CN102190618B - 有机化合物及包含其的有机电致发光装置 - Google Patents

有机化合物及包含其的有机电致发光装置 Download PDF

Info

Publication number
CN102190618B
CN102190618B CN 201010143878 CN201010143878A CN102190618B CN 102190618 B CN102190618 B CN 102190618B CN 201010143878 CN201010143878 CN 201010143878 CN 201010143878 A CN201010143878 A CN 201010143878A CN 102190618 B CN102190618 B CN 102190618B
Authority
CN
China
Prior art keywords
thickness
group
phenyl
compound
organic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN 201010143878
Other languages
English (en)
Other versions
CN102190618A (zh
Inventor
黄贺隆
林祺臻
赵登志
李豪浚
郑建鸿
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Industrial Technology Research Institute ITRI
Original Assignee
Industrial Technology Research Institute ITRI
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Industrial Technology Research Institute ITRI filed Critical Industrial Technology Research Institute ITRI
Priority to CN 201010143878 priority Critical patent/CN102190618B/zh
Publication of CN102190618A publication Critical patent/CN102190618A/zh
Application granted granted Critical
Publication of CN102190618B publication Critical patent/CN102190618B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供有机化合物及包含其的有机电致发光装置。该有机化合物具下所示的化学式:其中,R1、R2、R3、R4、R5、R6、及R7系分别为相同或不同的取代基,包含氢、C1-8烷基、C1-8烷氧基、C1-8卤烷基、芳香基、杂芳基、环烷基、杂环基、或环脂基;以及Z系独立且为
Figure DSA00000059221500011
Figure DSA00000059221500012
其中R8及R9系分别为相同或不同的取代基,包含芳香基、杂芳基、环烷基、杂环基、或环脂基。
Figure DSA00000059221500013

Description

有机化合物及包含其的有机电致发光装置
【技术领域】
本发明关于一种有机化合物及包含其的有机电致发光装置,特别关于一种作为主体材料的有机化合物及包含其的磷光有机电致发光装置。
【背景技术】
有机电致发光装置(organic electroluminescent device),亦称作有机发光二极管(organic light-emitting diode;OLED),是以有机层作为主动层的一种发光二极管(LED)。由于有机电致发光装置具有低电压操作、高亮度、重量轻、广视角、以及高对比值等优点,近年来已渐渐使用于平面面板显示器(flatpanel display)上。与液晶显示器不同,有机电致发光显示器所包含的有机发光二极管的像素阵列系具有自发光的特性,因此不需外加背光源。
一般而言,有机发光二极管元件包括一对电极,以及在电极之间的有机发光介质层。发光是导因于以下的现象。当电场施于两电极时,阴极射出电子到有机发光介质层,阳极射出空穴到有机发光介质层。当电子与空穴在有机发光介质层内结合时,会产生激子(excitons)。电子和空穴的再结合就伴随着发光。
依据空穴和电子的自旋态(spin state),由空穴和电子的再结合而产生的激子可具有三重态(triplet)或单重态(singlet)之自旋态。由单重态激子(singletexciton)所产生的发光为萤光(fluorescence),而由三重态激子(triplet exciton)所产生的发光为磷光(phosphorescence)。磷光的发光效率是萤光的三倍。因此,发展高效率的磷光材料以增进有机发光二极管元件的发光效率是非常重要的。
现今磷光材料在有机发光二极管元件的应用上,其放光机制须搭配能量相符的各种主体(host)材料才能达到最佳的放光效果与量子效率,而其中蓝光与绿光的主体材料需要有较大的能阶差值,而须符合这类要件的分子须有较短的共轭体系(conjugated system)。如果再考虑主体分子所需要的另一要件-热稳定性,也就是要有较大的分子质量,如此的需求对于主体分子结构设计上必带来相对的难度。
