CN1247712C - Visible light cured metal paint - Google Patents
Visible light cured metal paint Download PDFInfo
- Publication number
- CN1247712C CN1247712C CN 03105044 CN03105044A CN1247712C CN 1247712 C CN1247712 C CN 1247712C CN 03105044 CN03105044 CN 03105044 CN 03105044 A CN03105044 A CN 03105044A CN 1247712 C CN1247712 C CN 1247712C
- Authority
- CN
- China
- Prior art keywords
- methyl
- acrylate
- acid
- monomer
- phenyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a visible light cured metal paint and particularly relates to a visible light cured metal paint which is used for protecting and decorating various metal surfaces. The visible light cured metal paint is composed of components according to the proportion by weight: 0 to 20 wt% of prepolymer containing vinyl unsaturated groups, 20 to 80 wt% of monomer containing vinyl unsaturated groups, 1 to 10 wt% of photoinitiator, 0.5 to 30 wt% of aid initiator, 0 to 10 wt% of auxiliary agent, 0 to 40 wt% of filler or pigment and 0 to 30 wt% of solvent. The visible light cured metal paint can be widely used for painting and decorating various surfaces of metal or alloy, such as steel, aluminum, copper, etc.
Description
Technical field
The invention belongs to the metal paint field, particularly be used for the visible-light curing metallic paint of various metal surface protections and decoration.
Background technology
At present, the coating of metal finishing employing mainly contains alkyd paint, vinylformic acid baking vanish, electrocoating paint and powder coating.Alkyd paint VOC content height, the paint film physical and chemical performance is relatively poor; All there are shortcomings such as equipment investment cost height, time of drying length, energy consumption height in vinylformic acid baking vanish, electrocoating paint and powder coating.
Ultraviolet-curing paint is a kind of low smell, hypotoxicity, low VOC and quick-setting coating, has been successfully applied to the application of substrate surfaces such as woodenware, paper, plastics and metal.But UV-curing technology still has its disadvantage: the one, and ultraviolet light polymerization needs special equipment, can't solidify some shape irregularities and the big object of area (or volume); The 2nd, the short-wave ray that ultraviolet lamp produces has injury to human body, contact meeting skin ambustion and eyes accidentally, simultaneously, ultraviolet ray makes the ozone that oxygen produces in the air can cause that the people has a headache, fatigue, eyes and lung to the people have pungency, and long-term operator this environmental work is had certain harm.These problems have limited UV-curing technology to a certain extent in the more application and the development greatly of wide spectrum.
Do not contain short wave ultraviolet in the visible light source, do not produce ozone, skin is not had the effect of burning, need not fixture, safe and convenient to use; Simultaneously, visible wavelength is long, and penetration power is strong, compares with UV-light more to help deep layer curing.Therefore, exploitation visible-light curing coating can solve traditional metallic paint high toxicity, high energy consumption, with high investment, problem that curing speed is slow and the problem of ultraviolet-curing paint construction application inconvenience simultaneously.
Since nineteen sixty-eight, Germany Bayer company developed first-generation ultraviolet cured woodware coating, people were attempting the photo-cured coating of research and development by the visible light initiated polymerization always.For example, US6106999 discloses a kind of visible-light curing resin combination, wherein adopts organoboron compound as light trigger, adopts Ar or YAG laser vibration light as light source; JP10-17604A discloses a kind of visible light photosensitive resin composition, wherein adopts titanium compound and coumarin compound as light trigger; US6110987 discloses visible light solidified composition, has wherein adopted season boron salt and free radical uv photopolymerization initiator; US5368990A discloses visible light solidified composition, wherein with containing the compound of diaryl iodine as polymerization starter.These visible light initiator are very expensive, are difficult to promote the use of; In addition, CN1215421A discloses a kind of visible light polymerizable composition, and it contains the combination of polythiol and acylphosphine oxide class initiator, but the said composition shelf lives have only about a week, use very inconvenient.
Summary of the invention
The objective of the invention is advantages such as, good stability low, quick solidifying in conjunction with ultraviolet light polymerization initiator price, with advantage such as security, the penetrance of visible light be good, easy to use, provide a kind of using visible light light source irradiation to cause that solidified contains the visible-light curing metallic paint of radical photoinitiator, to substitute existing traditional metallic paint and ultraviolet light polymerization metallic paint.
