JP2005212135A - Packaging material - Google Patents
Packaging material Download PDFInfo
- Publication number
- JP2005212135A JP2005212135A JP2004018287A JP2004018287A JP2005212135A JP 2005212135 A JP2005212135 A JP 2005212135A JP 2004018287 A JP2004018287 A JP 2004018287A JP 2004018287 A JP2004018287 A JP 2004018287A JP 2005212135 A JP2005212135 A JP 2005212135A
- Authority
- JP
- Japan
- Prior art keywords
- metal
- ink
- thin film
- packaging material
- metal thin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、非金属性の基材上に金属光沢領域を有する印刷層又は塗布層を設けた包装材であって、金属探知器に非感応であることを特徴とする包装材に関する。 The present invention relates to a packaging material in which a printed layer or a coating layer having a metallic gloss region is provided on a nonmetallic substrate, and is insensitive to a metal detector.
一般的に食品包装等では包装時の異物（金属）混入検査に金属探知器を使用している。このため、包装材にアルミ箔の貼合紙を使用したり、メタリックインキを塗布または印刷して金属光沢領域を設けた場合、金属探知器に感応し、異物（金属）混入検査が出来なくなる。よって、金属探知が必要とされる用途の包装材には、金属光沢領域を設けることが出来なかった。また、チョコレート包装などでは、アルミ箔包装専用の金属探知器が必要であった。 In general, food detectors use metal detectors for inspection of foreign matter (metal) contamination during packaging. For this reason, when an aluminum foil bonding paper is used for the packaging material, or a metallic gloss region is provided by applying or printing metallic ink, it is sensitive to a metal detector, and foreign matter (metal) contamination inspection cannot be performed. Therefore, a metallic luster region could not be provided in a packaging material for applications that require metal detection. For chocolate packaging, a metal detector dedicated to aluminum foil packaging is required.
従来の包装材の金属光沢領域の形成においては、メタリックインキの印刷による方法がある。またアルミ箔の貼合紙を使用したり、基材フィルムへアルミニウムを蒸着する方法がある。メタリックインキには金インキ、銀インキと呼ばれるものが含まれ、顔料としてアルミペースト、ブロンズパウダー等を混合したもの等が使用される。非特許文献１には金インキ、銀インキの一般的な性状が記載されている。非特許文献２には銀インキの顔料として主として使用されるアルミニウム粉の製法や性質が記載されている。 In forming a metallic gloss region of a conventional packaging material, there is a method by printing with metallic ink. In addition, there are methods of using aluminum foil bonding paper or vapor depositing aluminum on a base film. Metallic ink includes what are called gold ink and silver ink, and a mixture of aluminum paste, bronze powder or the like is used as a pigment. Non-Patent Document 1 describes general properties of gold ink and silver ink. Non-Patent Document 2 describes the production method and properties of aluminum powder mainly used as a pigment for silver ink.
これらの方法では、意匠性の高い金属光沢領域を形成するためには、相当量の金属または金属粉を使用するため、金属探知器に感応するデメリットがある。 In these methods, since a considerable amount of metal or metal powder is used to form a metallic luster region having high design properties, there is a demerit that is sensitive to a metal detector.
特許文献１には、シート状物の任意表面に、金属粉末を主とする金属粉末固着層を設けたことを特徴とする金属光沢を有するシートが記載されている。該シートはアルミニウム箔と同等の金属光沢を有し、しかも金属探知器に反応しないとされている。該金属粉末固着層を形成するには、該公報の段落１２によれば、金属粉末とバインダー及び揮発性溶剤からなる混合液を付着させた後、該揮発性溶剤を乾燥させる方法による。そして段落１６によれば金属粉末は、金属光沢を発生させる金属の粉末であれば、あらゆる金属が適用されるとされているが、前記したように、使用する金属粉によっては相当量の金属を使用しなければ金属光沢が得られず、金属探知器に感応してしまう問題がある。
本発明は、金属光沢領域を持つ包装材でありながら、それ自身は金属探知器に感応せず、内容物を充填後の異物（金属）混入検査が容易に行える包装材と、その製造方法を提供することを課題とする。 The present invention is a packaging material having a metallic luster region, which itself is not sensitive to a metal detector, and can be easily subjected to foreign matter (metal) contamination inspection after filling the contents, and a manufacturing method thereof. The issue is to provide.
発明者は、非金属性基材上に、結着樹脂と金属薄膜細片を含有するインキを塗布又は印刷することによって金属光沢領域を形成すると、この金属光沢領域は優れた金属光沢を有しながら金属探知器に非感応であることを見出し、上記課題を解決した。 When the inventor forms a metallic luster area by applying or printing an ink containing a binder resin and a thin metal film strip on a nonmetallic substrate, the metallic luster area has an excellent metallic luster. However, they found it insensitive to metal detectors and solved the above problems.