已有一些有化合物被报导出来应用于运用于蓝色或绿色磷光发光二极管(PHOLED)元件上,如美国专利公告号2003/0205696A1与美国专利公告号2007/0141391A1。该等化合物多数具有咔唑(carbazole)或多苯硅官能基的衍生物。然而,这些已知的材料有着热稳定性不佳或运用在元件上产生电流密度低等问题。因此,开发出新的磷光有机发光二极管所适用的材料,来解决习知的问题,对于有机发光二极管技术而言是一个很重要的课题。
【发明内容】
本发明提出一种有机化合物,具有高三重态能阶(tEg),可应用在有机电致发光装置,作为有机发光单元的材料。此外,由于该有机化合物可增加传递能量到发光客体(guest emitter)的效率,因此可进一步作为蓝光或绿光磷光有机电致发光装置的发光层主体材料,可以达到提升磷光有机电致发光装置的元件效率。
根据本发明一较佳实施例,该有机化合物具有如式(I)所示的化学结构:
Figure GSA00000059221800021
其中,R1、R2、R3、R4、R5、R6、及R7系分别为相同或不同的取代基,包含氢、C1-8烷基、C1-8烷氧基、C1-8卤烷基、芳香基、杂芳基、环烷基、杂环基、或环脂基;以及
Z系独立且为
Figure GSA00000059221800031
其中
R8及R9系分别为相同或不同的取代基,包含芳香基、杂芳基、环烷基、杂环基、或环脂基。
根据本发明另一较佳实施例,本发明系提供一种有机电致发光装置,该装置包含一对电极;以及有机发光单元,配置于该对电极之间,其中该有机发光单元包含上述之有机化合物。
此外,根据本发明其他较佳实施例,该有机电致发光装置的有机发光单元可包含发光层,该发光层包含主体材料及磷光掺杂材料,而该主体材料包含上述之有机化合物,且该发光层系发出蓝光或绿光。
以下藉由数个实施例及比较实施例,以更进一步说明本发明之方法、特征及优点,但并非用来限制本发明之范围,本发明之范围应以所附之申请专利范围为准。
【图式简单说明】
图1为本发明一较佳实施例所述的有机电致发光装置的剖面结构图。
【主要元件符号说明】
有机电致发光装置~10;
基底~12;
下电极~14;
有机发光单元~16;以及
上电极~18。
【具体实施方式】
有机化合物
本发明系揭露一种有机化合物,系为具有式(I)所示的化学式:
Figure GSA00000059221800041
其中,R1及R2系分别为相同或不同的取代基,包含芳香基、杂芳基、环烷基、杂环基、或环脂基,例如:苯基(phenyl)、联苯基(biphenyl)、吡啶基(pyridyl)、呋喃基(furyl)、萘基(naphthyl)、蒽基(anthryl)、菲基(phenanthrenyl)、咪唑基(imidazolyl)、嘧啶基(pyrimidinyl)、喹啉基(quinolinyl)、吲哚基(indolyl),或噻唑基(thiazolyl)。
R1、R2、R3、R4、R5、R6、及R7系分别为相同或不同的取代基,包含氢、C1-8烷基、C1-8烷氧基、C1-8卤烷基、芳香基、杂芳基、环烷基、杂环基、或环脂基;以及
Z系独立且为
Figure GSA00000059221800042
其中
R8及R9系分别为相同或不同的取代基,包含芳香基、杂芳基、环烷基、杂环基、或环脂基。
举例来说,R1、R2、R3、R4、R5、R6、及R7可分别为相同或不同的取代基,包含甲基、乙基、丙基、异丙基、丁基、异丁基、甲氧基、乙氧基、丙氧基、异丙氧基、丁氧基、异丁氧基、苯基(phenyl)、联苯基(biphenyl)、吡啶基(pyridyl)、呋喃基(furyl)、萘基(naphthyl)、蒽基(anthryl)、菲基(phenanthrenyl)、咪唑基(imidazolyl)、嘧啶基(pyrimidinyl)、喹啉基(quinolinyl)、吲哚基(indolyl),或噻唑基(thiazolyl)。
此外,R8及R9包含取代或未取代的苯基(phenyl)、联苯基(biphenyl)、吡啶基(pyridyl)、呋喃基(furyl)、萘基(naphthyl)、蒽基(anthryl)、菲基(phenanthrenyl)、咪唑基(imidazolyl)、嘧啶基(pyrimidinyl)、喹啉基(quinolinyl)、吲哚基(indolyl),或噻唑基(thiazolyl)。
整体而言,本发明所述之具有式(I)的有机化合物,具有高三重态能阶(tEg),可以改善主体材料传递能量到发光客体的效率,尤其适合作为蓝光或绿光磷光有机电致发光装置之发光层主体材料。
表1系列举出本发明一系列较佳实施例所得之具有式(I)之有机化合物,其各自之化学结构均详列于表中,因此可清楚辨识其不同取代基所分别代表的官能基。
表1
Figure GSA00000059221800051
Figure GSA00000059221800061
Figure GSA00000059221800071
为进一步说明本发明有机化合物的制备方法,以下特别详述实施例1、及实施例2所示之化合物其制备流程。
实施例1
化合物Ds1的合成
将2,5-二溴-对二甲苯(2,5-dibromo-p-xylene)(2.64g,10mmol)和过锰酸钾(KMnO4,10.0g,50mmol)放入500mL双颈圆底瓶中,加入吡啶(pyridine,20mL)和水(10mL),加热至回流。每30分钟加入过锰酸钾水溶液(5g溶于10mL水),共加四次。持续回流隔夜后,以C盐(celite)趁热过滤,将滤液减压浓缩后,加入盐酸水溶液(10%,10mL),再以乙酸乙酯萃取,取有机层,以无水硫酸镁除水,过滤并抽干,得到化合物1,系为白色粉末固体产物,产率为81%。上述反应的反应式如下所示:
Figure GSA00000059221800081
接着,将化合物1(8.92g,27.5mmol)放入250mL单颈圆底瓶中,分别加入乙醇(100mL)和浓硫酸(5mL),加热至回流。反应12小时后,以乙酸乙酯萃取,取有机层,以无水硫酸镁除水,过滤并将滤液减压浓缩,以柱层析(洗脱液为乙酸乙酯∶正己烷=1∶19)纯化,得到化合物2,系为白色固体产物,产率为85%。上述反应之反应式如下所示:
Figure GSA00000059221800082
取化合物3(1.2g,5.8mmol)、化合物2(1.0g,2.6mmol)和Pd(PPh3)4(182mg,0.16mmol)放入250mL双颈瓶中,分别加入K2CO3(2M in H2O,5.2mL)以及toluene(100mL),加热回流18小时。以二氯甲烷萃取,并以饱和食盐水洗有机层,取有机层,以无水硫酸镁除水,过滤并将滤液减压浓缩,再以柱层析法纯化(SiO2,EA/Hexane=1/8),得到化合物4,系为白色固体,产率为75%。上述反应之反应式如下所示:
Figure GSA00000059221800091
取100ml双颈瓶置入化合物4(3.74g,10.0mmol),加入H2SO4(30ml)为溶剂开始加热回流,反应3小时后让溶液恢复到室温,再用二氯甲烷进行萃取,萃取出的有机液分别以饱和食盐水与无水MgSO4进行脱水动作,最后将溶剂抽干可得红色固体,再以二氯甲烷与正已烷(n-hexane)进行再沉淀可得微红色之化合物5,产率约20%。上述反应的反应式如下所示:
取100ml双颈瓶置入化合物6(3.24g,10.0mmol)后,将反应瓶连接于真空系统抽灌氮气三次,确保整体反应处于氮气系统,接下来使用针头抽取蒸馏过之无水THF溶剂20mL注射到反应瓶内,之后将反应瓶置于-78℃低温系统中,待整体系统温度达到平衡后,使用针头吸取n-BuLi(12.0mmol,0.77g,7.5mL(1.6M,在己烷中))慢慢打入反应瓶内,维持低温反应1小时后,再将化合物5(5.0mmole,1.41g)打入反应瓶内让整体反应由-78℃慢慢反应至室温。在室温下反应两小时后,将反应瓶连接上回流系统,并且加入AcOH(30mL)、HCl(3mL)为共溶剂开始加热回流,反应3小时后让溶液恢复到室温,再用二氯甲烷进行萃取,萃取出的有机液分别以饱和食盐水与无水MgSO4进行脱水动作,最后将溶剂抽干可得灰色固体,再以二氯甲烷与正己烷(n-hexane)进行再沉淀,可得化合物Ds1,系为纯白之产物,产率约20%。上述反应的反应式如下所示:
Figure GSA00000059221800101
利用核磁共振光谱分析化合物Ds1,所得光谱数据如下:
1H NMR(CDCl3,400MHz):δ7.79(d,J=7.6Hz,2H),7.71(t,J=7.6Hz,4H),7.57(t,J=7.6Hz,2H),7.51(m,2H),7.44(d,J=7.6Hz,4H),7.37(t,J=7.6Hz,4H),7.27(s,2H),6.91(td,J=8.4,1.6Hz,4H),6.56(t,J=8.0Hz,4H),6.41(dd,J=7.6,1.6Hz,4H),6.35(d,J=8.0Hz,4H)。
实施例2
化合物Ds2的合成
取化合物7(5.72g,22.0mmol)、化合物2(3.80g,10.0mmol)和Pd(PPh3)4(693mg,0.6mmol)放入250mL双颈瓶中,分别加入K2CO3(2M in H2O,20mL)以及toluene(100mL),加热回流18小时。以二氯甲烷萃取,并以饱和食盐水洗有机层,取有机层,以无水硫酸镁除水,过滤并将滤液减压浓缩,再以柱层析法纯化(SiO2,EA/Hexane=1/8),得到化合物8,系为白色固体,产率为72%。上述反应的反应式如下所示:
Figure GSA00000059221800111
取100ml双颈瓶置入化合物8(4.87g,10.0mmol),加入H2SO4(30ml)为溶剂开始加热回流,反应3小时后让溶液恢复到室温,再用二氯甲烷进行萃取,萃取出的有机液分别以饱和食盐水与无水MgSO4进行脱水动作,最后将溶剂抽干可得红色固体,再以二氯甲烷与正已烷(n-hexane)进行再沉淀可得微红色的化合物9,产率约18%。上述反应的反应式如下所示:
Figure GSA00000059221800112
利用核磁共振光谱分析化合物9,所得光谱数据如下:
1H NMR(CDCl3,200MHz):δ7.74(s,2H),7.71(s,2H),7.56(dd,J=8.0,1.8Hz,2H),7.44(dd,J=8.1,1.8Hz,2H),1.35(s,18H)。
取100ml双颈瓶置入化合物6(3.24g,10.0mmol)后,将反应瓶连接于真空系统抽灌氮气三次,确保整体反应处于氮气系统,接下来使用针头抽取蒸馏过的无水THF溶剂20mL注射到反应瓶内,之后将反应瓶置于-78℃低温系统中,待整体系统温度达到平衡后,使用针头吸取n-BuLi(12.0mmol,0.77g,7.5mL(1.6M,在己烷中))慢慢打入反应瓶内,维持低温反应1小时后,再将化合物9(5.0mmole,1.97g)打入反应瓶内,让整体反应由-78℃慢慢反应至室温。在室温下反应两小时后,将反应瓶连接上回流系统,并且加入AcOH(30mL)、HCl(3mL)为共溶剂开始加热回流,反应3小时后让溶液恢复到室温,再用二氯甲烷进行萃取,萃取出的有机液分别以饱和食盐水与无水MgSO4进行脱水动作,最后将溶剂抽干可得灰色固体,再以二氯甲烷与正己烷进行再沉淀,可得化合物Ds2,系为白色产物,产率约20%。上述反应的反应式如下所示:
Figure GSA00000059221800121
利用核磁共振光谱分析化合物Ds2,所得光谱数据如下:
1H NMR(CDCl3,400MHz):δ7.52(t,J=8.4Hz,4H),7.43(td,J=8.4,1.6Hz,,2H),7.28-7.21(m,8H),7.09-6.99(m,12H),6.91-6.84(m,8H),1.37(s,18H)。
接着,对化合物Ds1和Ds2的能阶(最高键结电子能阶(HOMO)与最低未键结能阶(LUMO))、玻璃转化温度(Tg)、熔点(Tm)、能隙(Eg)、及三重态能阶(tEg)进行测量,其测量结果请参照表2。
表2
化合物    LUMO    HOMO    Tg      Tm      Eg      tEg
          (eV)    (eV)    (℃)    (℃)    (eV)    (eV)
Ds1       5.8     2.4     -       427     3.4     2.9
DS2       5.7     2.4     167     430     3.3     2.9
实施例3
化合物Ds3的合成
将化合物11(4.39克,12.5mmole)放入500ml双颈圆底瓶中,于真空系统抽灌氮气数次,再以针筒加入干燥除水过的四氢呋喃(THF),降温至-78℃。于-78℃温度下,逐滴滴入n-BuLi(12.0mmol,0.77g,7.5mL(1.6M inhexane)),滴完后持续搅拌1小时。同样在-78℃下,加入化合物9(1.97g克,5.0mmole),搅拌隔夜,使其自然回温至室温。再以乙酸乙酯和饱和食盐水萃取、无水硫酸镁除水,减压浓缩抽干后,加入100ml醋酸,加热至70℃。于70℃下,加入5ml盐酸,并反应4小时。接着,以乙酸乙酯和饱和食盐水萃取、无水硫酸镁除水、及减压浓缩抽干后,利用柱层析法纯化(洗脱液为乙酸乙酯/正己烷=1/20),可得淡黄色固体产物(化合物Ds3)。上述反应之反应式如下所示:
Figure GSA00000059221800141
利用核磁共振光谱分析化合物Ds3,所得光谱数据如下:
1H NMR(CDCl3,400MHz):δ7.97(d,J=1.0Hz,2H),7.80(d,J=1.2H,2H),7.74(s,4H),7.58(d,J=7.8Hz,2H),7.44(d,J=8.2Hz,2H),7.18~7.38(m,24H),2.40(s,3H),2.33(s,3H),1.38(s,18H)。
实施例4
化合物Ds4的合成
将化合物12(4.93克,12.5mmole)放入500ml双颈圆底瓶中,于真空系统抽灌氮气数次,再以针筒加入干燥除水过之四氢呋喃(THF),降温至-78℃。于-78℃温度下,逐滴滴入n-BuLi,滴完后持续搅拌1小时。接着,在-78℃下,加入化合物9(1.97g克,5.0mmole),搅拌整夜,并使其自然回温至室温。接着,以乙酸乙酯和饱和食盐水萃取、无水硫酸镁除水,减压浓缩抽干后,加入100ml醋酸,加热至70℃。于70℃下,加入5ml盐酸,反应4小时后,以乙酸乙酯和饱和食盐水萃取、无水硫酸镁除水,减压浓缩抽干后,利用柱层析法纯化(洗脱液为乙酸乙酯/正己烷=1/20),可得淡黄色固体产物(化合物Ds4)。但是此产物为混合产物,因为不对称的化合物12(三芳基胺,triarylamine)在环化时,不具有选择性,所以可以从4-甲基苯基(4-methylbenzyl)的位置或是由4-叔丁基苯基(4-tert-butylbenzyl)的位置接上,所以除了得到化合物Ds4外,还会得到其他两种副产物,上述反应的反应式如下所示:
Figure GSA00000059221800151
Figure GSA00000059221800161
Figure GSA00000059221800171
利用核磁共振光谱分析化合物Ds4,所得光谱数据如下:
1H NMR(CDCl3,400MHz):δ7.87~7.77(m,8H),7.72~7.38(m,24H),7.02~6.97(m,8H),6.51~6.36(m,20H),2.57(s,3H),1.99(s,3H),1.49(s,9H),1.28(s,9H),1.26(s,9H),0.98(s,9H)。
有机电致发光装置
请参照图1,系显示符合本发明所述的有机电致发光装置10的剖面结构示意图,该有机电致发光装置10包括基底12、下电极14、有机发光单元16及上电极18。该有机电致发光装置10可为上发光、下发光、或双面发光有机电致发光装置。该基底可例如为玻璃、塑胶基板、或半导体基板。该下电极14及上电极18的材质可例如为锂、镁、钙、铝、银、铟、金、钨、镍、铂、铜、铟锡氧化物(ITO)、铟锌氧化物(IZO)、锌铝氧化物(AZO)、氧化锌(ZnO)或其结合,而其形成方式可为热蒸镀、溅射或等离子体增强式化学气相沉积方式。此外,该下电极14及上电极18至少之一需具有透光的性质。
该有机发光单元16至少包含发光层,可还包含空穴注入层、空穴传输层、电子传输层、电子注入层或其他膜层。值得注意的是,根据本发明较佳实施例,该有机发光单元16必需包含本发明所述具有式(I)的有机化合物。换言之,在该有机发光单元16中,至少有一膜层包含该有机化合物。