Visible-light curing metallic paint of the present invention is formed and content (by weight percentage) is:
The prepolymer 0-20% that contains alkene class unsaturated group
The monomer 20-80% that contains alkene class unsaturated group
Light trigger 1-10%
Aided initiating 0.5-30%
Auxiliary agent 0-10%
Filler and/or pigment 0-40%
Solvent 0-30%
Above-mentioned component according to described mixed, is stirred, promptly prepare visible-light curing metallic paint of the present invention.
The described prepolymer that contains alkene class unsaturated group comprises epoxy (methyl) acrylate, urethane (methyl) acrylate, polyester (methyl) acrylate, polyethers (methyl) acrylate, acrylic copolymer or their any mixture.
Described epoxy (methyl) acrylate be Resins, epoxy and unsaturated carboxylic acid (for example, vinylformic acid, methacrylic acid) adduct of reaction, comprise epoxy (methyl) acrylate of epoxy (methyl) acrylate, phenol or cresol-novolac epoxy resin of bisphenol A type epoxy resin or (methyl) acrylate of diglycidyl ether.
The reaction product that the reaction of described urethane (methyl) acrylate by hydroxyl (methyl) acrylate and polyvalent alcohol and organic multiple isocyanate makes.(methyl) acrylate of described hydroxyl is (methyl) acrylic acid hydroxy alkyl ester, for example (methyl) 2-hydroxyethyl acrylate or (methyl) vinylformic acid-2-hydroxypropyl ester.Described polyvalent alcohol comprises ethylene glycol, propylene glycol or butyleneglycol etc.Described organic multiple isocyanate comprises tolylene diisocyanate, 4,4 '-diphenylmethanediisocyanate, 4,4 '-dicyclohexyl methane diisocyanate, hexamethylene diisocyanate or isophorone diisocyanate.
Described polyester (methyl) acrylate is polyester polyol and (methyl) acrylic acid dehydrating condensation product.Described polyester polyol is the reaction product of polyvalent alcohol and diprotic acid, wherein polyvalent alcohol comprises ethylene glycol, polypropylene glycol, 1,6-hexylene glycol or TriMethylolPropane(TMP) etc., diprotic acid comprise hexanodioic acid, succsinic acid, phthalic acid, adjacent benzene two dioctyl phthalate of hexahydro-or terephthalic acid etc.
Described polyethers (methyl) acrylate is poly-alkyl diol two (methyl) acrylate, for example polyoxyethylene glycol two (methyl) acrylate or polypropylene glycol two (methyl) acrylate.
Described acrylic copolymer is monomers such as vinylformic acid, acrylate or vinylbenzene, in peroxide initiator (for example, Benzoyl Peroxide) effect down, and by the compounds that Raolical polymerizable obtained.
The described monomer that contains alkene class unsaturated group comprises styrenic, (methyl) esters of acrylic acid, vinyl ethers or their any mixture etc.
Described styrene monomer comprises vinylbenzene or alpha-methyl styrene etc.
Described (methyl) acrylic ester monomer comprises the simple function group monomer, for example butyl acrylate, cyclohexyl acrylate, Isooctyl acrylate monomer, (methyl) vinylformic acid-2-hydroxyl ethyl ester or (methyl) vinylformic acid-2-hydroxypropyl acrylate etc.; The bifunctional monomer, for example 1, oneself two omega-diol diacrylates (HDDA) of 6-, tri (propylene glycol) diacrylate (TPGDA), propylene glycol diacrylate (DPGDA), neopentylglycol diacrylate (NPGDA), ethoxylated neopentylglycol diacrylate (PO-NPGDA), bisphenol a diacrylate (DDA), tetraethylene-glycol diacrylate (TEGDA) or PDDA (PDDA) etc.; Trifunctional monomer, for example Viscoat 295 (TMPTA), ethoxylated trimethylolpropane triacrylate (EO-TMPTA), propoxylation Viscoat 295 (PO-TMPTA), pentaerythritol triacrylate (PETA) or three (2-hydroxyethyl) isocyanuric acid triacrylate etc.; Polyfunctional monomer, for example tetramethylol methane tetraacrylate, Dipentaerythritol five acrylate or dipentaerythritol acrylate etc.Usually with one or more the mixture in above-mentioned (methyl) acrylic ester monomer as application.