本発明は、従来金属探知器による異物（金属）混入検査を必要とする包装材では得ることが難しかった金属光沢領域の形成を可能とする。また金属探知器非感応型金属光沢領域を、金属薄膜インキを塗布するか又は印刷するという方法で安価かつ高速に大量生産できる。さらに、グラビア印刷を行うことにより、金属光沢領域に連続階調をもたせたグラデーションを形成することも可能である。
その結果、金属光沢領域をもつ包装材であっても、金属探知器による異物（金属）混入検査を行うことができ、また包装材に偽造防止効果をも付与し、さらに意匠デザインの自由度が格段に向上するという顕著な効果を奏する。
The present invention makes it possible to form a metallic luster region that has been difficult to obtain with a packaging material that conventionally requires a foreign object (metal) contamination inspection by a metal detector. Further, the metal detector non-sensitive metal gloss region can be mass-produced at a low cost and at a high speed by a method of applying a metal thin film ink or printing. Furthermore, by performing gravure printing, it is possible to form a gradation with continuous gradation in the metallic gloss region.
As a result, even a packaging material with a metallic luster area can be inspected for foreign matter (metal) contamination by a metal detector, and also has an anti-counterfeiting effect on the packaging material. There is a remarkable effect of significant improvement.
１．金属薄膜インキ
本発明で使用する金属薄膜インキは、金属薄膜細片、結着樹脂、添加剤および溶剤からなる。通常メタリックインキには金属粉が使用されるが、金属薄膜細片を使用した場合は、該インキを塗布した際に被塗物表面に対して金属薄膜の面が平行方向に配向する結果、金属含有量が少ないにも関わらず、従来の金属粉を使用するメタリックインキでは得られない高輝度の鏡面状金属光沢が得られる。本明細書ではこのインキを金属薄膜インキと称する。
1. Metal thin film ink The metal thin film ink used in the present invention comprises a metal thin film strip, a binder resin, an additive and a solvent. Normally, metallic powder is used for metallic inks, but when thin metal thin strips are used, the surface of the metal thin film is oriented parallel to the surface of the object when the ink is applied. Despite its low content, a high-brightness mirror-like metallic luster that cannot be obtained with metallic inks using conventional metal powders can be obtained. In the present specification, this ink is referred to as a metal thin film ink.
（１）金属薄膜細片
金属薄膜細片の金属としては、アルミニウム、金、銀、銅、真鍮、チタン、クロム、ニッケル、ニッケルクロム、ステンレス等を使用することができる。金属を薄膜にする方法としては、アルミニウムのように融点の低い金属の場合は蒸着による方法が挙げられる。アルミニウム、金、銀、銅など展性を有する場合は箔に加工する方法が挙げられる。融点が高く展性も持たない金属の場合は、スパッタリング等を挙げることができる。これらの中でも、蒸着金属薄膜から得た金属薄膜細片が好ましく用いられる。
(1) Metal thin film strip As the metal of the metal thin film strip, aluminum, gold, silver, copper, brass, titanium, chromium, nickel, nickel chromium, stainless steel, or the like can be used. As a method for forming a metal into a thin film, vapor deposition may be used in the case of a metal having a low melting point such as aluminum. In the case of having malleability such as aluminum, gold, silver and copper, a method of processing into a foil can be mentioned. In the case of a metal having a high melting point and no malleability, sputtering or the like can be mentioned. Among these, the metal thin film strip obtained from the vapor deposition metal thin film is preferably used.
金属薄膜の厚さは、０．０１〜０．１μｍが好ましく、さらに好ましくは０．０２〜０．０８μｍである。コーティング剤中に分散させる金属薄膜細片の大きさ（薄膜面の長辺の長さ）が５〜２５μｍが好ましく、さらに好ましくは１０〜１５μｍである。大きさが５μｍ未満の場合は、塗膜の輝度が不十分となり、２５μｍを超えると金属薄膜細片が配向しにくくなるので輝度が低下する。また金属薄膜インキを、グラビア方式あるいはスクリーン印刷方式で塗布する場合は、版の目詰まりの原因となる。 The thickness of the metal thin film is preferably 0.01 to 0.1 μm, more preferably 0.02 to 0.08 μm. The size of the metal thin film pieces dispersed in the coating agent (the length of the long side of the thin film surface) is preferably from 5 to 25 μm, more preferably from 10 to 15 μm. When the size is less than 5 μm, the brightness of the coating film is insufficient, and when it exceeds 25 μm, the metal thin film strips are difficult to be oriented, so that the brightness is lowered. Further, when the metal thin film ink is applied by a gravure method or a screen printing method, it may cause clogging of the plate.
以下に金属薄膜細片の作成方法を、蒸着法を例として説明する。
金属を蒸着する支持体フィルムには、ポリオレフィンフィルムやポリエステルフィルムなどを使用することができる。まず支持体フィルム上に塗布によって剥離層を設けた後、剥離層上に所定の厚さになるよう金属を蒸着する。蒸着膜面には、酸化を防ぐためトップコート層を塗布する。剥離層およびトップコート層形成用のコーティング剤は同一のものを使用することができる。
Hereinafter, a method for producing a metal thin film strip will be described by taking a vapor deposition method as an example.
A polyolefin film, a polyester film, etc. can be used for the support body film which vapor-deposits a metal. First, a release layer is provided on the support film by coating, and then a metal is deposited on the release layer so as to have a predetermined thickness. A top coat layer is applied to the surface of the deposited film to prevent oxidation. The same coating agent for forming the release layer and the top coat layer can be used.
