CN108646322A - A kind of on-slip film resin eyeglass and its production technology - Google Patents
A kind of on-slip film resin eyeglass and its production technology Download PDFInfo
- Publication number
- CN108646322A CN108646322A CN201810682756.7A CN201810682756A CN108646322A CN 108646322 A CN108646322 A CN 108646322A CN 201810682756 A CN201810682756 A CN 201810682756A CN 108646322 A CN108646322 A CN 108646322A
- Authority
- CN
- China
- Prior art keywords
- slip film
- eyeglass
- film
- slip
- production technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of on-slip film resin eyeglass of the present invention and its production technology, belong to lens technology field, including super waterproof film glass（1）With on-slip film, the super waterproof film glass（1）The resin lens of super waterproof membrane are plated for outer surface, it is characterised in that：The on-slip film is fluoride films, including outside on-slip film（2）With inside on-slip film（3）, thickness is 40nm~60nm, and the on-slip film secure attachment is in super waterproof film glass（1）Surface.Membrane system of the present invention and process design science, reasonable, novelty, product configurations are simple, last layer is plated outside eyeglass original film layer deliquesces structure on-slip film, eyeglass anti-cutting frontier defense slipping effect is apparent, on-slip film layer can be removed by gently being wiped with wet rubbing eyeglass cloth after the completion of eyeglass cut edge, eyeglass keeps original various performances, facilitates batch operation, effect safe and reliable.
Description
Technical field
The present invention relates to lens technology field more particularly to on-slip film resin eyeglass and its production technologies.
Technical background
Super waterproof eyeglass has good hydrophobic（Waterproof）Property, after causing eyeglass to contact with water in cut edge, it is easy to skid,
Axle position is caused to deviate and the harmful effects such as lens deformation.The prior art can prevent eyeglass by super waterproof lens sticker Anti-skid adhesive piece
It skids, still, attaches and the operation of removal Anti-skid adhesive piece is all cumbersome, it has not been convenient to which batch operation influences production efficiency, sometimes also
Eyeglass can be caused to damage.
Invention content
It is generated in terms of in order to solve the problems, such as above-mentioned eyeglass production, present invention aims at provide a kind of on-slip film resin
Eyeglass skill comprising deliquesce structure fluoride films construction, solid structure or liquid structure can be presented in the on-slip film.The present invention is another
One purpose is：A kind of on-slip film resin lens producing technology is provided.
The above-mentioned technical problem of the present invention is mainly to be addressed by following technical proposals：
A kind of on-slip film resin eyeglass and its production technology, the on-slip film resin eyeglass include eyeglass and on-slip film, feature
It is：The on-slip film is fluoride films, thickness 40nm（Nanometer）~60nm, the on-slip film secure attachment is in eyeglass table
Face.
A kind of on-slip film resin eyeglass and its production technology, it is characterised in that：The fluoride is Fuization Magnesium.
A kind of on-slip film resin eyeglass and its production technology, it is characterised in that：The fluoride is Fuization Magnesium, is fluorinated
Calcium, potassium fluoride, aluminum fluoride, any of which or a variety of.
A kind of on-slip film resin eyeglass and its production technology, it is characterised in that：The on-slip film has the micro- of deliquescence
See physique.
A kind of on-slip film resin eyeglass and its production technology, it is characterised in that：The on-slip film is solid knot
Structure or liquid structure.
A kind of on-slip film resin eyeglass and its production technology, it is characterised in that：The on-slip film includes outside on-slip
Film, the outside on-slip film secure attachment is in eyeglass outer surface.
A kind of on-slip film resin eyeglass and its production technology, it is characterised in that：The on-slip film includes inside on-slip
Film, the inside on-slip film secure attachment is in eyeglass inner surface.
A kind of on-slip film resin eyeglass and its production technology, it is characterised in that：The on-slip film includes outside on-slip
Film and inside on-slip film, the outside on-slip film secure attachment exist in eyeglass outer surface, the inside on-slip film secure attachment
Eyeglass inner surface.
A kind of on-slip film resin eyeglass and its production technology, it is characterised in that：The production technology is as follows：
On vacuum coating equipment, plated film vacuum degree is set as 3.0 × 10-3pa（Pa）, temperature is 35 DEG C~45 DEG C, respectively in mirror
On-slip film, thickness 40nm, evaporation rate 0.60nm/s is deposited in the both sides of piece（Nm/sec）.
A kind of on-slip film resin eyeglass and its production technology, it is characterised in that：The production technology is as follows：
On vacuum coating equipment, plated film vacuum degree is set as 3.0 × 10-3Pa, temperature is 35 DEG C~45 DEG C, respectively in eyeglass
On-slip film is deposited in both sides, and thickness is 40nm~60nm, evaporation rate 0.40nm/s~0.80nm/s.
On-slip film resin eyeglass of the present invention and its production technology, membrane system and process design science, reasonable, novel, production
Product simple structure plates last layer deliquescence structure on-slip film outside eyeglass original film layer, and eyeglass anti-cutting frontier defense slipping effect is apparent, eyeglass
On-slip film layer can be removed by gently being wiped with wet rubbing eyeglass cloth after the completion of cut edge, and eyeglass keeps original various performances, and batch is facilitated to grasp
Make, effect is safe and reliable.