Described vinyl ethers monomer comprises hexanaphthene dimethyl alcohol divinyl ether, hydroxyethyl vinyl ether or triethylene glycol divinyl ether etc.
The described monomer that contains alkene class unsaturated group further comprises N-vinyl pyrrolidone, N-caprolactam, acryloyl morpholine, N-vinyl formamide or N-vinyl acetamide.
The described monomer that contains alkene class unsaturated group preferably uses polyvalent alcohol many (methyl) acrylate, as two functionality 1,6 hexanediol diacrylates or three-functionality-degree Viscoat 295.1,6 hexanediol diacrylate is a kind of linear chain structure, gives the good snappiness of filming, and contains 3 two keys in the Viscoat 295, can improve curing speed, hardness and the electrical property of filming.
Described light trigger is meant that photochemical reaction can take place produces a free radical or a hydrionic compounds when accepting the special wavelength rayed.Thereby can causing the Raolical polymerizable of system, the free radical that radical photoinitiator produced makes paint solidification.The light trigger of different structure has different absorption spectrums and free radical activity, and the light trigger of selecting comparatively to mate with the light source light spectrum energy distribution will improve curing speed greatly.When the formula for a product of definite purposes of design and using method, may produce synergism from many-sides such as used light source, set time, paint film property and economy screening light trigger and the combination of different light trigger.
Described light trigger comprises benzoin ethers, benzil ketals class, acetophenones, anthraquinone class, thioxanthones, Benzophenones, acyl group see oxygen compound class, benzoates or dicyclo cyclohexadione compounds.
Described benzoin ether photoinitiator is benzoin methyl ether, bitter almond oil camphor ethyl ether or bitter almond oil camphor isopropyl ether etc.
Described benzil ketals photoinitiator is a benzil dimethyl ketal etc.
Described acetophenones light trigger is a methyl phenyl ketone, 2,2-dimethoxy-2-phenyl methyl phenyl ketone, 2,2-diethoxy-2-phenyl methyl phenyl ketone, 1, the 1-dichloroacetophenone, the 1-hydroxy acetophenone, 1-hydroxy-cyclohexyl phenyl ketone, 2-hydroxy-2-methyl-1-phenyl-1-acetone, 1-(4-isopropyl phenyl)-2-hydroxy-2-methyl-1-acetone, 1-[4-(2-hydroxyl-oxethyl) phenyl]-2-hydroxy-2-methyl-1-acetone, 2-methyl isophthalic acid-[4-(methyl mercapto) phenyl]-2-morpholinyl-1-acetone or 2-benzyl-2-dimethylamino-1-(4-morpholinyl phenyl)-1-butanone etc.
Described anthraquinone photoinitiator is 2-tertiary butyl anthraquinone, 1-chloroanthraquinone or 2-amyl anthraquinone etc.
Described thioxanthone photoinitiator is 2,4-dimethyl thia anthrone, 2,4-diethyl thioxanthone, 2 (or 4)-isopropyl thioxanthone, 2-chloro thioxanthone or 2,4-di-isopropyl thioxanthone etc.
Described Benzophenones light trigger is benzophenone, 4-chlorobenzophenone, to methyldiphenyl ketone or 4-benzoyl-4 '-dimethyl diphenyl sulfide etc.
The described acyl group oxygen compound photoinitiator of seeing is 2; 4; 6～trimethylbenzoyl diphenyl phosphine oxide, two (2; 4, the 6-trimethylbenzoyl)-the phenyl oxidation is seen, two (2, the 6-dimethylbenzoyl)-2; 4; 4-tri-methyl-amyl phosphine oxide or 2,4,6-trimethylbenzoyl phenyl ethoxy phosphine oxide etc.
Described benzoic ether photoinitiator is benzoylbenzoic acid methyl esters or methyl o-benzoylbenzoate etc.
Described dicyclo cyclohexadione compounds is camphorquinone or two imidazoles etc., and wherein camphorquinone has been successfully applied to the visible-light curing dental material.
When metallic paint of the present invention was varnish system, described light trigger accounted for the 1-5wt% of metallic paint gross weight, preferred 2-3wt%.
When metallic paint of the present invention was coloured system, described light trigger accounted for the 1-10wt% of metallic paint gross weight, preferred 2-5wt%.