剥離層、あるいはトップコート層に使用する樹脂は、特に限定されない。具体的にはたとえば、セルロース誘導体、アクリル樹脂、ビニル系樹脂、ポリアミド、ポリエステル、ＥＶＡ樹脂、塩素化ポリプロピレン、塩素化ＥＶＡ樹脂、石油系樹脂等を挙げることができる。またこれらの樹脂を溶解する溶剤としては、トルエン、キシレン等の芳香族系炭化水素、ｎ−ヘキサン、シクロヘキサン等の脂肪族または脂環式炭化水素、酢酸エチル、酢酸プロピル等のエステル類、メタノール、エタノール、イソプロピルアルコール等のアルコール類、アセトン、メチルエチルケトン等のケトン類、エチレングリコールモノエチルエーテル、プロピレングリコールモノメチルエーテル等のアルキレングリコールモノアルキルエーテル等を使用することができる。 Resin used for a peeling layer or a topcoat layer is not specifically limited. Specific examples include cellulose derivatives, acrylic resins, vinyl resins, polyamides, polyesters, EVA resins, chlorinated polypropylene, chlorinated EVA resins, petroleum resins, and the like. Solvents for dissolving these resins include aromatic hydrocarbons such as toluene and xylene, aliphatic or alicyclic hydrocarbons such as n-hexane and cyclohexane, esters such as ethyl acetate and propyl acetate, methanol, Alcohols such as ethanol and isopropyl alcohol, ketones such as acetone and methyl ethyl ketone, alkylene glycol monoalkyl ether such as ethylene glycol monoethyl ether and propylene glycol monomethyl ether, and the like can be used.
上記金属蒸着フィルムを、剥離層およびトップコート層を溶解する溶剤中に浸漬して撹拌し、金属蒸着膜を支持体フィルムから剥離した後、さらに撹拌して金属薄膜細片の大きさを約１５０μｍとし、濾別、乾燥する。溶剤は、剥離層あるいはトップコート層に使用する樹脂を溶解するものであること以外に、特に限定はない。 The metal vapor-deposited film is immersed in a solvent that dissolves the release layer and the topcoat layer and stirred. After the metal vapor-deposited film is peeled from the support film, the metal vapor-deposited film is further stirred to reduce the size of the metal thin film strip to about 150 μm. And filtered and dried. The solvent is not particularly limited except that it dissolves the resin used for the release layer or the topcoat layer.
金属薄膜をスパッタリングで作成した場合も、上記と同様の方法で金属薄膜細片とすることができる。金属箔を用いる場合は、溶剤中でそのまま撹拌機で所定の大きさに粉砕すればよい。 Even when the metal thin film is formed by sputtering, the metal thin film can be formed by the same method as described above. When using a metal foil, it may be pulverized to a predetermined size with a stirrer as it is in a solvent.
金属薄膜細片は、金属薄膜インキ中における分散性を高めるために表面処理するのが好ましい。表面処理剤としては、ステアリン酸、オレイン酸、パルミチン酸等の有機脂肪酸、メチルシリルイソシアネート、ニトロセルロース、セルロースアセテートプロピオネート、セルロースアセテートブチレート、エチルセルロース等のセルロース誘導体が挙げられる。 The metal thin film strip is preferably surface-treated in order to enhance dispersibility in the metal thin film ink. Examples of the surface treatment agent include organic fatty acids such as stearic acid, oleic acid, and palmitic acid, and cellulose derivatives such as methylsilyl isocyanate, nitrocellulose, cellulose acetate propionate, cellulose acetate butyrate, and ethyl cellulose.
（２）結着樹脂
結着樹脂は、従来の塗料、グラビアインキ、フレキソインキ、あるいはスクリーンインキ等に通常使われているものを使用することができる。具体的にはたとえば、（メタ）アクリル樹脂、ポリエステル、ポリアミド、ポリウレタン、尿素樹脂、メラミン樹脂、エポキシ樹脂、ロジン変性マレイン酸樹脂、石油系樹脂、ポリスチレン、スチレン−マレイン酸樹脂、セラック、アルキッド樹脂等を挙げることができる。
(2) Binder Resin As the binder resin, those usually used in conventional paints, gravure inks, flexo inks, screen inks, and the like can be used. Specifically, for example, (meth) acrylic resin, polyester, polyamide, polyurethane, urea resin, melamine resin, epoxy resin, rosin-modified maleic acid resin, petroleum resin, polystyrene, styrene-maleic acid resin, shellac, alkyd resin, etc. Can be mentioned.
（３）添加剤
本発明の高輝度コーティング剤には、必要に応じて、従来の塗料、グラビアインキ、フレキソインキ、あるいはスクリーンインキ等に使用されている各種添加剤を使用することができる。このような添加剤としては、着色用顔料、染料、ワックス、可塑剤、レベリング剤、界面活性剤、分散剤、消泡剤、キレート化剤等を挙げることができる。
(3) Additives Various additives that are used in conventional paints, gravure inks, flexographic inks, screen inks, and the like can be used as necessary for the high-brightness coating agent of the present invention. Examples of such additives include coloring pigments, dyes, waxes, plasticizers, leveling agents, surfactants, dispersants, antifoaming agents, chelating agents, and the like.
