CN105113271A - Preparation method of fireproof smoke-suppressing PVC synthetic leather - Google Patents
Preparation method of fireproof smoke-suppressing PVC synthetic leather Download PDFInfo
- Publication number
- CN105113271A CN105113271A CN201510607348.1A CN201510607348A CN105113271A CN 105113271 A CN105113271 A CN 105113271A CN 201510607348 A CN201510607348 A CN 201510607348A CN 105113271 A CN105113271 A CN 105113271A
- Authority
- CN
- China
- Prior art keywords
- polyvinyl chloride
- layer
- weight portion
- mixed paste
- synthetic leather
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of fireproof smoke-suppressing PVC synthetic leather. The PVC synthetic leather is prepared by tightly compositing a polyurethane fabric layer, a PVC layer, a glass fiber cloth bottom layer from top to bottom, wherein the PVC layer is prepared through the steps of blending PVC, a plasticizer, tris(2-chloroethyl) phosphate, epoxidized aliphatic ester, aluminium hydroxide, magnesium hydroxide, a barium zinc stabilizer and PVC color paste into mixed paste with certain viscosity and drying the mixed paste. The preparation method comprises the following steps: preparing the mixed paste, drying the mixed paste to obtain the PVC layer, bonding the polyurethane fabric layer, PVC layer and glass fiber cloth bottom layer into a whole by using the mixed paste step by step, drying, and trimming, so as to obtain the PVC synthetic leather. The PVC synthetic leather is fireproof, thermal-insulating and sound-insulating, suppresses smoke, and is more ideal in use effect.
Description
Technical field
The invention belongs to artificial leather production technical field, relate to PVC synthetic leather production technical field, particularly a kind of fire prevention presses down the preparation method of the PVC synthetic leather of cigarette.
Background technology
At present, the range of application of synthetic leather says benefit extensively, but the application in building trade is at the early-stage, be mainly used in the inner wall decoration of household and place of public amusement, the inner wall decoration of place of public amusement presses down cigarette and there are certain requirements heat insulation, sound insulation, fire prevention, the fire-retardant PVC synthetic leather of prior art, its fire retardant normally adds antimonous oxide fire retardant, antimonous oxide is the fire retardant applied the earliest, and when being used alone, consumption is large, and flame retardant effect is poor; When with halide (R.HX) and the used time then have good cooperative effect, flame retardant effect is obvious.
The fire-retardant PVC synthetic leather of prior art, can use certainly, but only prevent fires not press down the inadequate Environmental Safety of cigarette, have impact on the use of synthetic leather in building trade to a certain extent.Smog to produce at first and the most lethal and affect the factor on fire fighting opportunity adversely in a fire, death toll according to statistics in fire have 80% be suffocate caused by, so it is more even more important than " fire-retardant " " to press down cigarette " to the PVC synthetic leather of building trade application, the fire-retardant PVC synthetic leather of prior art is only prevented fires and is not pressed down cigarette, heat-insulating sound-insulating heat insulation effect is also poor, and its fire retardant used is from bibliographical information, has carcinogenic possibility, result of use is desirable not enough.
Summary of the invention
For overcoming the deficiencies in the prior art, the invention provides the preparation method that a kind of fire prevention presses down the PVC synthetic leather of cigarette.
