CN204123487U - Bamboo China fir cross laminate composite construction material - Google Patents
Bamboo China fir cross laminate composite construction material Download PDFInfo
- Publication number
- CN204123487U CN204123487U CN201420358655.1U CN201420358655U CN204123487U CN 204123487 U CN204123487 U CN 204123487U CN 201420358655 U CN201420358655 U CN 201420358655U CN 204123487 U CN204123487 U CN 204123487U
- Authority
- CN
- China
- Prior art keywords
- bamboo
- china fir
- carry out
- composite construction
- laminate composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses a kind of bamboo China fir cross laminate composite construction material, comprise at least one piece of bamboo blank plate and at least one block of wooden blanket, described bamboo blank plate and wooden blanket carry out assembly by 90 degree of direction orthogonal superposition modes, by side direction hot press pressurization sizing, obtain bamboo China fir cross laminate composite construction material.This products material wide material sources, the bamboo China fir cross laminate composite construction material made has that intensity is high, breadth is wide, thickness range is wide, the feature of environmental protection, the efficiency of construction of architectural engineering can be drastically increased, have that cost is low, the advantage of short construction period.
Description
Technical field
The utility model relates to bamboo wood technical field of comprehensive utilization, particularly a kind of bamboo China fir cross laminate composite construction material.
Background technology
The research of bamboo China fir cross laminate composite construction material has no report at home.At present, external like product crosswise lamination CLT (note: CLT full name is cross-laminatedtimber, crosswise lamination timber) be made up of pine square bar, owing to all using pine square bar, its raw material sources is deficient, therefore, CLT have that cost is high, resource scarcity, shortcoming that consumption forest tree resource is large.
Utility model content
In view of this, the purpose of this utility model is to provide a kind of bamboo China fir cross laminate composite construction material, and employing bamboo and wood materials is raw material, has the advantages that intensity is high, breadth is wide, thickness range is wide, has wide range of applications.
The purpose of this utility model is achieved through the following technical solutions:
Bamboo China fir cross laminate composite construction material of the present utility model, comprise at least one piece of bamboo blank plate and at least one block of wooden blanket, described bamboo blank plate and wooden blanket carry out assembly by 90 degree of direction orthogonal superposition modes, by side direction hot press pressurization sizing, obtain bamboo China fir cross laminate composite construction material.
Further, described bamboo blank plate is by the well-thought-out plan section of saw, remove ring, subdivision is processed into bamboo cane, then by rough milling removal surf green, send to after natural drying in carbide furnace and carry out carbonization treatment, remove the sugar of bamboo cane and moisture, and then send in drying oven and carry out drying process, the bamboo cane after drying has processed is to its two-sided dip-coating bonded adhesives, plate blank between one-tenth thickness 8-15 millimeter bonded to each other, then approaching side is made to hot press pressurization sizing;
Further, described wooden blanket is by the China fir section of saw, subdivision is processed into batten, send to after natural drying in carbide furnace and carry out carbonization treatment, remove the sugar of batten and moisture, and then send in drying oven and carry out drying process, the batten after drying has processed is to its two-sided dip-coating bonded adhesives, plate blank between one-tenth thickness 8-15 millimeter bonded to each other, then approaching side is made to hot press pressurization sizing.
Further, described bonded adhesives adopts phenolic resin glue.
The beneficial effects of the utility model are:
This products material wide material sources, the bamboo China fir cross laminate composite construction material made has that intensity is high, breadth is wide, thickness range is wide, the feature of environmental protection, the efficiency of construction of architectural engineering can be drastically increased, have that cost is low, the advantage of short construction period.
Other advantages of the present utility model, target and feature will be set forth to a certain extent in the following description, and to a certain extent, based on will be apparent to those skilled in the art to investigating hereafter, or can be instructed from practice of the present utility model.Target of the present utility model and other advantages can be realized by description below and claims and be obtained.
Accompanying drawing explanation
In order to make the purpose of this utility model, technical scheme and advantage clearly, below in conjunction with accompanying drawing, the utility model is described in further detail, wherein:
Fig. 1 is that bamboo blank plate and wooden blanket stack mode schematic diagram;
Fig. 2 is the structure side view that have employed three-decker.