（４）溶剤
本発明の金属薄膜インキに使用する溶剤もまた、従来の塗料、グラビアインキ、フレキソインキ、あるいはスクリーンインキ等に使われている公知慣用の溶剤を使用することができる。具体的にはたとえば、トルエン、キシレン等の芳香族系炭化水素、ｎ−ヘキサン、シクロヘキサン等の脂肪族または脂環式炭化水素、酢酸エチル、酢酸プロピル等のエステル類、メタノール、エタノール、イソプロピルアルコール等のアルコール類、アセトン、メチルエチルケトン等のケトン類、エチレングリコールモノエチルエーテル、プロピレングリコールモノメチルエーテル等のアルキレングリコールモノアルキルエーテル等を挙げることができる。
(4) Solvent The solvent used for the metal thin film ink of the present invention can also be a known and commonly used solvent used in conventional paints, gravure inks, flexographic inks, screen inks, and the like. Specifically, for example, aromatic hydrocarbons such as toluene and xylene, aliphatic or alicyclic hydrocarbons such as n-hexane and cyclohexane, esters such as ethyl acetate and propyl acetate, methanol, ethanol, isopropyl alcohol and the like Alcohols, ketones such as acetone and methyl ethyl ketone, and alkylene glycol monoalkyl ethers such as ethylene glycol monoethyl ether and propylene glycol monomethyl ether.
（５）金属薄膜インキの調整方法
一般にインキの配合原料を安定して分散させるには、ロールミル、ボールミル、ビーズミル、あるいはサンドミル等を使用して練肉することにより、顔料その他添加剤をサブミクロンまで微粒子化する方法が用いられる。
(5) Preparation method of metal thin film ink In general, in order to stably disperse the ink raw materials, the pigment and other additives can be sub-micron by kneading using a roll mill, ball mill, bead mill, or sand mill. A method of making fine particles is used.
しかし、本発明の金属薄膜インキにおいては、金属光沢を発現させるために配合する金属薄膜細片は５〜２５μｍの大きさを必要とし、上記練肉を行った場合は金属薄膜細片が微粒子化しすぎてしまい、金属光沢が極端に低下する。したがって、本発明においては練肉は行わず、単に上記配合原料を混合し、ターボミキサー等の撹拌機により撹拌して金属薄膜を５〜２５μｍの大きさに粉砕して金属薄膜インキとする。その際は分散性を向上させる目的で、前記したように表面処理剤を添加して混合・撹拌することが好ましい。 However, in the metal thin film ink of the present invention, the metal thin film strip to be blended in order to develop a metallic luster requires a size of 5 to 25 μm. Too much and the metallic luster is extremely lowered. Therefore, in the present invention, kneaded meat is not used, the above blended raw materials are simply mixed and stirred with a stirrer such as a turbo mixer to pulverize the metal thin film to a size of 5 to 25 μm to obtain a metal thin film ink. In that case, for the purpose of improving the dispersibility, it is preferable to add the surface treatment agent as described above, and mix and stir.
２．アルミペーストインキ（従来の銀インキ。参考）
従来使われているアルミペーストインキについて以下に説明する。本インキは粒径が６〜２０μｍくらいのアルミペースト、結着樹脂、添加剤、および溶剤からなる。
（１）アルミペースト
非特許文献２に記載のアルミニウム粉が主な顔料として使用されている。リーフィング、ノンリーフィングいずれをも用いることができる。
（２）結着樹脂
結着樹脂は、従来の塗料、グラビアインキ、フレキソインキあるいはスクリーンインキ等に通常使われている物を使用することができる。具体的には例えば（メタ）アクリル樹脂、ポリエステル、ポリアミド、ポリウレタン、尿素樹脂、メラミン樹脂、エポキシ樹脂、ロジン変性マレイン酸樹脂、石油系樹脂、ポリスチレン、スチレン−マレイン酸樹脂、セラック、アルキッド樹脂等を挙げることができる。
（３）添加剤
ペーストインキには必要に応じて従来の塗料、グラビアインキ、フレキソインキ、あるいはスクリーンインキ等に使用されている各種添加剤を使用することができる。このような添加剤としては、着色用顔料、染料、ワックス、可塑剤、レベリング剤、界面活性剤、分散剤、消泡剤、キレート化剤等を挙げることができる。
（４）溶剤
ペーストインキに使用する溶剤は、従来の塗料、グラビアインキ、フレキソインキ、あるいはスクリーンインキ等に使われているものを使用することができる。具体的には、トルエン、キシレン等の芳香族系炭化水素、ｎ−ヘキサン、シクロヘキサン等の脂肪族または脂環式炭化水素、酢酸エチル、酢酸プロピル等のエステル類、メタノール、エタノール、イソプロピルアルコール等のアルコール類、アセトン、メチルエチルケトン等のケトン類、エチレングリコールモノエチルエーテル、プロピレングリコールモノメチルエーテル等のアルキレングリコールモノアルキルエーテル等が挙げられる。
2. Aluminum paste ink (conventional silver ink. Reference)
The conventionally used aluminum paste ink will be described below. This ink consists of an aluminum paste having a particle size of about 6 to 20 μm, a binder resin, an additive, and a solvent.
(1) Aluminum paste Aluminum powder described in Non-Patent Document 2 is used as a main pigment. Either leafing or non-leafing can be used.
(2) Binder Resin As the binder resin, those usually used in conventional paints, gravure inks, flexo inks, screen inks and the like can be used. Specifically, for example, (meth) acrylic resin, polyester, polyamide, polyurethane, urea resin, melamine resin, epoxy resin, rosin-modified maleic acid resin, petroleum resin, polystyrene, styrene-maleic acid resin, shellac, alkyd resin, etc. Can be mentioned.