The present invention for the technical scheme reaching above-mentioned technical purpose and adopt is: a kind of fire prevention presses down the preparation method of the PVC synthetic leather of cigarette, described PVC synthetic leather from top to bottom by polyurethane fabric layer, polyvinyl chloride layer, glass fabric bottom totally three layers be closely composited; Wherein, described polyvinyl chloride layer makes after being dried by the mixed paste of polyvinyl chloride, plasticizer, three (2-chloroethyl) phosphate, epoxy aliphatic ester, aluminium hydroxide, magnesium hydroxide, barium zinc stabilizer, polyvinyl chloride color; Described preparation method comprises the following steps:
Steps A, preparation mixed paste; The preparation of mixed paste utilizes DOTP, as plasticizer, the mixed material of polyvinyl chloride, three (2-chloroethyl) phosphate, epoxy aliphatic ester, aluminium hydroxide, magnesium hydroxide, barium zinc stabilizer, polyvinyl chloride color is diluted to the mixed paste that viscosity number is 1500-3000cps; Wherein:
The weight portion of polyvinyl chloride: 100 parts;
The weight portion of DOTP: 10-30 part;
The weight portion of three (2-chloroethyl) phosphate: 10-30 part;
The weight portion of epoxy aliphatic ester: 5-10 part;
Aluminium hydroxide weight portion: 30-80 part;
The weight portion of magnesium hydroxide: be 1 with the ratio of the weight portion of above-mentioned aluminium hydroxide used
:2;
The weight portion of barium zinc stabilizer: 1-3 part;
The weight portion of polyvinyl chloride color: 1-10 part;
Step B, the polyurethane slurry prepared by traditional handicraft is spread evenly across in lines release liners, after peeling off lines release liners after drying, makes polyurethane fabric layer; On the bottom surface of the polyurethane fabric layer made, use precision coating machine with the good above-mentioned mixed paste prepared of the coating thickness even spread being less than 0.5mm again, after oven dry, make the combination layer of above-mentioned polyvinyl chloride layer and above-mentioned polyurethane fabric layer; Described bake out temperature is 175-185 DEG C;
Step C, on the polyvinyl chloride of combinations thereof layer is laminated, after laminating after the above-mentioned thickener of precision coating machine even spread is dried after glass fabric bottom at 175-185 DEG C of temperature, obtain three layers of tight composite bed, the coating thickness of this thickener will adjust with reference to the thickness of fiberglass cloth, make the coating weight of coating mixed paste just by fiberglass cloth complete wetting, if the thickener amount of coating is very few, there will be the phenomenon that the glass fabric bottom of finished product is easily cracked; If the thickener amount of coating is too much, then there will be in production process easy sizing on compound wheel face, affect the attractive in appearance of the product back side;
PVC synthetic leather is obtained after step D, trimming.
The invention has the beneficial effects as follows: due to the PVC synthetic leather formula for a product of the present invention by optimizing, the proportioning of cigarette material is pressed down by combination fire prevention, simultaneously by combination composite glass fiber cloth, utilize that glass fibre is high temperature resistant, fire-retardant, rotproofness is good, the feature that thermal insulation is good, sound-proofing is good, reach the object that fire prevention presses down cigarette, heat-insulating sound-insulating, result of use is better.
Below in conjunction with embodiment, the invention will be further described.
Detailed description of the invention
Embodiments of the invention 1, a kind of fire prevention presses down the preparation method of PVC synthetic leather of cigarette, described PVC synthetic leather from top to bottom by polyurethane fabric layer, polyvinyl chloride layer, glass fabric bottom totally three layers be closely composited; Wherein, described polyvinyl chloride layer makes after being dried by the mixed paste of polyvinyl chloride, plasticizer, three (2-chloroethyl) phosphate, epoxy aliphatic ester, aluminium hydroxide, magnesium hydroxide, barium zinc stabilizer, polyvinyl chloride color; Described preparation method comprises the following steps:
Steps A, preparation mixed paste; The preparation of mixed paste utilizes DOTP, as plasticizer, the mixed material of polyvinyl chloride, three (2-chloroethyl) phosphate, epoxy aliphatic ester, aluminium hydroxide, magnesium hydroxide, barium zinc stabilizer, polyvinyl chloride color is diluted to the mixed paste that viscosity number is 1500cps; Wherein: the weight portion of polyvinyl chloride: 100 parts;
The weight portion of DOTP: 30 parts;
The weight portion of three (2-chloroethyl) phosphate: 10 parts;
The weight portion of epoxy aliphatic ester: 5 parts;
Aluminium hydroxide weight portion: 30 parts;
The weight portion of magnesium hydroxide: 15 parts;
The weight portion of barium zinc stabilizer: 1 part;
The weight portion of polyvinyl chloride color: 1 part;
Step B, the polyurethane slurry prepared by traditional handicraft is spread evenly across in lines release liners, after peeling off lines release liners after drying, makes polyurethane fabric layer; On the bottom surface of the polyurethane fabric layer made, use precision coating machine with the good above-mentioned mixed paste prepared of the coating thickness even spread being less than 0.5mm again, after oven dry, make the combination layer of above-mentioned polyvinyl chloride layer and above-mentioned polyurethane fabric layer; Described bake out temperature is 175 DEG C;
Step C, on the polyvinyl chloride of combinations thereof layer is laminated, after laminating after the above-mentioned thickener of precision coating machine even spread is dried after glass fabric bottom at 175 DEG C of temperature, obtain three layers of tight composite bed, the coating thickness of this thickener will adjust with reference to the thickness of fiberglass cloth, make the coating weight of coating mixed paste just by fiberglass cloth complete wetting, if the thickener amount of coating is very few, there will be the phenomenon that the glass fabric bottom of finished product is easily cracked; If the thickener amount of coating is too much, then there will be in production process easy sizing on compound wheel face, affect the attractive in appearance of the product back side;
PVC synthetic leather is obtained after step D, trimming.