Described aided initiating comprises the acrylic ester monomer or the prepolymer of alkyl hydroxy aminated compounds, dimethylaminobenzoic acid ester compound or amine modification.
Described alkyl hydroxy amine aided initiating is trolamine, tri-isopropanolamine or methyldiethanolamine.
Described dimethylaminobenzoic acid ester class aided initiating is 4-dimethylamino-ethyl benzoate or the different monooctyl ester of 4-dimethylaminobenzoic acid.
The acrylic ester monomer of described amine modification or prepolymer be aminated compounds (for example, diethylamine) with acrylic ester monomer or prepolymer (for example, Viscoat 295) reaction product that affine substitution reaction obtained taking place, comprises diethylamine modification Viscoat 295 or diethylamine modification ethoxylated trimethylolpropane triacrylate etc.
Described aided initiating has good promoter action to light trigger, and it has the effect that overcomes oxygen inhibition to radical polymerization simultaneously.Because low-molecular-weight aided initiating alkyl hydroxy aminated compounds is easy to from its internal migration to the surface after photo-curing material solidifies, thereby cause " perspiration " or " sending out frost " phenomenon, therefore, the acrylic ester monomer or the prepolymer of preferred dimethylaminobenzoic acid ester class or amine modification among the present invention.The addition of dimethylaminobenzoic acid ester class aided initiating is preferably 0.5-10wt%, more preferably 1-5wt% (accounting for the metallic paint gross weight); The acrylic ester monomer of amine modification or the addition of prepolymer are preferably 5-30wt% (accounting for the metallic paint gross weight), more preferably 10-20wt%.
Described auxiliary agent comprises flow agent, defoamer, wetting dispersing agent and stopper.Wherein the flow agent add-on is the 0-5wt% of prescription gross weight, and defoamer is the 0-2wt% of prescription gross weight, and wetting dispersing agent is the 0-2wt% of prescription gross weight, and stopper is the 0-1wt% of prescription gross weight.
Described flow agent includes organic siloxane type flow agent, for example BYK-306, EFKA-3031, DEUCHEM-432 or HX-3010 etc.; Active organosilicon oxygen alkane type flow agent, for example BYK-373 or EFKA-3883 etc.; Polymer flow agent, for example BYK-358 or EFKA-3277 etc.; Solvent-borne type flow agent, for example HX-3060 etc.Can select wherein one or more mixture.
Described defoamer comprises and does not contain organo-siloxane type defoamer, for example BYK-055, EFKA-2721, DEUCHEM-2700 or HX-2100 etc.; Contain organo-siloxane type defoamer, for example EFKA-2022, DEUCHEM-5600 or HX-2000 etc.Can select wherein one or more mixture.
Described wetting dispersing agent comprises high molecular weight polypropylene acid esters, for example Disperbyk-161 or EFKA-4800 etc.; Macromolecule polyurethane, for example EFKA-4010 etc.; Polymeric carboxylic, for example DEUCHEM-904 etc.; Lower molecular weight is unsaturated, the saturated carboxylic acid amine salt, for example HX-4010 etc.Can select wherein one or more mixture.
Described stopper comprises quinhydrones, Hydroquinone monomethylether, thiodiphenylamine, N-nitrophenyl oxyamine aluminium salt, Resorcinol or MEHQ etc.Can select wherein one or more mixture.
Described filler mainly comprises silicon-dioxide, talcum powder, barium sulfate, Zinic stearas, clay or lime carbonate, and nano materials such as nano silicon or nano titanium oxide, the physical and chemical performance that they can improve paint film to a great extent for example improves hardness of paint film, toughness, wear resistance and weathering resistance etc.; Described pigment comprises mineral dye (for example titanium dioxide, carbon black, copper powder, aluminium powder or pearlescence etc.) or pigment dyestuff (for example phthalocyanine blue, green, the brown chrome yellow of the phthalein mountain valley with clumps of trees and bamboo or bright red etc.).
Described solvent comprises N-BUTYL ACETATE, vinyl acetic monomer, toluene, dimethylbenzene, butanone, pimelinketone or their any mixture.
Coating composition of the present invention is cured with visible light source, if coating composition of the present invention is used for outdoor use, then can utilize sunlight to solidify.Coating of the present invention is pressed the difference of filler in the composition or pigment, is divided into high light varnish, matte varnish, colored paint, pearlescent lacquer and metal flash paint etc.Can be used for the application of various metallic surfaces, mainly comprise metal and alloy materials thereof such as iron and steel, aluminium, aluminium alloy, copper.
