CN104725570A - Latex and preparation method thereof - Google Patents
Latex and preparation method thereof Download PDFInfo
- Publication number
- CN104725570A CN104725570A CN201510036596.5A CN201510036596A CN104725570A CN 104725570 A CN104725570 A CN 104725570A CN 201510036596 A CN201510036596 A CN 201510036596A CN 104725570 A CN104725570 A CN 104725570A
- Authority
- CN
- China
- Prior art keywords
- latex
- modified polyurethane
- rubber latex
- water
- epoxy resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides latex prepared from the following raw materials in percentage by weight: 5-20% of water-based modified polyurethane rubber latex, 8-30% of methyl methacrylate, 6-20% of butyl acrylate, 0.5-1.0% of a functional monomer, 0.5-0.8% of sodium hydrogen carbonate, 0.8-1.2% of an anionic emulsifier, 0.4-0.6% of a nonionic emulsifier, 40-60% of deionized water and 0.2-0.6% of an initiating agent. According to the latex provided by the invention, an epoxy resin component is introduced into the water-based modified polyurethane rubber latex, so that modified polyurethane-acrylate grafted copolymerized latex can be endowed with the characteristics such as strong adhesive force with a base material, solvent resistance and excellent corrosion resistance of epoxy resin, the hardness of a latex film can reach 6H, the latex can form a film at room temperature, a rubber latex film is transparent, weather-resistant, water-resistant and heat-resistant, and similar characteristics are not reported in literatures.
Description
Technical field
The present invention relates to a kind of latex and preparation method thereof.
Background technology
Perfect further along with environmental law, low VOC or Diamond Search discharge new coating become the focus of research and development.Aqueous polyurethane is the new polyurethane system using water to replace organic solvent as dispersion medium, can be widely used in the aspects such as coating, tackiness agent, hide finishes, fabric finishing agent.Owing to possessing nontoxic, inexpensive, safe, improving constantly of advantage and the self performance such as not firing, show huge market outlook and have the trend progressively replacing solvent based product.Existence due to hydrophilic radical makes aqueous polyurethane product poor in water-fast, solvent resistant, weathering resistance etc.; And polyacrylic ester series products has good performance in weather-proof, water-fast, solvent resistant, film gloss retention etc., but do not possess that urethane intensity is high, elasticity and the advantage such as adhesiveproperties is good, therefore polyacrylic ester (PA) and urethane (PU) performance have good complementarity.
Summary of the invention
For above-mentioned defect and the problem of prior art, the object of this invention is to provide a kind of modified polyurethane-acrylic ester graft copolymerized latex and preparation method thereof, this latex had both had the splendid sticking power of urethane resin and wear resistance, there is again the extraordinary cold-hot water-based of acrylic resin, excellent weathering resistance, chemical-resistant and pigment wettability and mechanical stability against short circuit preferably, avoid the problem of shortcoming that urethane resin easily turns yellow and vinylformic acid, urethane mixed emulsion poor compatibility and poor chemical stability simultaneously.
Based on above-mentioned purpose, the invention provides following technical scheme:
A kind of latex, is made up of the raw material of following weight proportion: the watersoluble modified polyurethane rubber latex of 5 ~ 20%, the methyl methacrylate of 8 ~ 30%, 6 ~ 20% butyl acrylate, 0.5 ~ 1.0% functional monomer, 0.5 ~ 0.8% sodium bicarbonate, 0.8 ~ 1.2% anionic emulsifier, the nonionic emulsifier of 0.4 ~ 0.6%, the deionized water of 40 ~ 60% and 0.2 ~ 0.6% initiator.
Further, described watersoluble modified polyurethane rubber latex is made up of aliphatic diisocyanate, polyester polyol, epoxy resin, 2,2-two (methylol) propionic acid, Hydroxyethyl acrylate and triethylamines, adopts self-emulsification to be prepared from;
The weight ratio of described aliphatic diisocyanate, polyester polyol, epoxy resin, 2,2-two (methylol) propionic acid, Hydroxyethyl acrylate and triethylamines is 15: 19: 1: 1: 0.5: 1.5.
Further, the solid content of described watersoluble modified polyurethane rubber latex is 35 ~ 40%.
Beneficial effect of the present invention, because watersoluble modified polyurethane adhesive Ruzhong introduces epoxy resin ingredient, the feature of modified polyurethane-acrylic ester graft copolymerized latex epoxy resin can be given, as with the advantage such as the strong adhesion of base material, solvent resistance and antiseptic property be excellent, the hardness of latex film can up to 6H, and latex can room temperature film-forming, and latex film is transparent, weather-proof, water-fast and heat-resisting, similar character has no bibliographical information.