Detailed description of the invention
Hereinafter with reference to accompanying drawing, preferred embodiment of the present utility model is described in detail.Should be appreciated that preferred embodiment only in order to the utility model is described, instead of in order to limit protection domain of the present utility model.
As shown in Figure 1, bamboo China fir cross laminate composite construction material of the present utility model, comprises one piece of bamboo blank plate 1 and one block of wooden blanket 2, and bamboo blank plate and wooden blanket carry out assembly by 90 degree of direction orthogonal superposition modes, by side direction hot press pressurization sizing, obtain bamboo China fir cross laminate composite construction material.
Wherein, bamboo blank plate is by the well-thought-out plan section of saw, remove ring, subdivision is processed into bamboo cane, then by rough milling removal surf green, send to after natural drying in carbide furnace and carry out carbonization treatment, remove the sugar of bamboo cane and moisture, and then send in drying oven and carry out drying process, the bamboo cane after drying has processed is to its two-sided dip-coating phenolic resin glue, plate blank between one-tenth thickness 8-15 millimeter bonded to each other, then approaching side is made to hot press pressurization sizing.
Wood blanket is by the China fir section of saw, subdivision is processed into batten, send to after natural drying in carbide furnace and carry out carbonization treatment, remove sugar and the moisture of batten, and then send in drying oven carry out drying process, dry process after batten to its two-sided dip-coating phenolic resin glue, the plate blank between one-tenth thickness 8-15 millimeter bonded to each other, then approaching side is made to hot press sizing of pressurizeing.
Certainly, it should be pointed out that the phenolic resin glue of above-mentioned employing also can adopt other to replace at the bonded adhesives that the industry is conventional, adopt the bonded adhesives of other type also should belong to protection domain of the present utility model.
In above-described embodiment, the breadth of composite construction material and thickness combine as requested, namely bamboo blank plate and the quantity of wooden blanket on longitudinal Direction of superposition are not restricted, and as required, the breadth of composite construction material also can carry out polylith arrangement as required and extend simultaneously.Generally, wooden blanket and bamboo blank plate adopt the mode of interval superposition, namely one piece of bamboo blank plate are placed by one block of wooden blanket, then are again up one block of wooden blankets ... superpose successively.
The utility model utilizes local abundant mao bamboon and China fir to be raw material, is a kind of Novel bamboo China fir composite wood building structural materials.Product can be widely used in the fields such as building, interior decoration, sports buildings.
What finally illustrate is, above embodiment is only in order to illustrate the technical solution of the utility model and unrestricted, although be described in detail the utility model with reference to preferred embodiment, those of ordinary skill in the art is to be understood that, can modify to the technical solution of the utility model or equivalent replacement, and not departing from aim and the scope of the technical program, it all should be encompassed in the middle of right of the present utility model.
Claims (1)
1. bamboo China fir cross laminate composite construction material, it is characterized in that: comprise at least one piece of bamboo blank plate and at least one block of wooden blanket, described bamboo blank plate and wooden blanket carry out assembly by 90 degree of direction orthogonal superposition modes, by side direction hot press pressurization sizing, obtain bamboo China fir cross laminate composite construction material, described bamboo blank plate is by the well-thought-out plan section of saw, remove ring, subdivision is processed into bamboo cane, then by rough milling removal surf green, send to after natural drying in carbide furnace and carry out carbonization treatment, remove sugar and the moisture of bamboo cane, and then send in drying oven carry out drying process, bamboo cane after drying has processed is to its two-sided dip-coating bonded adhesives, plate blank between one-tenth thickness 8-15 millimeter bonded to each other, approaching side is made to hot press pressurization sizing again, described wooden blanket is by the China fir section of saw, remove knaur, subdivision is processed into batten, send to after natural drying in carbide furnace and carry out carbonization treatment, remove sugar and the moisture of batten, and then send in drying oven carry out drying process, batten after drying has processed is to its two-sided dip-coating bonded adhesives, plate blank between one-tenth thickness 8-15 millimeter bonded to each other, approaching side is made to hot press pressurization sizing again, described bonded adhesives adopts phenolic resin glue.