The present invention preferably uses the visible light source of spectral range at 360-780nm, comprises sunlight, luminescent lamp, metal halide lamp and xenon lamp etc.More preferably use metal halide lamp, indium lamp especially, its spectral range is at 360-750nm, and its main peak is at 410nm and 450nm, and the most effective spectral range is 400-460nm.
Coating composition of the present invention can be in packaging vessel stably stored more than six months.
Coating composition of the present invention can or be printed on the base material with the method coating known to usually.
Embodiment
Following embodiment and reference examples can illustrate further characteristics of the present invention, but are not subjected to the restriction of these examples.
Embodiment uses 400W indium lamp as visible light source, and test piece and fluorescent tube distance are 10cm, and coating thickness is 40um, but the present invention is not limited thereto.Reference examples uses the 400W high voltage mercury lamp as UV-light (UV) light source, and test piece and fluorescent tube distance are 10cm, and coating thickness is 40um.
Abbreviation among the embodiment has following connotation:
HEA: Hydroxyethyl acrylate
MHEA: hydroxyethyl methylacrylate
EHA: Isooctyl acrylate monomer
HDDA:1,6 hexanediyl esters
PDDA: PDDA
TPGDA: tri (propylene glycol) diacrylate
PO-NPGDA: ethoxylated neopentylglycol diacrylate
TMPTA: Viscoat 295
EO-TMPTA: ethoxylated trimethylolpropane triacrylate
PO-TMPTA: propoxylation Viscoat 295
DEA-TMPTA: diethylamine modification Viscoat 295
184:1-hydroxy-cyclohexyl phenyl ketone
1173:2-hydroxy-2-methyl-1-phenyl-1-acetone
BP: benzophenone
ITX: isopropyl thioxanthone
CTX:2-chloro thioxanthone
TPO:2,4,6-trimethylbenzoyl diphenyl phosphine oxide
819: two (2,4, the 6-trimethylbenzoyl)-phenyl phosphine oxides
BMS:4-benzoyl-4 '-dimethyl diphenyl sulfide
EDAB:4-dimethylamino-ethyl benzoate
OK-500: silicon-dioxide, as cutting photo etching, German Degussa company product
Embodiment 1
Bisphenol A epoxy acrylate 20wt%
TPGDA 25wt％
TMPTA 37wt％
DEA-TMPTA 15wt％
ITX 3wt％
Above-mentioned component according to described mixed, is stirred, promptly prepare visible-light curing metallic paint.
Purposes: high light varnish
Be 5 seconds the set time of prescription sample under the indium lamp of embodiment 1.
Reference examples 1
Be 6 seconds the set time of prescription sample under the UV lamp of embodiment 1.
Embodiment 2
Bisphenol A epoxy acrylate 15wt%
Urethane acrylate 5wt%
HDDA 37wt％
TMPTA 25wt％
DEA-TMPTA 16wt％
819 2wt％
Above-mentioned component according to described mixed, is stirred, promptly prepare visible-light curing metallic paint.
Purposes: high light varnish
Be 5 seconds the set time of prescription sample under the indium lamp of embodiment 2.
Reference examples 2
Be 6 seconds the set time of prescription sample under the UV lamp of embodiment 2.
Embodiment 3
Bisphenol A epoxy acrylate 5wt%
Acrylic copolymer 10wt%
PO-NPGDA 20wt％
EO-TMPTA 25wt％
EHA 15wt％
DEA-TMPTA 18wt％
TPO 2wt％
OK-500 5wt％
Above-mentioned component according to described mixed, is stirred, promptly prepare visible-light curing metallic paint.
Purposes: half matte varnish
Be 6 seconds the set time of prescription sample under the indium lamp of embodiment 3.
Reference examples 3
Be 8 seconds the set time of prescription sample under the UV lamp of embodiment 3.
Embodiment 4
Bisphenol A epoxy acrylate 10wt%
TPGDA 22wt％
TMPTA 40wt％
DEA-TMPTA 20wt％
ITX 2wt％
184 2wt％
OK-500 4wt％
Above-mentioned component according to described mixed, is stirred, promptly prepare visible-light curing metallic paint.