Embodiment
Below in conjunction with embodiments of the invention, be clearly and completely described technical scheme of the present invention, obviously, described embodiment is only the present invention's part embodiment, instead of whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art, not making the every other embodiment obtained under creative work prerequisite, belong to the scope of protection of the invention.
A kind of latex, is made up of the raw material of following weight proportion: the watersoluble modified polyurethane rubber latex of 5 ~ 20%, the methyl methacrylate of 8 ~ 30%, 6 ~ 20% butyl acrylate, 0.5 ~ 1.0% functional monomer, 0.5 ~ 0.8% sodium bicarbonate, 0.8 ~ 1.2% anionic emulsifier, the nonionic emulsifier of 0.4 ~ 0.6%, the deionized water of 40 ~ 60% and 0.2 ~ 0.6% initiator.
Preferably technical scheme, described watersoluble modified polyurethane rubber latex is made up of aliphatic diisocyanate, polyester polyol, epoxy resin, 2,2-two (methylol) propionic acid, Hydroxyethyl acrylate and triethylamines, adopts self-emulsification to be prepared from;
The weight ratio of described aliphatic diisocyanate, polyester polyol, epoxy resin, 2,2-two (methylol) propionic acid, Hydroxyethyl acrylate and triethylamines is 15: 19: 1: 1: 0.5: 1.5.
Preferably technical scheme, the solid content of described watersoluble modified polyurethane rubber latex is 35 ~ 40%.
Concrete steps are as follows:
(1) take each raw material of following weight proportion: the watersoluble modified polyurethane rubber latex of 5%, the methyl methacrylate of 30%, 12.1% butyl acrylate, 1.0% vinylformic acid, 0.5% sodium bicarbonate, 0.8% sodium lauryl sulphate, the polyoxyethylene nonylphenol ether of 0.4%, the deionized water of 50% and 0.2% Potassium Persulphate.
Wherein, above-mentioned methyl methacrylate, butyl acrylate, vinylformic acid, sodium bicarbonate, sodium lauryl sulphate, polyoxyethylene nonylphenol ether, deionized water and Potassium Persulphate are added room temperature pre-emulsification in emulsor, obtain pre-emulsion; Again the watersoluble modified polyurethane rubber latex in above-mentioned raw materials is added and stir in polymerization reactor, raised temperature to 70 DEG C;
(2) described pre-emulsion was evenly added drop-wise in 3 hours described watersoluble modified polyurethane adhesive Ruzhong, temperature controls at 80 DEG C;
(3) after dropping terminates, then at the temperature of 80 DEG C, stir after 0.5 hour, be warming up to 88 DEG C, continue reaction 0.5 hour, be cooled to 40 DEG C, filter, obtain modified polyurethane-acrylic ester graft copolymerized latex.
The modified polyurethane-acrylic ester graft copolymerized latex obtained is spherical, and particle diameter is 80nm.
The above; be only the specific embodiment of the present invention, but protection scope of the present invention is not limited thereto, is anyly familiar with those skilled in the art in the technical scope that the present invention discloses; change can be expected easily or replace, all should be encompassed within protection scope of the present invention.Therefore, protection scope of the present invention should described be as the criterion with the protection domain of claim.
Claims (3)
1. a latex, it is characterized in that, be made up of the raw material of following weight proportion: the watersoluble modified polyurethane rubber latex of 5 ~ 20%, the methyl methacrylate of 8 ~ 30%, 6 ~ 20% butyl acrylate, 0.5 ~ 1.0% functional monomer, 0.5 ~ 0.8% sodium bicarbonate, 0.8 ~ 1.2% anionic emulsifier, the nonionic emulsifier of 0.4 ~ 0.6%, the deionized water of 40 ~ 60% and 0.2 ~ 0.6% initiator.
2. latex according to claim 1, it is characterized in that, described watersoluble modified polyurethane rubber latex is made up of aliphatic diisocyanate, polyester polyol, epoxy resin, 2,2-two (methylol) propionic acid, Hydroxyethyl acrylate and triethylamines, adopts self-emulsification to be prepared from;
The weight ratio of described aliphatic diisocyanate, polyester polyol, epoxy resin, 2,2-two (methylol) propionic acid, Hydroxyethyl acrylate and triethylamines is 15: 19: 1: 1: 0.5: 1.5.
3. latex according to claim 1, is characterized in that, the solid content of described watersoluble modified polyurethane rubber latex is 35 ~ 40%.