Embodiments of the invention 2, a kind of fire prevention presses down the preparation method of PVC synthetic leather of cigarette, described PVC synthetic leather from top to bottom by polyurethane fabric layer, polyvinyl chloride layer, glass fabric bottom totally three layers be closely composited; Wherein, described polyvinyl chloride layer makes after being dried by the mixed paste of polyvinyl chloride, plasticizer, three (2-chloroethyl) phosphate, epoxy aliphatic ester, aluminium hydroxide, magnesium hydroxide, barium zinc stabilizer, polyvinyl chloride color; Described preparation method comprises the following steps:
Steps A, preparation mixed paste; The preparation of mixed paste utilizes DOTP, as plasticizer, the mixed material of polyvinyl chloride, three (2-chloroethyl) phosphate, epoxy aliphatic ester, aluminium hydroxide, magnesium hydroxide, barium zinc stabilizer, polyvinyl chloride color is diluted to the mixed paste that viscosity number is 3000cps; Wherein: the weight portion of polyvinyl chloride: 100 parts;
The weight portion of DOTP: 10 parts;
The weight portion of three (2-chloroethyl) phosphate: 30 parts;
The weight portion of epoxy aliphatic ester: 10 parts;
Aluminium hydroxide weight portion: 80 parts;
The weight portion of magnesium hydroxide: 40 parts;
The weight portion of barium zinc stabilizer: 3 parts;
The weight portion of polyvinyl chloride color: 10 parts;
Step B, the polyurethane slurry prepared by traditional handicraft is spread evenly across in lines release liners, after peeling off lines release liners after drying, makes polyurethane fabric layer; On the bottom surface of the polyurethane fabric layer made, use precision coating machine with the good above-mentioned mixed paste prepared of the coating thickness even spread being less than 0.5mm again, after oven dry, make the combination layer of above-mentioned polyvinyl chloride layer and above-mentioned polyurethane fabric layer; Described bake out temperature is 185 DEG C;
Step C, on the polyvinyl chloride of combinations thereof layer is laminated, after laminating after the above-mentioned thickener of precision coating machine even spread is dried after glass fabric bottom at 185 DEG C of temperature, obtain three layers of tight composite bed, the coating thickness of this thickener will adjust with reference to the thickness of fiberglass cloth, make the coating weight of coating mixed paste just by fiberglass cloth complete wetting, if the thickener amount of coating is very few, there will be the phenomenon that the glass fabric bottom of finished product is easily cracked; If the thickener amount of coating is too much, then there will be in production process easy sizing on compound wheel face, affect the attractive in appearance of the product back side;
PVC synthetic leather is obtained after step D, trimming.