Purposes: half matte varnish
Be 6 seconds the set time of prescription sample under the indium lamp of embodiment 4.
Reference examples 4
Be 7 seconds the set time of prescription sample under the UV lamp of embodiment 4.
Embodiment 5
Bisphenol A epoxy acrylate 15wt%
Polyester acrylate 5wt%
EO-TMPTA 30wt％
DEA-TMPTA 36wt％
819 2wt％
1173 2wt％
OK-500 10wt％
Above-mentioned component according to described mixed, is stirred, promptly prepare visible-light curing metallic paint.
Purposes: full matte varnish
Be 3 seconds the set time of prescription sample under the indium lamp of embodiment 5.
Reference examples 5
Be 4 seconds the set time of prescription sample under the UV lamp of embodiment 5.
Embodiment 6
Acrylic copolymer 15wt%
HDDA 25wt％
EO-TMPTA 15wt％
DEA-TMPTA 25wt％
TPO 7wt％
184 3wt％
Titanium dioxide 10wt%
Above-mentioned component according to described mixed, is stirred, promptly prepare visible-light curing metallic paint.
Purposes: white paint
Be 10 seconds the set time of prescription sample under the indium lamp of embodiment 6.
Reference examples 6
Be 12 seconds the set time of prescription sample under the UV lamp of embodiment 6.
Embodiment 7
PDDA 40wt％
HDDA 10wt％
TMPTA 20wt％
DEA-TMPTA 18wt％
CTX 3wt％
Titanium dioxide 7wt%
Phthalocyanine blue 2wt%
Above-mentioned component according to described mixed, is stirred, promptly prepare visible-light curing metallic paint.
Purposes: blue lacquer
Be 8 seconds the set time of prescription sample under the indium lamp of embodiment 7.
Reference examples 7
Be 10 seconds the set time of prescription sample under the UV lamp of embodiment 7.
Embodiment 8
Bisphenol A epoxy acrylate 3wt%
Acrylic copolymer 7wt%
TPGDA 25wt％
EO-TMPTA 45wt％
DEA-TMPTA 15wt％
BMS 2wt％
EDAB 1wt％
Pearlescence 2wt%
Above-mentioned component according to described mixed, is stirred, promptly prepare visible-light curing metallic paint.
Purposes: pearlescent lacquer
Be 5 seconds the set time of prescription sample under the indium lamp of embodiment 8.
Reference examples 8
Be 7 seconds the set time of prescription sample under the UV lamp of embodiment 8.
Embodiment 9
Bisphenol A epoxy acrylate 15wt%
Urethane acrylate 5wt%
TPGDA 15wt％
TMPTA 30wt％
DEA-TMPTA 20wt％
ITX 2.5wt％
BP 2wt％
Aluminium powder 0.5wt%
N-BUTYL ACETATE 10wt%
Above-mentioned component according to described mixed, is stirred, promptly prepare visible-light curing metallic paint.
Purposes: flash of light silver paint
Be 7 seconds the set time of prescription sample under the indium lamp of embodiment 9.
Reference examples 9
Be 9 seconds the set time of prescription sample under the UV lamp of embodiment 9.
Initiator content and the test result of embodiments of the invention 1-9 see Table 1.
Initiator combination and the test result of table 1 embodiment 1-9
| Embodiment | Purposes | The initiator combination | Set time | Sticking power | 60 degree gloss | Pencil hardness |
| Embodiment 1 | High light varnish | ITX+DEA-TMPTA | 5s | 0 grade | 110 | 3H |
| Embodiment 2 | High light varnish | 819+DEA-TMPTA | 5s | 0 grade | 105 | 3H |
| Embodiment 3 | Half matte varnish | TPO+DEA-TMPTA | 6s | 0 grade | 55 | 2H |
| Embodiment 4 | Half matte varnish | ITX+184+DEA-TMPTA | 6s | 0 grade | 60 | 3H |
| Embodiment 5 | Full matte varnish | 819+1173+DEA-TMPTA | 3s | 1 grade | 25 | 2H |
| Embodiment 6 | White paint | TPO+184+DEA-TMPTA | 10s | 1 grade | 45 | 2H |
| Embodiment 7 | Blue lacquer | CTX+DEA-TMPTA | 8s | 1 grade | 50 | 2H |
| Embodiment 8 | Pearlescent lacquer | BMS+EDAB+DEA-TMPTA | 5s | 1 grade | 75 | 2H |
| Embodiment 9 | The flash of light silver paint | ITX+BP+DEA-TMPTA | 7s | 1 grade | 80 | 2H |
| Testing method | ———— | —— | —— | GB/T9286 | GB/T9754 | GB/T 6739 |
From the foregoing description and reference examples as can be seen, light trigger described in the present invention and aided initiating carry out suitable combination, and solidifying with UV-light (high voltage mercury lamp) with visible light (indium lamp) curing ratio needs the shorter time, and has good film performance.The charateristic avsorption band that shows the combined light initiator can move to the visible spectrum zone to the long wave direction from the UV spectrum zone, thereby realizes visible-light curing.Compare with UV-curing technology, visible-light curing is safe ready more, and this will promote photocuring technology to a certain extent and further advance.
