear or branched alkoxycarbonyl group having 1 to 4 carbon atoms, or a halogen atom. R3 is a hydrogen atom , a linear or branched-chain alkyl group having 1 to 4 carbon atoms, a linear or branched-chain alkenyl group having 2 to 4 carbon atoms, or a linear or branched-chain carbon. The number 1 to 4 hydroxyalkyl groups are shown. m and n represent integers of 1 to 5, respectively. p indicates 0 or 1. ]
JP2018030469A 2018-02-23 2018-02-23 Olefin-based thermoplastic elastomer with excellent transparency Active JP7064130B2 (en)