Embodiments of the invention 3, a kind of fire prevention presses down the preparation method of PVC synthetic leather of cigarette, described PVC synthetic leather from top to bottom by polyurethane fabric layer, polyvinyl chloride layer, glass fabric bottom totally three layers be closely composited; Wherein, described polyvinyl chloride layer makes after being dried by the mixed paste of polyvinyl chloride, plasticizer, three (2-chloroethyl) phosphate, epoxy aliphatic ester, aluminium hydroxide, magnesium hydroxide, barium zinc stabilizer, polyvinyl chloride color; Described preparation method comprises the following steps:
Steps A, preparation mixed paste; The preparation of mixed paste utilizes DOTP, as plasticizer, the mixed material of polyvinyl chloride, three (2-chloroethyl) phosphate, epoxy aliphatic ester, aluminium hydroxide, magnesium hydroxide, barium zinc stabilizer, polyvinyl chloride color is diluted to the mixed paste that viscosity number is 2200cps; Wherein: the weight portion of polyvinyl chloride: 100 parts;
The weight portion of DOTP: 20 parts;
The weight portion of three (2-chloroethyl) phosphate: 20 parts;
The weight portion of epoxy aliphatic ester: 7 parts;
Aluminium hydroxide weight portion: 56 parts;
The weight portion of magnesium hydroxide: 28 parts;
The weight portion of barium zinc stabilizer: 2 parts;
The weight portion of polyvinyl chloride color: 5 parts;
Step B, the polyurethane slurry prepared by traditional handicraft is spread evenly across in lines release liners, after peeling off lines release liners after drying, makes polyurethane fabric layer; On the bottom surface of the polyurethane fabric layer made, use precision coating machine with the good above-mentioned mixed paste prepared of the coating thickness even spread being less than 0.5mm again, after oven dry, make the combination layer of above-mentioned polyvinyl chloride layer and above-mentioned polyurethane fabric layer; Described bake out temperature is 180 DEG C;
Step C, on the polyvinyl chloride of combinations thereof layer is laminated, after laminating after the above-mentioned thickener of precision coating machine even spread is dried after glass fabric bottom at 180 DEG C of temperature, obtain three layers of tight composite bed, the coating thickness of this thickener will adjust with reference to the thickness of fiberglass cloth, make the coating weight of coating mixed paste just by fiberglass cloth complete wetting, if the thickener amount of coating is very few, there will be the phenomenon that the glass fabric bottom of finished product is easily cracked; If the thickener amount of coating is too much, then there will be in production process easy sizing on compound wheel face, affect the attractive in appearance of the product back side;
PVC synthetic leather is obtained after step D, trimming.
Claims (1)
1. fire prevention presses down the preparation method of PVC synthetic leather for cigarette, it is characterized in that: described PVC synthetic leather from top to bottom by polyurethane fabric layer, polyvinyl chloride layer, glass fabric bottom totally three layers be closely composited; Wherein, described polyvinyl chloride layer makes after being dried by the mixed paste of polyvinyl chloride, plasticizer, three (2-chloroethyl) phosphate, epoxy aliphatic ester, aluminium hydroxide, magnesium hydroxide, barium zinc stabilizer, polyvinyl chloride color; Described preparation method comprises the following steps:
Steps A, preparation mixed paste; The preparation of mixed paste utilizes DOTP, as plasticizer, the mixed material of polyvinyl chloride, three (2-chloroethyl) phosphate, epoxy aliphatic ester, aluminium hydroxide, magnesium hydroxide, barium zinc stabilizer, polyvinyl chloride color is diluted to the mixed paste that viscosity number is 1500-3000cps; Wherein:
The weight portion of polyvinyl chloride: 100 parts;
The weight portion of DOTP: 10-30 part;
The weight portion of three (2-chloroethyl) phosphate: 10-30 part;
The weight portion of epoxy aliphatic ester: 5-10 part;
Aluminium hydroxide weight portion: 30-80 part;
The weight portion of magnesium hydroxide: be 1:2 with the ratio of the weight portion of above-mentioned aluminium hydroxide used;
The weight portion of barium zinc stabilizer: 1-3 part;
The weight portion of polyvinyl chloride color: 1-10 part;
Step B, the polyurethane slurry prepared by traditional handicraft is spread evenly across in lines release liners, after peeling off lines release liners after drying, makes polyurethane fabric layer; On the bottom surface of the polyurethane fabric layer made, use precision coating machine with the good above-mentioned mixed paste prepared of the coating thickness even spread being less than 0.5mm again, after oven dry, make the combination layer of above-mentioned polyvinyl chloride layer and above-mentioned polyurethane fabric layer; Described bake out temperature is 175-185 DEG C;
Step C, on the polyvinyl chloride of combinations thereof layer is laminated, after laminating after the above-mentioned thickener of precision coating machine even spread is dried after glass fabric bottom at 175-185 DEG C of temperature, obtain three layers of tight composite bed, the coating thickness of this thickener will adjust with reference to the thickness of fiberglass cloth, make the coating weight of coating mixed paste just by fiberglass cloth complete wetting, if the thickener amount of coating is very few, there will be the phenomenon that the glass fabric bottom of finished product is easily cracked; If the thickener amount of coating is too much, then there will be in production process easy sizing on compound wheel face, affect the attractive in appearance of the product back side;
PVC synthetic leather is obtained after step D, trimming.