Description of the drawings
Fig. 1 is optical film partial schematic diagram on the outside of a kind of on-slip film resin eyeglass of the present invention；
Fig. 2 is optical film partial schematic diagram on the inside of a kind of on-slip film resin eyeglass of the present invention；
In above-mentioned attached drawing：1- eyeglasses；On-slip film on the outside of 2-；On-slip film on the inside of 3-.
The present invention is further illustrated with reference to the accompanying drawings and examples.
Specific implementation mode
The present embodiment preferably 1.598 acrylics（Acrylics）Material plates super waterproof film glass 250, passes through vacuum
The method of plated film plates one layer of fluoride, and the fluoride is Fuization Magnesium, calcirm-fluoride, potassium fluoride, aluminum fluoride any of which or more
Kind, thickness is 40 nm~60nm, obtains on-slip film resin eyeglass.
On-slip film resin eyeglass of the present invention, including super waterproof film glass 1 and on-slip film, the super waterproof film glass 1 are
The resin lens of super waterproof membrane are plated in outer surface, and the eyeglass includes plano lens, concave lens, hyperopic lens or old light microscopic piece,
The on-slip film includes outside on-slip film 2 and inside on-slip film 3, and the on-slip film is fluoride films, and thickness is preferably 40nm,
In the present embodiment, the preferred Fuization Magnesium of fluoride.
The on-slip film resin lens producing technology and steps are as follows：
On vacuum coating equipment, plated film vacuum degree is set as 3.0 × 10-3Pa, temperature be 35~45 DEG C, the both sides of eyeglass by
Layer vapor deposition Fuization Magnesium vacuum diaphragms, thickness 40nm, 0.40 nm/s of evaporation rate~0.80nm/s, the present embodiment evaporation rate are excellent
Select 0.60 nm/s.
The on-slip film secure attachment（Attachment）On 1 surface of resin lens of super waterproof membrane, as shown in Figure 1, the outside
2 secure attachment of on-slip film is in super 1 outer surface of waterproof film glass, as shown in Fig. 2, 3 secure attachment of inside on-slip film is super
1 inner surface of waterproof film glass.
Present invention batch plates last layer on-slip film outside the former film layer of super waterproof eyeglass 1, so non-slip when eyeglass cut edge.
In the present embodiment, the fluoride has the physical change characteristic of deliquescence, so, the on-slip film has the microphysics that can be deliquesced
Construction.The deliquescence is the vapor in on-slip film spontaneous absorption moisture or air, and saturated solution, i.e. on-slip film are formed by solid
Solution is become from solid-state construction（Liquid）Construction.Since they do not generate novel substance, deliquescence is physical change.In practical application
In, since on-slip film can deliquesce, gently wiped with water or wet rubbing eyeglass cloth, so that it becomes liquid solution, then erasable on-slip film layer.
In addition to the above, the present invention can also have other embodiment, and redundant, every use are not replaced equally one by one herein
Change or equivalent transformation formed technical solution, belong to the present invention claims protection domain.
Claims (10)
1. a kind of on-slip film resin eyeglass and its production technology, the on-slip film resin eyeglass includes eyeglass（1）With on-slip film,
It is characterized in that：The on-slip film is fluoride films, and thickness is 40nm~60nm, and the on-slip film secure attachment is in eyeglass（1）Table
Face.
2. a kind of on-slip film resin eyeglass and its production technology according to claim 1, it is characterised in that：The fluoride is
Fuization Magnesium.
3. a kind of on-slip film resin eyeglass and its production technology according to claim 1, it is characterised in that：The fluoride is
Fuization Magnesium, calcirm-fluoride, potassium fluoride, aluminum fluoride, any of which or a variety of.
4. a kind of on-slip film resin eyeglass and its production technology according to claim 1, it is characterised in that：The on-slip film tool
There is the microphysics of deliquescence to construct.
5. a kind of on-slip film resin eyeglass and its production technology according to claim 1, it is characterised in that：The on-slip film is
Solid structure or liquid structure.
6. a kind of on-slip film resin eyeglass and its production technology according to claim 1, it is characterised in that：The on-slip film packet
Include outside on-slip film（2）, the outside on-slip film（2）Secure attachment is in eyeglass（1）Outer surface.
7. a kind of on-slip film resin eyeglass and its production technology according to claim 1, it is characterised in that：The on-slip film packet
Include inside on-slip film（3）, the inside on-slip film（3）Secure attachment is in eyeglass（1）Inner surface.
8. a kind of on-slip film resin eyeglass and its production technology according to claim 1, it is characterised in that：The on-slip film packet
Include outside on-slip film（2）With inside on-slip film（3）, the outside on-slip film（2）Secure attachment is in eyeglass（1）Outer surface, institute
State inside on-slip film（3）Secure attachment is in eyeglass（1）Inner surface.
9. a kind of on-slip film resin eyeglass and its production technology according to claim 1, it is characterised in that：The production technology
It is as follows：
On vacuum coating equipment, plated film vacuum degree is set as 3.0 × 10-3Pa, temperature is 35 DEG C~45 DEG C, respectively in eyeglass（1）
Both sides be deposited on-slip film, thickness 40nm, 0.60 nm/s of evaporation rate.
10. a kind of on-slip film resin eyeglass and its production technology according to claim 1, it is characterised in that：The production work
Skill is as follows：
On vacuum coating equipment, plated film vacuum degree is set as 3.0 × 10-3Pa, temperature is 35 DEG C~45 DEG C, respectively in eyeglass（1）
Both sides be deposited on-slip film, thickness be 40nm~60nm, evaporation rate 0.40nm/s~0.80nm/s.