Claims (6)
1. visible-light curing metallic paint, it is characterized in that: the composition of described visible-light curing metallic paint and content are:
The prepolymer 0-20wt% that contains alkene class unsaturated group
The monomer 20-80wt% that contains alkene class unsaturated group
Light trigger 1-10wt%
Aided initiating 0.5-30wt%
Auxiliary agent 0-10wt%
Filler and/or pigment 0-40wt%
Solvent 0-30wt%;
The described prepolymer that contains alkene class unsaturated group comprises epoxy (methyl) acrylate, urethane (methyl) acrylate, polyester (methyl) acrylate, polyethers (methyl) acrylate, acrylic copolymer or their any mixture;
The described monomer that contains alkene class unsaturated group comprises styrenic, (methyl) esters of acrylic acid, vinyl ethers or their any mixture;
Described light trigger comprises benzoin ethers, benzil ketals class, acetophenones, anthraquinone class, thioxanthones, Benzophenones, acyl group see oxygen compound class, benzoates or dicyclo cyclohexadione compounds;
Described aided initiating comprises the acrylic ester monomer or the prepolymer of alkyl hydroxy aminated compounds, dimethylaminobenzoic acid ester compound or amine modification.
2. coating as claimed in claim 1, it is characterized in that: described epoxy (methyl) acrylate is the adduct of Resins, epoxy and unsaturated carboxylic acid reaction, comprises epoxy (methyl) acrylate of epoxy (methyl) acrylate, phenol or cresol-novolac epoxy resin of bisphenol A type epoxy resin or (methyl) acrylate of diglycidyl ether;
The reaction product that the reaction of described urethane (methyl) acrylate by hydroxyl (methyl) acrylate and polyvalent alcohol and organic multiple isocyanate makes;
(methyl) acrylate of described hydroxyl is (methyl) 2-hydroxyethyl acrylate or (methyl) vinylformic acid-2-hydroxypropyl ester; Described polyvalent alcohol comprises ethylene glycol, propylene glycol or butyleneglycol; Described organic multiple isocyanate comprises tolylene diisocyanate, 4,4 '-diphenylmethanediisocyanate, 4,4 '-dicyclohexyl methane diisocyanate, hexamethylene diisocyanate or isophorone diisocyanate;
Described polyester (methyl) acrylate is polyester polyol and (methyl) acrylic acid dehydrating condensation product;
Described polyester polyol is the reaction product of polyvalent alcohol and diprotic acid, and wherein polyvalent alcohol comprises ethylene glycol, polypropylene glycol, 1,6-hexylene glycol or TriMethylolPropane(TMP); Diprotic acid comprises hexanodioic acid, succsinic acid, phthalic acid, hexahydro-phthalic acid or terephthalic acid;
Described polyethers (methyl) acrylate is polyoxyethylene glycol two (methyl) acrylate or polypropylene glycol two (methyl) acrylate;
Described acrylic copolymer is vinylformic acid, acrylate or styrene monomer, under the Benzoyl Peroxide effect, by the compounds that Raolical polymerizable obtained.