根据本发明另一较佳实施例,该有机电致发光装置可为磷光有机电致发光装置,而该磷光有机发光单元的发光层包含主体材料及磷光掺杂材料,而该主体材料包含本发明所述具有式(I)所示结构的有机化合物。本领域技术人员可视所使用的有机电致发光材料及所需的元件特性,将本发明所述有机化合物与所需的磷光掺杂材料掺杂,并改变所搭配的掺杂物的掺杂量。因此,掺杂物的掺杂量非关本发明之特征,非为限制本发明范围的依据。
为进一步说明本发明有机电致发光装置,以下实施例系将由实施例2所得的有机化合物Ds2作为发光层材料,来分别搭配蓝光跟绿光的掺杂材料。此外,以下亦提供数个有机电致发光装置的比较实施例,来验证本发明所述之有机化合物具有与现有技术材料相比确实具有较高的光电特性。
实施例5:
使用中性清洁剂、丙酮、及乙醇以超音波振荡将已图案化的ITO(厚度为120nm)玻璃基底洗净。以氮气将基材吹干,然后UV-OZONE 30分钟,接着于10-6torr的压力下依序沉积NPB(N,N’-二(萘-1-基)-N,N’-二苯基联苯胺,N,N′-di(naphthalene-l-yl)-N,N′-diphenyl-benzidine,厚度为30nm)、Ds2掺杂Firpic(双(4,6-二氟苯基吡啶-N,C2)吡啶甲酰合铱,Iridium-bis(4,6difluorophenyl-pyridinato-N,C2)-picolinate)(Ds2与Firpic的比例为100∶6、厚度为30nm)、BCP(2,9-二甲基-4,7-二苯基-1,10-菲咯啉,2,9-dimethyl-4,7diphenyl-1,10-phenanthroline、厚度为15nm)、Alq3(三(8-羟基喹啉)铝,tris(8-hydroxyquinoline)aluminum,厚度为30nm)、LiF(厚度为1nm)、及Al(厚度为100nm),封装后获致该电致发光装置(1)。该电致发光装置(1)的结构可表示为:ITO/NPB/Ds2:FIrpic(6%)/BCP/Alq3/LiF/Al。
接着,测量该电致发光装置(1)的光学特性,其测量结果请参照表3。
实施例6:
使用中性清洁剂、丙酮、及乙醇以超音波振荡将已图案化的ITO(厚度为120nm)玻璃基底洗净。以氮气将基材吹干,然后UV-OZONE 30分钟,接着于10-6torr的压力下依序沉积NPB(N,N′-di(naphthalene-l-yl)-N,N′-diphenyl-benzidine、厚度为30nm)、mCP(N,N’-二咔唑基-3,5-二苯,N,N’-dicarbazolyl-3,5-dibenzene、厚度为20nm)、Ds2掺杂Firpic(Iridium-bis(4,6difluorophenyl-pyridinato-N,C2)-picolinate)(DS2与Firpic的比例为100∶6、厚度为30nm)、BCP(2,9-dimethyl-4,7diphenyl-1,10-phenanthroline、厚度为15nm)、Alq3(tris(8-hydroxyquinoline)aluminum、厚度为30nm)、LiF(厚度为1nm)、及Al(厚度为100nm),封装后获致该电致发光装置(2)。该电致发光装置(2)之结构可表示为:ITO/NPB/mCP/Ds2:FIrpic(6%)/BCP/Alq3/LiF/Al,
接着,测量该电致发光装置(1)的光学特性,其测量结果请参照表3。
实施例7:
使用中性清洁剂、丙酮、及乙醇以超音波振荡将已图案化的ITO(厚度为120nm)玻璃基底洗净。以氮气将基材吹干,然后UV-OZONE 30分钟,接着于10-6torr的压力下依序沉积TCTA(4,4’,4”-三(N-咔唑基)三苯胺,4,4’,4”-tri(N-carbazolyl)triphenylamine,厚度为30nm)、mCP(N,N’-二咔唑基-3,5-二苯,N,N’-dicarbazolyl-3,5-dibenzene,厚度为20nm)、DS2掺杂Firpic(Iridium-bis(4,6difluorophenyl-pyridinato-N,C2)-picolinate)(DS2与Firpic的比例为100∶6、厚度为30nm)、BCP(2,9-dimethyl-4,7diphenyl-1,10-phenanthroline、厚度为15nm)、Alq3((tris(8-hydroxyquinoline)aluminum、厚度为30nm)、LiF(厚度为1nm)、及Al(厚度为100nm),封装后获致该电致发光装置(3)。该电致发光装置(3)之结构可表示为:ITO/TCTA/mCP/Ds2:FIrpic(6%)/BCP/Alq3/LiF/Al,
接着,测量该电致发光装置(3)的光学特性,其测量结果请参照表3。
实施例8:
使用中性清洁剂、丙酮、及乙醇以超音波振荡将已图案化的ITO(厚度为120nm)玻璃基底洗净。以氮气将基材吹干,然后UV-OZONE 30分钟,接着于10-6torr的压力下依序沉积NPB(N,N′-di(naphthalene-l-yl)-N,N′-diphenyl-benzidine、厚度为30nm)、mCP(N,N’-dicarbazolyl-3,5-dibenzene、厚度为20nm)、Ds2掺杂Firpic(Iridium-bis(4,6difluorophenyl-pyridinato-N,C2)-picolinate)(Ds2与Firpic的比例为100∶6、厚度为30nm)、TPBI(1,3,5-tris(phenyl-2-benzimidazolyl)-benzene、厚度为20nm)、LiF(厚度为1nm)、及Al(厚度为100nm),封装后获致该电致发光装置(4)。该电致发光装置(4)之结构可表示为:ITO/NPB/mCP/Ds2:FIrpic(6%)/TPBI/LiF/Al,