(3) Additives Various additives used in conventional paints, gravure inks, flexographic inks, screen inks, and the like can be used as necessary for the paste ink. Examples of such additives include coloring pigments, dyes, waxes, plasticizers, leveling agents, surfactants, dispersants, antifoaming agents, chelating agents, and the like.
(4) Solvent As the solvent used for the paste ink, those used in conventional paints, gravure inks, flexographic inks, screen inks, and the like can be used. Specifically, aromatic hydrocarbons such as toluene and xylene, aliphatic or alicyclic hydrocarbons such as n-hexane and cyclohexane, esters such as ethyl acetate and propyl acetate, methanol, ethanol, isopropyl alcohol, etc. Examples include alcohols, ketones such as acetone and methyl ethyl ketone, and alkylene glycol monoalkyl ethers such as ethylene glycol monoethyl ether and propylene glycol monomethyl ether.
３．包装材
（１）基材
本発明においては、基材としては、紙、オレフィン、ポリエステル等、従来からの公知慣用のフィルム等を使用することができる。本発明による金属探知器非感応型包装材は、印刷層の一部に金属光沢領域を設けること以外は、公知公用の包装材と同様にして製造することが出来る。
3. Packaging Material (1) Substrate In the present invention, conventionally known films such as paper, olefin and polyester can be used as the substrate. The metal detector non-sensitive packaging material according to the present invention can be produced in the same manner as a publicly known packaging material except that a metallic gloss region is provided in a part of the printed layer.
（２）金属光沢領域の形成
本発明の包装材の金属光沢領域は、基材の片面に金属薄膜インキを塗布又は印刷して形成する。従来行われている、金属箔と基材との貼り合わせや、金属の蒸着、スパッタリングによる方法では設備が大がかりになってしまうような大面積の金属光沢領域を、塗布又は印刷という高速かつ安価な方法で大量生産することができる。
(2) Formation of metallic luster region The metallic luster region of the packaging material of the present invention is formed by applying or printing a metal thin film ink on one side of the substrate. High speed and low cost of coating or printing a large area of metallic luster that would require a large facility in the conventional methods of bonding metal foil and substrate, metal deposition, and sputtering. It can be mass-produced by the method.
塗布方法としては、ロールコート、グラビアコート、カーテンコート、スプレーコート、ダイコート等、通常の塗装方式が挙げられる。これらの他に、グラビア印刷、フレキソ印刷、あるいはスクリーン印刷等の印刷方式を使用できることもできる。印刷方式によるコーティングでは版を使用するところから、全面塗布ばかりでなく任意の場所に、任意のパターンを形成した部分金属光沢領域を作成することができる。また、グラビア印刷を行う場合には、金属光沢領域の光反射率に連続階調をもたせたグラデーションを作成することもできる。本発明の金属光沢領域を有する包装材を使用すれば、単に金属光沢を付与するだけでなく、グラデーションによる偽造防止効果を付与する事も可能となり、意匠デザインの自由度が格段に向上する。 Examples of the coating method include usual coating methods such as roll coating, gravure coating, curtain coating, spray coating, and die coating. In addition to these, printing methods such as gravure printing, flexographic printing, and screen printing can also be used. Since the printing method uses a plate, it is possible to create a partial metallic gloss region in which an arbitrary pattern is formed not only on the entire surface but also at an arbitrary location. Further, when performing gravure printing, it is also possible to create a gradation in which a continuous gradation is given to the light reflectance of the metallic gloss region. If the packaging material having the metallic gloss region of the present invention is used, it is possible not only to impart metallic luster but also to impart an anti-counterfeit effect by gradation, and the design design freedom is greatly improved.
以下、実施例を用いて本発明をさらに具体的に説明する。なお、特に断らない限り、部および％はそれぞれ質量部および質量％を表す。 Hereinafter, the present invention will be described more specifically with reference to examples. Unless otherwise specified, parts and% represent parts by mass and% by mass, respectively.
［金属薄膜インキの調製］
（１）アルミニウム薄膜細片
ニトロセルロース（旭化成株式会社製ＨＩＧ７）を、酢酸エチル：イソプロピルアルコール＝６：４の混合溶剤に溶解して６％溶液とした。該溶液を、スクリーン線数１７５線／インチ、セル深度２５μｍのグラビア版でポリエステルフィルム上に塗布して剥離層を形成した。十分乾燥した後、剥離層上に厚さが０．０４μｍとなるようにアルミニウムを蒸着し、蒸着膜面に、剥離層に使用したものと同じニトロセルロース溶液を、剥離層の場合と同じ条件で塗布し、トップコート層を形成した。
[Preparation of metal thin film ink]
(1) Aluminum thin film strip Nitrocellulose (HIG7 manufactured by Asahi Kasei Corporation) was dissolved in a mixed solvent of ethyl acetate: isopropyl alcohol = 6: 4 to obtain a 6% solution. The solution was applied onto a polyester film with a gravure plate having a screen line number of 175 lines / inch and a cell depth of 25 μm to form a release layer. After sufficiently drying, aluminum is vapor-deposited on the release layer to a thickness of 0.04 μm, and the same nitrocellulose solution as that used for the release layer is applied to the deposited film surface under the same conditions as in the release layer. The top coat layer was formed by coating.