3. coating as claimed in claim 1 is characterized in that: described styrene monomer comprises vinylbenzene or alpha-methyl styrene;
Described (methyl) acrylic ester monomer comprises the monomeric butyl acrylate of simple function group, cyclohexyl acrylate, Isooctyl acrylate monomer, (methyl) vinylformic acid-2-hydroxyl ethyl ester or (methyl) vinylformic acid-2-hydroxypropyl acrylate;
Or bifunctional monomer's 1,6 hexanediol diacrylate, tri (propylene glycol) diacrylate, propylene glycol diacrylate, neopentylglycol diacrylate, ethoxylated neopentylglycol diacrylate, bisphenol a diacrylate, tetraethylene-glycol diacrylate or PDDA;
Or the monomeric Viscoat 295 of trifunctional, ethoxylated trimethylolpropane triacrylate, propoxylation Viscoat 295, pentaerythritol triacrylate or three (2-hydroxyethyl) isocyanuric acid triacrylate;
Or the tetramethylol methane tetraacrylate of polyfunctional monomer, Dipentaerythritol five acrylate or dipentaerythritol acrylate;
Or any two or more mixture of above-mentioned (methyl) acrylic ester monomer;
Described vinyl ethers monomer comprises hexanaphthene dimethyl alcohol divinyl ether, hydroxyethyl vinyl ether or triethylene glycol divinyl ether;
4. coating as claimed in claim 1 is characterized in that: the described monomer that contains alkene class unsaturated group further comprises N-vinyl pyrrolidone, N-caprolactam, acryloyl morpholine, N-vinyl formamide or N-vinyl acetamide.
5. coating as claimed in claim 1 is characterized in that: described benzoin ether photoinitiator is benzoin methyl ether, bitter almond oil camphor ethyl ether or bitter almond oil camphor isopropyl ether;
Described benzil ketals photoinitiator is the benzil dimethyl ketal;
Described acetophenones light trigger is a methyl phenyl ketone, 2,2-dimethoxy-2-phenyl methyl phenyl ketone, 2,2-diethoxy-2-phenyl methyl phenyl ketone, 1,1-dichloroacetophenone, 1-hydroxy acetophenone, 1-hydroxy-cyclohexyl phenyl ketone, 2-hydroxy-2-methyl-1-phenyl-1-acetone, 1-(4-isopropyl phenyl)-2-hydroxy-2-methyl-1-acetone, 1-[4-(2-hydroxyl-oxethyl) phenyl]-2-hydroxy-2-methyl-1-acetone, 2-methyl isophthalic acid-[4-(methyl mercapto) phenyl]-2-morpholinyl-1-acetone or 2-benzyl-2-dimethylamino-1-(4-morpholinyl phenyl)-1-butanone;
Described anthraquinone photoinitiator is 2-tertiary butyl anthraquinone, 1-chloroanthraquinone or 2-amyl anthraquinone;
Described thioxanthone photoinitiator is 2,4-dimethyl thia anthrone, 2,4-diethyl thioxanthone, 2-isopropyl thioxanthone, 4-isopropyl thioxanthone, 2-chloro thioxanthone or 2,4-di-isopropyl thioxanthone;
Described Benzophenones light trigger is benzophenone, 4-chlorobenzophenone, to methyldiphenyl ketone or 4-benzoyl-4 '-dimethyl diphenyl sulfide;
The described acyl group oxygen compound photoinitiator of seeing is 2,4,6-trimethylbenzoyl diphenyl phosphine oxide, two (2,4, the 6-trimethylbenzoyl)-phenyl phosphine oxide, two (2, the 6-dimethylbenzoyl)-2,4,4-tri-methyl-amyl phosphine oxide or 2,4,6-trimethylbenzoyl phenyl ethoxy phosphine oxide;
Described benzoic ether photoinitiator is benzoylbenzoic acid methyl esters or methyl o-benzoylbenzoate;
Described dicyclo cyclohexadione compounds is camphorquinone or two imidazoles.
6. coating as claimed in claim 1 is characterized in that: described aided initiating alkyl hydroxy amine is trolamine, tri-isopropanolamine or methyldiethanolamine;
Described aided initiating dimethylaminobenzoic acid ester class is 4-dimethylamino-ethyl benzoate or the different monooctyl ester of 4-dimethylaminobenzoic acid;
The acrylic ester monomer of described aided initiating amine modification or prepolymer are that the reaction product that affine substitution reaction obtains takes place for aminated compounds and acrylic ester monomer or prepolymer, comprise diethylamine modification Viscoat 295 or diethylamine modification ethoxylated trimethylolpropane triacrylate.