接着,测量该电致发光装置(4)的光学特性,其测量结果请参照表3。
比较实施例1:
使用中性清洁剂、丙酮、及乙醇以超音波振荡将已图案化的ITO(厚度为120nm)玻璃基底洗净。以氮气将基材吹干,然后UV-OZONE 30分钟,接着于10-6torr的压力下依序沉积TCTA(4,4’,4”-tri(N-carbazolyl)triphenylamine、厚度为30nm)、DAT掺杂Firpic(Iridium-bis(4,6difluorophenyl-pyridinato-N,C2)-picolinate)(DAT与Firpic的比例为100∶6、厚度为30nm)、TPBI(1,3,5-tris(phenyl-2-benzimidazolyl)-benzene)、厚度为30nm)、LiF(厚度为1nm)、及Al(厚度为100nm),封装后获致该电致发光装置(5)。该电致发光装置(5)之结构可表示为:ITO/TCTA/DAT:Firpic(6%)/TPBI/LiF/Al,
DAT之结构为:
Figure GSA00000059221800201
接着,测量该电致发光装置(5)的光学特性,其测量结果请参照表3。
比较实施例2
使用中性清洁剂、丙酮、及乙醇以超音波振荡将已图案化的ITO(厚度为120nm)玻璃基底洗净。以氮气将基材吹干,然后UV-OZONE 30分钟,接着于10-6torr的压力下依序沉积TCTA((4,4’,4”-tri(N-carbazolyl)triphenylamine)、厚度为30nm)、DAT掺杂Firpic(Iridium-bis(4,6difluorophenyl-pyridinato-N,C2)-picolinate)(DAT与Firpic的比例为100∶6、厚度为30nm)、BCP(2,9-dimethyl-4,7diphenyl-1,10-phenanthroline、厚度为30nm)、Alq3(tris(8-hydroxyquinoline)aluminum、厚度为30nm)、LiF(厚度为1nm)、及Al(厚度为100nm),封装后获致该电致发光装置(6)。该电致发光装置(6)之结构可表示为:ITO/TCTA/DAT:FIrpic(6%)/BCP/Alq3/LiF/Al,
接着,测量该电致发光装置(6)的光学特性,其测量结果请参照表3。
比较实施例3
使用中性清洁剂、丙酮、及乙醇以超音波振荡将已图案化的ITO(厚度为120nm)玻璃基底洗净。以氮气将基材吹干,然后UV-OZONE 30分钟,接着于10-6torr的压力下依序沉积TCTA((4,4’,4”-tri(N-carbazolyl)triphenylamine)、厚度为30nm)、DAT掺杂Firpic(Iridium-bis(4,6difluorophenyl-pyridinato-N,C2)-picolinate)(DAT与Firpic的比例为100∶6、厚度为30nm)、BPhen(4,7-二苯基-1,10-菲咯啉,4,7-diphenyl-1,10-phenanthroline)、厚度为30nm)、LiF(厚度为1nm)、及Al(厚度为100nm),封装后获致该电致发光装置(7)。该电致发光装置(7)之结构可表示为:
ITO/TCTA/DAT:FIrpic(6%)/BPhen/LiF/Al,
接着,测量该电致发光装置(7)的光学特性,其测量结果请参照表3。
比较实施例4
使用中性清洁剂、丙酮、及乙醇以超音波振荡将已图案化的ITO(厚度为120nm)玻璃基底洗净。以氮气将基材吹干,然后UV-OZONE 30分钟,接着于10-6torr的压力下依序沉积TCTA(4,4’,4”-tri(N-carbazolyl)triphenylamine、厚度为30nm)、DAT掺杂Firpic(Iridium-bis(4,6difluorophenyl-pyridinato-N,C2)-picolinate)(DAT与Firpic的比例为100∶9、厚度为30nm)、TPBI(1,3,5-tris(phenyl-2-benzimidazolyl)-benzene)、厚度为30nm)、LiF(厚度为1nm)、及Al(厚度为100nm),封装后获致该电致发光装置(8)。该电致发光装置(8)之结构可表示为:ITO/TCTA/DAT:Firpic(9%)/TPBI/LiF/Al,
接着,测量该电致发光装置(8)的光学特性,其测量结果请参照表3。
比较实施例5
使用中性清洁剂、丙酮、及乙醇以超音波振荡将已图案化的ITO(厚度为120nm)玻璃基底洗净。以氮气将基材吹干,然后UV-OZONE 30分钟,接着于10-6torr的压力下依序沉积TCTA((4,4’,4”-tri(N-carbazolyl)triphenylamine)、厚度为30nm)、CBP(4,4′-N,N′-dicarbazole-biphenyl)掺杂Firpic(Iridium-bis(4,6difluorophenyl-pyridinato-N,C2)-picolinate)(CBP与Firpic的比例为100∶6、厚度为30nm)、TPBI(1,3,5-tris(phenyl-2-benzimidazolyl)-benzene、厚度为30nm)、LiF(厚度为1nm)、及Al(厚度为100nm),封装后获致该电致发光装置(9)。该电致发光装置(9)之结构可表示为:ITO/TCTA/CBP:FIrpic(6%)/TPBI/LiF/Al,
接着,测量该电致发光装置(9)的光学特性,其测量结果请参照表3。