上記蒸着フィルムを、酢酸エチル：イソプロピルアルコール＝６：４の混合溶剤中に浸積してポリエステルフィルムからアルミニウム蒸着膜を剥離したのち、大きさが約１５０μｍとなるよう撹拌機でアルミニウム蒸着膜を粉砕し、アルミニウム薄膜細片を調製した。 The above deposited film is immersed in a mixed solvent of ethyl acetate: isopropyl alcohol = 6: 4 and the aluminum deposited film is peeled off from the polyester film, and then the aluminum deposited film is pulverized with a stirrer so that the size becomes about 150 μm. An aluminum thin film strip was prepared.
（２）アルミニウム薄膜細片スラリー
アルミニウム薄膜細片・・・・１０部、
酢酸エチル・・・・・・・・・３５部、
メチルエチルケトン・・・・・３０部、
イソプロピルアルコール・・・３０部、
上記１０５部を混合し、撹拌しながら、下記組成のニトロセルロース溶液５部を加えた。
ニトロセルロース（旭化成株式会社製ＨＩＧ１／４）・・・・２５％、
酢酸エチル：イソプロピルアルコール＝６：４混合溶剤・・・７５％、
上記の混合物（全体で１１５部）を、温度を３５℃以下に保ちながら、ターボミキサーを使用して、アルミニウム薄膜細片の大きさが１０〜１５μｍになるまで撹拌し、アルミニウム薄膜細片スラリーを調製した。
(2) Aluminum thin film strip slurry Aluminum thin film strip ... 10 parts,
Ethyl acetate ... 35 parts,
Methyl ethyl ketone 30 parts,
30 parts isopropyl alcohol
105 parts of the above were mixed and 5 parts of a nitrocellulose solution having the following composition was added while stirring.
Nitrocellulose (HIG1 / 4 manufactured by Asahi Kasei Corporation) ... 25%,
Ethyl acetate: isopropyl alcohol = 6: 4 mixed solvent 75%
The above mixture (115 parts in total) was stirred using a turbo mixer while maintaining the temperature at 35 ° C. or lower until the aluminum thin film pieces had a size of 10 to 15 μm. Prepared.
（３）金属薄膜インキ
アルミニウム薄膜細片スラリー・・・・・・・・・・・・・・・・・・・３０部、
ウレタン樹脂（大日本インキ化学工業株式会社製「バーノックＬ７−６１７」）
・・・・・・・・・・・・・・・・・・・・・・・・・・・・・・・・・３０部、
セルロース（イーストマンケミカル「ＣＡＰ−４８２−０．５」）・・・・２部、
下記組成ポリエチレンワックスコンパウンド・・・・・・・・・・・・・・３部、
三井化学株式会社製「ハイワックス２２０ＭＰ」・・・２０％
旭化成株式会社製 「ＨＩＧ７」・・・・・・・・・・１０％
酢酸エチル・・・・・・・・・・・・・・・・・７０％、
酢酸エチル・・・・・・・・・・・・・・・・・・・・・・・・・・・・３０部、
上記９５部を混合し、金属薄膜インキを調製した。
(3) Metal thin film ink Aluminum thin film slurry ... 30 parts,
Urethane resin ("Bernock L7-617" manufactured by Dainippon Ink and Chemicals, Inc.)
... 30 parts,
Cellulose (Eastman Chemical "CAP-482-0.5") ... 2 parts,
Polyethylene wax compound with the following composition: 3 parts,
"High Wax 220MP" made by Mitsui Chemicals, Inc. 20%
"HIG7" made by Asahi Kasei Corporation 10%
Ethyl acetate ... 70%,
Ethyl acetate ... 30 parts,
95 parts of the above were mixed to prepare a metal thin film ink.
［グラビア印刷版］
基材フィルムの片面に、金属薄膜インキを部分的、あるいは全面に塗布又は印刷するためのグラビア版は下記のものを使用した。
グラビア版彫刻機：ヘルグラビアシステムズ社製「HelioKlischograph K500」
スクリーン線数 ：１７５線／インチ
セル深度 ：２５〜３０μｍ
スタイラス角度 ：１２０°
[Gravure printing plate]
The gravure plate for applying or printing the metal thin film ink partially or on the entire surface of one side of the base film was as follows.
Gravure engraving machine: “HelioKlischograph K500” manufactured by Helgravia Systems
Number of screen lines: 175 lines / inch Cell depth: 25-30 μm
Stylus angle: 120 °
［ペーストインキの調整］
アルミペースト（東洋アルミニウム株式会社製 TD-200T）・・・・・・・２０部、
ウレタン樹脂（大日本インキ化学工業株式会社製バーノック L7-617）・・３０部、
セルロース樹脂（イーストマンケミカル社製CAP−482−0.5）・・・・・・・２部、
下記組成のポリエチレンワックスコンパウンド・・・・・・・・・・・・・３部、
三井化学株式会社製「ハイワックス２２０ＭＰ」・・・２０％、
旭化成株式会社製 「ＨＩＧ７」・・・・・・・・・・１０％、
酢酸エチル・・・・・・・・・・・・・・・・・７０％、
酢酸エチル・・・・・・・・・・・・・・・・・・・・・・・・・・・・・３０部、
上記の合計８５部を混合し、ペーストインキを調整した。
[Adjustment of paste ink]
Aluminum paste (TD-200T manufactured by Toyo Aluminum Co., Ltd.) ... 20 parts,
Urethane resin (Bernock L7-617 manufactured by Dainippon Ink and Chemicals, Inc.) 30 parts,
Cellulose resin (CAP-482-0.5, manufactured by Eastman Chemical Co., Ltd.) ... 2 parts,
Polyethylene wax compound with the following composition: 3 parts
“High Wax 220MP” manufactured by Mitsui Chemicals, Inc. 20%
"HIG7" made by Asahi Kasei Corporation 10%,
Ethyl acetate ... 70%,
Ethyl acetate ... 30 parts,
A total of 85 parts of the above was mixed to prepare a paste ink.
［グラビア印刷版］
基材フィルムの片面に、ペーストインキを部分的、あるいは全面に塗布又は印刷するためのグラビア版は下記のものを使用した。
グラビア版彫刻機：ヘルグラビアシステムズ社製「HelioKlischograph K500」
スクリーン線数 ：１７５線／インチ
セル深度 ：２５〜３０μｍ
スタイラス角度 ：１２０°
[Gravure printing plate]
The gravure plate for applying or printing the paste ink partially or entirely on one side of the base film was as follows.
Gravure engraving machine: “HelioKlischograph K500” manufactured by Helgravia Systems
Number of screen lines: 175 lines / inch Cell depth: 25-30 μm
Stylus angle: 120 °
（実施例１：紙容器）
市販のコート紙に、グラビア版を使用して、先ず目止めニス（大日本インキ化学工業株式会社製「ファインラップ ＳＭＳ目止めニス」）をコーティングし、次いで、金属薄膜インキをデザイン全面に印刷し、まず部分金属光沢領域を形成した。次いで、グラビア版にて各種カラーインキ（大日本インキ化学工業株式会社製「ＸＯＳ−１２００型インキ」）を印刷した後、保護層並びに成型時の接着層としてポリエチレンを押し出しラミネートした。この印刷物を裁断し、成形して金属探知器非感応型包装材を得た。
(Example 1: paper container)
First, coat commercially available coated paper with gravure varnish (Dainippon Ink Chemical Co., Ltd. “Fine Wrap SMS Sealing Varnish”), then print metal thin film ink on the entire design surface. First, a partial metallic gloss region was formed. Next, after printing various color inks (“XOS-1200 ink” manufactured by Dainippon Ink & Chemicals, Inc.) with a gravure plate, polyethylene was extruded and laminated as a protective layer and an adhesive layer at the time of molding. This printed material was cut and molded to obtain a metal detector non-sensitive packaging material.
（実施例２：表刷り包装材）
市販のポリプロピレンフィルムに、グラビア版を使用して、各種カラーインキ（大日本インキ化学工業株式会社製「アルティマＮＴ型インキ」）を印刷した。次いで、グラビア版にて金属薄膜インキを部分印刷し、部分金属光沢領域を形成した後、保護層としてオーバーコートニス（大日本インキ化学工業株式会社製「アルティマＮＴ メジューム」）を印刷し、製袋して金属探知器非感応型包装材を得た。
(Example 2: Surface-printing packaging material)
Various color inks ("Ultima NT ink" manufactured by Dainippon Ink & Chemicals, Inc.) were printed on a commercially available polypropylene film using a gravure plate. Next, the metal thin film ink is partially printed with a gravure plate to form a partially metallic glossy region, and then overcoat varnish ("Ultima NT Medium" manufactured by Dainippon Ink & Chemicals, Inc.) is printed as a protective layer. As a result, a metal detector insensitive packaging material was obtained.
（実施例３：透明フィルム使用の裏刷り包装材）
市販のポリプロピレンに、グラビア版を使用して、各種カラーインキ（大日本インキ化学工業株式会社製「ユニバーサル２１型インキ」）でデザイン印刷を行う。次いで、金属薄膜インキを印刷した。通常グラビアインキと金属薄膜インキを印刷した側の面に、ラミネート用接着剤（大日本インキ化学工業株式会社製「ディックドライＬＸ−４０１Ａ／ＳＰ−６０」）を塗布量２．５ｇ／ｍ２となるように塗布した後、ポリプロピレンフィルムを貼り合わせ、製袋し金属探知器非感応型包装材を得た。
(Example 3: Back-printing packaging material using a transparent film)
Design printing is performed on commercially available polypropylene using gravure plates with various color inks ("Universal 21 ink" manufactured by Dainippon Ink & Chemicals, Inc.). Then, metal thin film ink was printed. Usually, a laminating adhesive (“Dick Dry LX-401A / SP-60” manufactured by Dainippon Ink & Chemicals, Inc.) is applied to the surface on which the gravure ink and the metal thin film ink are printed, and the coating amount is 2.5 g / m 2 . After coating, the polypropylene film was bonded together to form a bag to obtain a metal detector non-sensitive packaging material.