表3
  编号   最大亮度(cd/m2)   功率效率(lm/W)   电流效率(cd/A)   CIE
  电致发光装置(1)   37000(电压为13.5V)   4.5(电压为5.0V)   17.2(电压为5.0V) (0.14,0.31)
  电致发光装置(2)   46000(电压为12.5V)   6.3(电压为5.5V)   21.9(电压为5.5V) (0.13,0.28)
  电致发光装置(3)   29000(电压为13V)   4.0(电压为4.5V)   13.8(电压为4.5V) (0.15,0.33)
  电致发光装置(4)   17000(电压为12.5V)   3.1(电压为6.0V)   10.8(电压为5.0V) (0.13,0.29)
  电致发光装置(5)   4644(电压为11V)   7.19(电压为4.0V)   9.16(电压为4.0V) (0.13,0.30)
  电致发光装置(6)   1733(电压为11V)   5.72(电压为6.5V)   2.57(电压为6.5V) (0.13,0.29)
  电致发光装置(7)   6668(电压为10.5V)   5.86(电压为4.5V)   8.39(电压为4.5V (0.13,0.30)
  电致发光装置(8)  2200(电压为11V)   10.2(电压为5.5V)   5.9(电压为5.5V) (0.12,0.29)
  电致发光装置(9)  1532(电压为13V)   3.27(电压为6.5V)   1.6(电压为6.5V) (0.26,0.45)
如表3所示,在搭配相同蓝光材料,本发明所述之有机化合物Ds2与DAT及已知CBP相比,有比较好的元件效率及亮度。
实施例9:
使用中性清洁剂、丙酮、及乙醇以超音波振荡将已图案化的ITO(厚度为120nm)玻璃基底洗净。以氮气将基材吹干,然后UV-OZONE 30分钟,接着于10-6torr的压力下依序沉积NPB(N,N′-di(naphthalene-l-yl)-N,N′-diphenyl-benzidine、厚度为30nm)、Ds2掺杂Ir(ppy)3(Ds2与Ir(ppy)3的比例为100∶6、厚度为30nm)、BCP(2,9-dimethyl-4,7diphenyl-1,10-phenanthroline、厚度为10nm)、Alq3(tris(8-hydroxyquinoline)aluminum、厚度为40nm)、LiF(厚度为1nm)、及Al(厚度为100nm),封装后获致该电致发光装置(2)。该电致发光装置(10)之结构可表示为:ITO/NPB/Ds2:Ir(ppy)3(6%)/BCP/Alq3/LiF/Al,
接着,测量该电致发光装置(10)之光学特性,其测量结果请参照表4。
实施例10:
使用中性清洁剂、丙酮、及乙醇以超音波振荡将已图案化的ITO(厚度为120nm)玻璃基底洗净。以氮气将基材吹干,然后UV-OZONE 30分钟,接着于10-6torr的压力下依序沉积TCTA(4,4’,4”-tri(N-carbazolyl)triphenylamine、厚度为30nm)、Ds2掺杂Ir(ppy)3(Ds2与Ir(ppy)3的比例为100∶6、厚度为30nm)、TPBI(1,3,5-tris(phenyl-2-benzimidazolyl)-benzene、厚度为30nm)、LiF(厚度为1nm)、及Al(厚度为100nm),封装后获致该电致发光装置(11)。该电致发光装置(11)之结构可表示为:ITO/NPB/Ds2:Ir(ppy)3(6%)/TPBI/LiF/Al,
接着,测量该电致发光装置(11)之光学特性,其测量结果请参照表4。
比较实施例6:
使用中性清洁剂、丙酮、及乙醇以超音波振荡将已图案化的ITO(厚度为120nm)玻璃基底洗净。以氮气将基材吹干,然后UV-OZONE 30分钟,接着于10-6torr的压力下依序沉积TCTA(4,4’,4”-tri(N-carbazolyl)triphenylamine、厚度为30nm)、DAT掺杂Ir(ppy)3(DAT与Ir(ppy)3的比例为100∶6、厚度为30nm)、TPBI(1,3,5-tris(phenyl-2-benzimidazolyl)-benzene)、厚度为30nm)、LiF(厚度为1nm)、及Al(厚度为100nm),封装后获致该电致发光装置(12)。该电致发光装置(12)之结构可表示为:ITO/TCTA/DAT:Ir(ppy)3(6%)/TPBI/LiF/Al,DAT之结构为:
Figure GSA00000059221800241
接着,测量该电致发光装置(12)之光学特性,其测量结果请参照表4。
比较实施例7
使用中性清洁剂、丙酮、及乙醇以超音波振荡将已图案化的ITO(厚度为120nm)玻璃基底洗净。以氮气将基材吹干,然后UV-OZONE 30分钟,接着于10-6torr的压力下依序沉积TCTA(4,4’,4”-tri(N-carbazolyl)triphenylamine、厚度为30nm)、DAT掺杂Ir(ppy)3(DAT与Ir(ppy)3的比例为100∶9、厚度为30nm)、BCP(2,9-dimethyl-4,7diphenyl-1,10-phenanthroline、厚度为30nm)、Alq3(tris(8-hydroxyquinoline)aluminum、厚度为30nm)、LiF(厚度为1nm)、及Al(厚度为100nm),封装后获致该电致发光装置(12)。该电致发光装置(12)之结构可表示为:ITO/TCTA/DAT:Ir(ppy)3(9%)/BCP/Alq3/LiF/Al,