（比較例１：紙容器）
市販のコート紙に、グラビア版を使用して、ペーストインキをデザイン全面に印刷し、まず部分金属光沢領域を形成した。次いで、グラビア版にて各種カラーインキ（大日本インキ化学工業株式会社製「ＸＯＳ−１２００型インキ」）を印刷した後、保護層並びに成型時の接着層としてポリエチレンを押し出しラミネートした。この印刷物を裁断し、成形して包装材を得た。
(Comparative example 1: paper container)
Using a gravure plate on a commercially available coated paper, a paste ink was printed on the entire design surface, and first a partially metallic gloss region was formed. Next, after printing various color inks (“XOS-1200 ink” manufactured by Dainippon Ink & Chemicals, Inc.) with a gravure plate, polyethylene was extruded and laminated as a protective layer and an adhesive layer at the time of molding. The printed material was cut and molded to obtain a packaging material.
（比較例２：表刷り包装材）
市販のポリプロピレンフィルムに、グラビア版を使用して、各種カラーインキ（大日本インキ化学工業株式会社製「アルティマＮＴ型インキ」）を印刷した。次いで、グラビア版にてペーストインキを部分印刷し、部分金属光沢領域を形成し、製袋して包装材を得た。
(Comparative Example 2: Surface-printing packaging material)
Various color inks ("Ultima NT ink" manufactured by Dainippon Ink & Chemicals, Inc.) were printed on a commercially available polypropylene film using a gravure plate. Subsequently, the paste ink was partially printed with a gravure plate to form a partial metallic gloss region, and a bag was produced to obtain a packaging material.
（比較例３：透明フィルム使用の裏刷り包装材）
市販のポリプロピレンに、グラビア版を使用して、各種カラーインキ（大日本インキ化学工業株式会社製「ユニバーサル２１型インキ」）でデザイン印刷を行う。次いで、ペーストインキを印刷した。通常印刷した側の面に、ラミネート用接着剤（大日本インキ化学工業株式会社製「ディックドライＬＸ−４０１Ａ／ＳＰ−６０」）を塗布量２．５ｇ／ｍ２となるように塗布した後、ポリプロピレンフィルムを貼り合わせ、製袋し包装材を得た。
(Comparative Example 3: Backprint packaging material using transparent film)
Design printing is performed on commercially available polypropylene using gravure plates with various color inks ("Universal 21 ink" manufactured by Dainippon Ink & Chemicals, Inc.). The paste ink was then printed. After applying a laminating adhesive ("Dick Dry LX-401A / SP-60" manufactured by Dainippon Ink & Chemicals, Inc.) on the normally printed side so that the application amount is 2.5 g / m 2 , A polypropylene film was pasted and a bag was made to obtain a packaging material.
（比較結果）
前記の実施例１〜３並びに比較例１〜３に記載の包装材を金属探知器（日新電子工業株式会社製金属検出機ＮＤ−８１０）にて金属検出の有無を評価した。
試料は実施例と比較例に使用したインキ単体（１００ｃｃポリ容器に５０ｇのインキを詰めたもの）と、それぞれの容器または包装材（０．２５ｍ２）とする。
検出感度はインキ単体の場合２５．４（自動設定、製品影響減少はオフ）、容器または包装材の場合は６５．４（デジタル設定、製品影響減少はオフ）とする。検出信号電圧は３．０Ｖ以上。製品に水分や塩分を含む場合は金属が無くても本検出器が反応しやすいので、製品影響減少スイッチをオンにする。
表における金属探知器の検出の評価結果は、◎は金属探知器ではまったく検知されないことを表し、×はほぼ確実に検知されることを表す。
金属光沢はマイクロ−トリ−グロス光沢計（ＢＹＫ製）にて２０゜／６０゜の光沢を測定した。光沢値は数値がより大きい方が光沢が高く、測定不能とは非常に光沢が高く、機器の測定範囲を超えた場合を指す。
(Comparison result)
The packaging materials described in Examples 1 to 3 and Comparative Examples 1 to 3 were evaluated for the presence or absence of metal detection using a metal detector (metal detector ND-810 manufactured by Nissin Electronics Industry Co., Ltd.).
The sample is the ink used in Examples and Comparative Examples (100 cc poly container filled with 50 g of ink) and each container or packaging material (0.25 m 2 ).
The detection sensitivity is 25.4 (automatic setting, product effect reduction is OFF) for ink alone, and 65.4 (digital setting, product effect reduction is OFF) for containers or packaging materials. The detection signal voltage is 3.0V or higher. If the product contains moisture or salt, the detector will react easily even if there is no metal, so turn on the product effect reduction switch.
The evaluation results of detection of the metal detector in the table indicate that ◎ is not detected at all by the metal detector, and × is detected almost certainly.
The metallic luster was measured at 20 ° / 60 ° with a micro-tri-gloss gloss meter (manufactured by BYK). The gloss value is higher when the numerical value is higher, and the measurement is impossible when the measurement value is too high.
表１、表２及び表３より、比較例１〜３に比べて、実施例１〜３は非常に高い金属光沢を示すにも拘わらず、金属探知器には安定して検出されないように該探知機を設定できることがわかる。
From Table 1, Table 2, and Table 3, although Examples 1-3 show very high metallic luster compared with Comparative Examples 1-3, it is not detected stably by a metal detector. It can be seen that the detector can be set.
Claims (3)
The packaging material insensitive to the metal detector according to claim 2, wherein the metal thin film strip is surface-treated with at least one selected from the group consisting of organic fatty acids, methylsilyl isocyanate and cellulose derivatives.