接着,测量该电致发光装置(13)之光学特性,其测量结果请参照表4。
比较实施例8
使用中性清洁剂、丙酮、及乙醇以超音波振荡将已图案化的ITO(厚度为120nm)玻璃基底洗净。以氮气将基材吹干,然后UV-OZONE 30分钟,接着于10-6torr的压力下依序沉积TCTA(4,4’,4”-tri(N-carbazolyl)triphenylamine、厚度为30nm)、CBP(4,4′-N,N′-dicarbazole-biphenyl)掺杂FIrpic(CBP与FIrpic的比例为100∶6、厚度为30nm)、BCP(2,9-dimethyl-4,7diphenyl-1,10-phenanthroline、厚度为30nm)、Alq3(tris(8-hydroxyquinoline)aluminum、厚度为30nm)、LiF(厚度为1nm)、及Al(厚度为100nm),封装后获致该电致发光装置(14)。该电致发光装置(14)之结构可表示为:ITO/TCTA/CBP:FIrpic(6%)/BCP/Alq3/LiF/Al,
接着,测量该电致发光装置(14)之光学特性,其测量结果请参照表4。
表4
  编号   最大亮度(cd/m2)   功率效率(lm/W)   电流效率(cd/A)   CIE
  电致发光装置(10)   110000(电压为15V)   15.7(电压为6V)   40.2(电压为5.5V) (0.25,0.66)
  电致发光装置(11)   67000(电压为15V)   10.7(电压为6V)   25.7(电压为5V) (0.25,0.65)
  电致发光装置(12)   12115(电压为11.5V)   4.2(电压为7.5V)   10.3(电压为8V) (0.37,0.58)
  电致发光装置(13)   32837(电压为10.5V)   5.02(电压为5.5V)   11.2(电压为7V) (0.27,0.62)
  电致发光装置(14)   15441(电压为11.5V)   12.5(电压为8V)   31.8(电压为8V) (0.33,0.60)
如表4所示,在搭配相同绿光材料,本发明所述的有机化合物Ds2与DAT及已知材料CBP相比,有比较好的元件效率及亮度。
虽然本发明已以较佳实施例揭露如上,然其并非用以限定本发明,任何本领域技术人员在不脱离本发明之精神和范围内,当可作些许之更动与润饰,因此本发明的保护范围以所附权利要求为准。

Claims (5)

1.一种有机化合物,其具有如式(I)所示的化学式:
Figure FSB00001031440400011
其中,R1、R2、R3、R4、R5、R6、及R7系分别为相同或不同的取代基,是氢、甲基、乙基、丙基、异丙基、丁基、异丁基、甲氧基、乙氧基、丙氧基、异丙氧基、丁氧基、异丁氧基、苯基(phenyl)、联苯基(biphenyl)、吡啶基(pyridyl)、呋喃基(furyl)、萘基(naphthyl)、蒽基(anthryl)、菲基(phenanthrenyl)、咪唑基(imidazolyl)、嘧啶基(pyrimidinyl)、喹啉基(quinolinyl)、吲哚基(indolyl),或噻唑基(thiazolyl);以及
Z系
Figure FSB00001031440400012
其中
R8系为苯基。
2.如权利要求1所述的有机化合物,其中该有机化合物系为
3.一种有机电致发光装置,包括:
一对电极;以及
有机发光单元,配置于该对电极之间,其中该有机发光单元包含具有式(I)所示结构:
Figure FSB00001031440400031
其中,R1、R2、R3、R4、R5、R6、及R7系分别为相同或不同的取代基,是甲基、乙基、丙基、异丙基、丁基、异丁基、甲氧基、乙氧基、丙氧基、异丙氧基、丁氧基、异丁氧基、苯基(pheny1)、联苯基(biphenyl)、吡啶基(pyridyl)、呋喃基(furyl)、萘基(naphthyl)、蒽基(anthryl)、菲基(phenanthrenyl)、咪唑基(imidazolyl)、嘧啶基(pyrimidinyl)、喹啉基(quinolinyl)、吲哚基(indolyl),或噻唑基(thiazolyl);以及
Z系其中
R8系为苯基。
4.一种有机电致发光装置,包括:
一对电极;以及
有机发光单元,配置于该对电极之间,
其中,该有机发光单元包含发光层,该发光层包含主体材料及磷光掺杂材料,而该主体材料包含具有式(I)所示结构的化合物:
Figure FSB00001031440400041
其中,R1、R2、R3、R4、R5、R6、及R7系分别为相同或不同的取代基,是氢、甲基、乙基、丙基、异丙基、丁基、异丁基、甲氧基、乙氧基、丙氧基、异丙氧基、丁氧基、异丁氧基、苯基(phenyl)、联苯基(biphenyl)、吡啶基(pyridyl)、呋喃基(furyl)、萘基(naphthyl)、蒽基(anthryl)、菲基(phenanthrenyl)、咪唑基(imidazolyl)、嘧啶基(pyrimidinyl)、喹啉基(quinolinyl)、吲哚基(indolyl),或噻唑基(thiazolyl);以及
Z系
Figure FSB00001031440400042
其中
R8系为苯基。
5.如权利要求4所述的有机电致发光装置,其中该发光层系发出蓝光或绿光。
CN 201010143878 2010-03-17 2010-03-17 有机化合物及包含其的有机电致发光装置 Active CN102190618B (zh)